Relationship between localized strain and irradiation assisted stress corrosion cracking in an austenitic alloy

Abstract Irradiation assisted stress corrosion cracking may be linked to the local slip behavior near grain boundaries that exhibit high susceptibility to cracking. Fe–13Cr–15Ni austenitic steel was irradiated with 2 MeV protons at 360 °C to 5 dpa and strained in 288 °C simulated BWR conditions. Clusters of grains from the experiment were created in an atomistic simulation and then virtually strained using molecular dynamic simulation techniques. Cracking and grain orientation data were characterized in both the experiment and the simulation. Random high angle boundaries with high surface trace angles with respect to the tensile direction were found to be the most susceptible to cracking. Grain boundary cracking susceptibility was also found to correlate strongly with slip continuity, indicating that the strain accommodation at the boundary is related to cracking resistance. Higher cracking susceptibility was also found at grain boundaries adjacent to grains with low Schmid factor or high Taylor factor. The basic trends reported here are supported by both the experiments and the simulations.

[1]  D. Farkas,et al.  Molecular Dynamics Investigation on the Fracture Behavior of Nanocrystalline Fe , 2002 .

[2]  Diana Farkas,et al.  Tensile deformation of fcc Ni as described by an EAM potential , 2009 .

[3]  D. Wolf.  Structure-energy correlation for grain boundaries in F.C.C. metals—I. Boundaries on the (111) and (100) planes , 1989 .

[4]  N. Soneda,et al.  Mechanism of irradiation assisted stress corrosion crack initiation in thermally sensitized 304 stainless steel , 2005 .

[5]  V. Randle,et al.  Microtexture determination by electron back-scatter diffraction , 1992 .

[6]  J. C. Hamilton,et al.  Dislocation nucleation and defect structure during surface indentation , 1998 .

[7]  David L. McDowell,et al.  Atomistic simulations of tension-compression asymmetry in dislocation nucleation for copper grain boundaries , 2008 .

[8]  岸本 喜久雄,et al.  Advances in Fracture and Failure Prevention , 2004 .

[9]  K. Kunze,et al.  Orientation imaging: The emergence of a new microscopy , 1993 .

[10]  Michael J. Mehl,et al.  Interatomic potentials for monoatomic metals from experimental data and ab initio calculations , 1999 .

[11]  J. Busby,et al.  Deformation microstructure of proton-irradiated stainless steels , 2007 .

[12]  D. McDowell,et al.  Dislocation nucleation in Σ3 asymmetric tilt grain boundaries , 2008 .

[13]  J. Schiøtz.  Atomic-scale modeling of plastic deformation of nanocrystalline copper , 2004 .

[14]  Horst Hahn,et al.  Interactions between non-screw lattice dislocations and coherent twin boundaries in face-centered cubic metals , 2008 .

[15]  Sidney Yip,et al.  Atomistic simulations of dislocations and defects , 2002 .

[16]  S. Zinkle,et al.  Mechanisms of stacking fault tetrahedra destruction by gliding dislocations in quenched gold , 2008 .

[17]  D. Farkas.  Fracture mechanisms of symmetrical tilt grain boundaries , 2000 .

[18]  Alfredo Caro,et al.  A molecular dynamics study of polycrystalline fcc metals at the nanoscale: grain boundary structure and its influence on plastic deformation , 2001 .

[19]  S. Zinkle,et al.  The collapse of stacking-fault tetrahedra by interaction with gliding dislocations , 2005 .

[20]  Steve Plimpton,et al.  Fast parallel algorithms for short-range molecular dynamics , 1993 .

[21]  D. McDowell,et al.  Grain boundary dislocation sources in nanocrystalline copper , 2008 .

[22]  D. Farkas,et al.  Effect of dislocation blocking on fracture behavior of Al and α-Fe: a multiscale study , 2004 .

[23]  Z. Jiao,et al.  Impact of localized deformation on IASCC in austenitic stainless steels , 2011 .

[24]  Horst Hahn,et al.  The interaction mechanism of screw dislocations with coherent twin boundaries in different face-centred cubic metals , 2006 .

[25]  Y. Kitsunai,et al.  Deformation Structure in Highly Irradiated Stainless Steels , 2008 .