Fabrication of <5 nm width lines in poly(methylmethacrylate) resist using a water:isopropyl alcohol developer and ultrasonically-assisted development

We report on the fabrication of 3–4 nm wide continuous lines in a positive tone electron beam resist poly(methylmethacrylate) on a solid substrate. This narrow linewidth was made possible through the use of a nonsolvent-based developer system, water:isopropyl alcohol, together with ultrasonically-assisted development, which reduced the effective development time thus limiting the swelling of the unexposed resist. This combination of solvent system and development technique results in a smaller radius of gyration in the developing polymer molecules and in a wider exposure dose latitude compared to conventional processing and so allows ultrasmall features to be reproduced.

[1]  C. G. Willson,et al.  Introduction to microlithography , 1994 .

[2]  David K. Ferry,et al.  Effect of molecular weight on poly(methyl methacrylate) resolution , 1996 .

[3]  David G. Hasko,et al.  Characterisation of the ultrasonic development process in UVIII resist , 2000 .

[4]  Shazia Yasin,et al.  Nanolithography using ultrasonically assisted development of calixarene negative electron beam resist , 2001 .

[5]  Nanowriter: A new high‐voltage electron beam lithography system for nanometer‐scale fabrication , 1988 .

[6]  Gary H. Bernstein,et al.  New high-contrast developers for poly(methyl methacrylate) resist , 1992 .

[7]  A. Mumtaz,et al.  Influence of developer and development conditions on the behavior of high molecular weight electron beam resists , 2000 .

[8]  D. Cumming,et al.  Fabrication of 3 nm wires using 100 keV electron beam lithography and poly(methyl methacrylate) resist , 1996 .

[9]  Kenji Yamazaki,et al.  Nanometer-scale linewidth fluctuations caused by polymer aggregates in resist films , 1997 .

[10]  J. Cowie,et al.  Enhanced sensitivity in the electron beam resist poly(methyl methacrylate) using improved solvent developer , 1988 .

[11]  H. Ahmed,et al.  Comparison of sensitivity and exposure latitude for polymethylmethacrylate, UVIII, and calixarene using conventional dip and ultrasonically assisted development , 1999 .

[12]  Wei Chen,et al.  Fabrication of 5–7 nm wide etched lines in silicon using 100 keV electron‐beam lithography and polymethylmethacrylate resist , 1993 .

[13]  H. Elias,et al.  An Introduction to Polymer Science , 1997 .