Nanostructured Fe–Ag electrocatalysts for the oxygen reduction reaction in alkaline media

The impregnation of Ketjen Black (C) with iron(II) and silver(II) phthalocyanines (MPc) individually or as a 1 : 1 stoichiometric mixture, followed by heat treatment at 600 °C under inert atmosphere, gave a series of novel nanostructured electrocatalysts AgPc/C(600), FePc/C(600) and FeAgPc/C(600) (ca. 3 wt% metal loadings) for the oxygen reduction reaction (ORR) in alkaline media. The catalysts were structurally characterized by XRPD, XPS, HR-TEM/STEM and chemisorption measurements. During the synthetic heat treatment of AgPc/C(600) at temperatures above 250 °C, the AgPc decomposed to form small finely dispersed carbon supported Ag nanoparticles (mean diameter 8.5 nm). This process was delayed for FeAgPc/C(600) to above 300 °C and the resulting Ag nanoparticles were much smaller (mean diameter 2.3 nm). As expected, at 600 °C the FePc/C(600) forms highly dispersed arrays of single Fe ions coordinated by four nitrogen atoms (Fe–N4 units). Electrodes coated with AgPc/C(600), FePc/C(600) and FeAgPc/C(600) were investigated for ORR in alkaline media by linear sweep voltammetry and the RRDE system was used to probe the production of HO2−. The electrochemical activity of all materials was analyzed by Tafel and Koutecky–Levich plots and the stability of each catalyst was followed using chronopotentiometry. Both Fe-containing electrocatalysts, FeAgPc/C(600) and FePc/C(600), were highly active for the ORR promoting exclusively the four electron pathway also during chronopotentiometry, while AgPc/C(600) was found to produce up to 35 mol% HO2−. Compared to FePc/C(600), the binary FeAgPc/C(600) catalyst displayed remarkably higher activity and stability. This experimental evidence could be explained in terms of a synergistic Ag–Fe interaction which results from the unique nanostructure that forms during heat treatment which consists of very finely dispersed Ag nanoparticles and Fe–N4 moieties.

[1]  P. Kohl,et al.  Anionic polysulfone ionomers and membranes containing fluorenyl groups for anionic fuel cells , 2009 .

[2]  H Jahnke,et al.  Organic dyestuffs as catalysts for fuel cells. , 1976, Topics in current chemistry.

[3]  Shuqin Song,et al.  Low and non-platinum electrocatalysts for PEMFCs: Current status, challenges and prospects , 2012 .

[4]  R. Kostecki,et al.  A novel CuFe-based catalyst for the oxygen reduction reaction in alkaline media , 2011 .

[5]  H. Tributsch,et al.  Catalysts for the Oxygen Reduction from Heat-Treated Iron(III) Tetramethoxyphenylporphyrin Chloride: Structure and Stability of Active Sites , 2003 .

[6]  Mathias Schulze,et al.  Long term investigations of silver cathodes for alkaline fuel cells , 2004 .

[7]  Sebastian Doniach,et al.  Many-electron singularity in X-ray photoemission and X-ray line spectra from metals , 1970 .

[8]  M. Arenz,et al.  Investigation of the Oxygen Reduction Activity on Silver – A Rotating Disc Electrode Study , 2010 .

[9]  J. Ozaki,et al.  Enhancement of oxygen reduction activity of nanoshell carbons by introducing nitrogen atoms from metal phthalocyanines , 2010 .

[10]  Y. Yamazaki,et al.  Influence of anion ionomer content and silver cathode catalyst on the performance of alkaline membrane electrode assemblies (MEAs) for direct methanol fuel cells (DMFCs) , 2008 .

[11]  C. Hsieh,et al.  Synthesis of silver nanoparticles on carbon papers for electrochemical catalysts , 2011 .

[12]  P. Atanassov,et al.  Anion-Exchange Membrane Fuel Cells: Dual-Site Mechanism of Oxygen Reduction Reaction in Alkaline Media on Cobalt−Polypyrrole Electrocatalysts , 2010 .

[13]  Rongrong Chen,et al.  Tuning the Electrochemical Interface of Ag/C Electrodes in Alkaline Media with Metallophthalocyanine Molecules , 2013 .

[14]  N. Wagner,et al.  Preparation of Gas Diffusion Electrodes with Silver Catalysts for Alkaline Fuel Cells , 2003 .

[15]  Rongrong Chen,et al.  OH−-Binding Effects on Metallophthalocyanine Catalysts for O2 Reduction Reaction in Anion Exchange Membrane Fuel Cells , 2012, Electrocatalysis.

[16]  Xuejun Zhou,et al.  Electrochemical behavior of nanostructured nickel phthalocyanine (NiPc/C) for oxygen reduction reaction in alkaline media , 2012, Journal of Applied Electrochemistry.

[17]  J. Leger,et al.  How does α-FePc catalysts dispersed onto high specific surface carbon support work towards oxygen reduction reaction (orr)? , 2006 .

[18]  P. Walker,et al.  Platinum catalysts supported on graphitized carbon black—I: Characterization of the platinum by titrations and differential calorimetry , 1982 .

[19]  Jaeyoung Lee,et al.  Oxygen electrocatalysis in chemical energy conversion and storage technologies , 2013 .

[20]  Yu Chuan Liu,et al.  New pathway for the synthesis of ultrafine silver nanoparticles from bulk silver substrates in aqueous solutions by sonoelectrochemical methods , 2004 .

[21]  Seung Yong Lee,et al.  Highly active N-doped-CNTs grafted on Fe/C prepared by pyrolysis of dicyandiamide on Fe2O3/C for electrochemical oxygen reduction reaction , 2011 .

[22]  Young Dok Kim,et al.  Ag nanoparticles on highly ordered pyrolytic graphite (HOPG) surfaces studied using STM and XPS , 2005 .

[23]  Won-Yong Lee,et al.  Performance of solid alkaline fuel cells employing anion-exchange membranes , 2008 .

[24]  Hubert A. Gasteiger,et al.  Oxygen reduction on a high-surface area Pt/Vulcan carbon catalyst: a thin-film rotating ring-disk electrode study , 2001 .

[25]  Nigel P. Brandon,et al.  Review of gas diffusion cathodes for alkaline fuel cells , 2009 .

[26]  Svitlana Pylypenko,et al.  Non-platinum oxygen reduction electrocatalysts based on pyrolyzed transition metal macrocycles , 2008 .

[27]  Frédéric Jaouen,et al.  Iron-Based Catalysts with Improved Oxygen Reduction Activity in Polymer Electrolyte Fuel Cells , 2009, Science.

[28]  Patrick Bertrand,et al.  Heat-treated iron and cobalt tetraphenylporphyrins adsorbed on carbon black: Physical characterization and catalytic properties of these materials for the reduction of oxygen in polymer electrolyte fuel cells , 1996 .

[29]  H. Hassan,et al.  Electrochemical Behaviour of a Silver Electrode in NaOH Solutions , 1998 .

[30]  Yuyan Shao,et al.  Recent progress in nanostructured electrocatalysts for PEM fuel cells , 2013 .

[31]  Christophe Coutanceau,et al.  Development of electrocatalysts for solid alkaline fuel cell (SAFC) , 2006 .

[32]  Zhongwei Chen,et al.  A soluble and highly conductive ionomer for high-performance hydroxide exchange membrane fuel cells. , 2009, Angewandte Chemie.

[33]  Tebello Nyokong,et al.  Metallophthalocyanine-based molecular materials as catalysts for electrochemical reactions , 2010 .

[34]  T. Yamashita,et al.  Analysis of XPS spectra of Fe2+ and Fe3+ ions in oxide materials , 2008 .

[35]  Dc Kitty Nijmeijer,et al.  Anion exchange membranes for alkaline fuel cells: A review , 2011 .

[36]  K. Scott,et al.  Effect of anion functional groups on the conductivity and performance of anion exchange polymer membrane fuel cells , 2012 .

[37]  X. Ren,et al.  Electrochemical and spectroscopic study of novel Cu and Fe-based catalysts for oxygen reduction in alkaline media , 2012 .

[38]  Ning Li,et al.  Ag/C nanoparticles as an cathode catalyst for a zinc-air battery with a flowing alkaline electrolyte , 2009 .

[39]  G. Tremiliosi‐Filho,et al.  Straightforward Synthesis of Carbon-Supported Ag Nanoparticles and Their Application for the Oxygen Reduction Reaction , 2012, Electrocatalysis.

[40]  G. Geoffroy,et al.  Measurement of silver surface area by the H2 titration of chemisorbed oxygen , 1983 .

[41]  B. Améduri,et al.  Polymeric materials as anion-exchange membranes for alkaline fuel cells , 2011 .

[42]  D. Goodman,et al.  Preparation and characterization of ultra-thin iron oxide films on a Mo(100) surface , 1995 .

[43]  P. Bertrand,et al.  Catalytic activity and stability of heat-treated iron phthalocyanines for the electroreduction of oxygen in polymer electrolyte fuel cells , 1996 .

[44]  K. Scott,et al.  Electrochemical and fuel cell evaluation of Co based catalyst for oxygen reduction in anion exchange , 2011 .

[45]  Robert C T Slade,et al.  Steady-state dc and impedance investigations of H2/O2 alkaline membrane fuel cells with commercial Pt/C, Ag/C, and Au/C cathodes. , 2006, The journal of physical chemistry. B.

[46]  Jiujun Zhang,et al.  Highly active electrocatalysts for oxygen reduction from carbon-supported copper-phthalocyanine synthesized by high temperature treatment , 2012 .

[47]  R. Jasinski,et al.  A New Fuel Cell Cathode Catalyst , 1964, Nature.

[48]  R. Slade,et al.  Prospects for Alkaline Anion‐Exchange Membranes in Low Temperature Fuel Cells , 2005 .

[49]  Rongrong Chen,et al.  Improving Oxygen Reduction Reaction Activities on Carbon-Supported Ag Nanoparticles in Alkaline Solutions , 2010 .

[50]  Claudio Bianchini,et al.  Single-site and nanosized Fe–Co electrocatalysts for oxygen reduction: Synthesis, characterization and catalytic performance , 2011 .

[51]  Stephen Maldonado,et al.  Direct preparation of carbon nanofiber electrodes via pyrolysis of iron(II) phthalocyanine: Electrocatalytic aspects for oxygen reduction , 2004 .

[52]  K. Nouneh,et al.  XPS study of silver, nickel and bimetallic silver–nickel nanoparticles prepared by seed-mediated growth , 2012 .

[53]  Hsing-lin Wang,et al.  A carbon-nanotube-supported graphene-rich non-precious metal oxygen reduction catalyst with enhanced performance durability. , 2013, Chemical communications.

[54]  Deryn Chu,et al.  Unraveling Oxygen Reduction Reaction Mechanisms on Carbon-Supported Fe-Phthalocyanine and Co-Phthalocyanine Catalysts in Alkaline Solutions , 2009 .

[55]  Piotr Zelenay,et al.  Recent advances in non-precious metal catalysis for oxygen-reduction reaction in polymer electrolyte fuel cells , 2011 .

[56]  H. Miller,et al.  H2/air alkaline membrane fuel cell performance and durability, using novel ionomer and non-platinum group metal cathode catalyst , 2010 .

[57]  R. Lan,et al.  Anionic membrane and ionomer based on poly(2,6-dimethyl-1,4-phenylene oxide) for alkaline membrane fuel cells , 2011 .

[58]  T. Abe,et al.  Alkaline direct alcohol fuel cells using an anion exchange membrane , 2005 .

[59]  M. Chatenet,et al.  Oxygen reduction on silver catalysts in solutions containing various concentrations of sodium hydroxide – comparison with platinum , 2002 .

[60]  A. Kannan,et al.  Non-platinum cathode catalysts for alkaline membrane fuel cells , 2012 .

[61]  Bin Wang,et al.  Comparison of the Carbonyl and Nitrosyl Complexes Formed by Adsorption of CO and NO on Mono layers of Iron Phthalocyanine on Au(111) , 2011 .

[62]  Anders Widelöv.  Pyrolysis of iron and cobalt porphyrins sublimated onto the surface of carbon black as a method to prepare catalysts for O2 reduction , 1993 .

[63]  K. Scott,et al.  Radiation grafted membranes for superior anion exchange polymer membrane fuel cells performance , 2012 .

[64]  P. Kohl,et al.  Characterization of anion exchange ionomers in hybrid polymer electrolyte fuel cells. , 2010, ChemSusChem.

[65]  Andrew Dicks,et al.  Non precious metal catalysts for the PEM fuel cell cathode , 2012 .

[66]  Gang Wu,et al.  High-Performance Electrocatalysts for Oxygen Reduction Derived from Polyaniline, Iron, and Cobalt , 2011, Science.

[67]  T. Tamm,et al.  Synthesis, EPR and DFF calculations of rare Ag(II)porphyrins and the crystal structure of [Zn(II)tetrakis(4-bromo-2-thiophene)porphyrin] , 2008 .

[68]  Rongrong Chen,et al.  Novel nanostructured high-performance anion exchange ionomers for anion exchange membrane fuel cells , 2012 .