Preparation and properties of C/C−ZrB2−SiC composites by high-solid-loading slurry impregnation and polymer infiltration and pyrolysis (PIP)

[1]  Lai-fei Cheng,et al.  Oxidation degradation and mechanical reduction on C/SiC composites with artificial notch defects , 2018, Ceramics International.

[2]  Yuehuan Li,et al.  Carbon layer-exfoliated, wettability-enhanced, SO3H-functionalized carbon paper: A superior positive electrode for vanadium redox flow battery , 2018 .

[3]  Q. Fu,et al.  Preparation, ablation behavior and thermal retardant ability of C/C-HfB2-SiC composites , 2017 .

[4]  Xinghong Zhang,et al.  Preparation of ZrB2-SiC ceramics by single-step and optimized two-step hot pressing using nanosized ZrB2 powders , 2017 .

[5]  Q. Fu,et al.  The ablation behavior and mechanical property of C/C-SiC-ZrB2 composites fabricated by reactive melt infiltration , 2017 .

[6]  Hongwei Liu,et al.  Effect of ZrC–SiC content on microstructure and ablation properties of C/C composites , 2016 .

[7]  Qizhong Huang,et al.  Microstructure and ablation behavior of C/C–HfC composites prepared by precursor infiltration and pyrolysis , 2015 .

[8]  S. Bai,et al.  Reactive melt infiltration of a ZrB2 modified C/ZrC composite by a eutectic Zr–B alloy , 2015 .

[9]  Wei Sun,et al.  Preparation and ablation properties of ZrB2–SiC protective laminae for carbon/carbon composites , 2014 .

[10]  Xin Yang,et al.  Pyrolysis mechanism of ZrC precursor and fabrication of C/C-ZrC composites by precursor infiltration and pyrolysis , 2014 .

[11]  Hejun Li,et al.  Effect of heat flux on ablation behaviour and mechanism of C/C–ZrB2–SiC composite under oxyacetylene torch flame , 2013 .

[12]  孟祥利,et al.  浆料浸渍法制备C/C-SiC-ZrB2超高温复合材料及其烧蚀性能研究 , 2013 .

[13]  Jiaping Zhang,et al.  SiC–MoSi2/ZrO2–MoSi2 coating to protect C/C composites against oxidation , 2013 .

[14]  Ping Hu,et al.  Preparation of high solid loading, low viscosity ZrB2–SiC aqueous suspensions using PEI as dispersant , 2013 .

[15]  L. Chai,et al.  Preparation and oxidation resistance of mullite/SiC coating for carbon materials at 1150 °C , 2012 .

[16]  Xinghong Zhang,et al.  Gelcasting of complex-shaped ZrB2–SiC ultra high temperature ceramic components , 2012 .

[17]  Yue Zhang,et al.  Formation Mechanism of Zircon Phase in ZrB 2 -SiC Ceramic Composites during Oxidation: Formation Mechanism of Zircon Phase in ZrB 2 -SiC Ceramic Composites during Oxidation , 2011 .

[18]  Hejun Li,et al.  Ablation of the carbon/carbon composite nozzle-throats in a small solid rocket motor , 2011 .

[19]  Lai-fei Cheng,et al.  Preparation and properties of 2D C/SiC–ZrB2–TaC composites , 2011 .

[20]  William E Lee,et al.  Reactive infiltration processing (RIP) of ultra high temperature ceramics (UHTC) into porous C/C composite tubes , 2011 .

[21]  H. Hu,et al.  Preparation and characterization of C/SiC–ZrB2 composites by precursor infiltration and pyrolysis process , 2010 .

[22]  C. Hong,et al.  Ablation behavior of ZrB2–SiC–ZrO2 ceramic composites by means of the oxyacetylene torch , 2009 .

[23]  Y. Leong,et al.  Interparticle forces in spherical monodispersed silica dispersions: effects of branched polyethylenimine and molecular weight. , 2009, Journal of colloid and interface science.

[24]  Lai-fei Cheng,et al.  Ablation Resistance of Different Coating Structures for C/ZrB2–SiC Composites Under Oxyacetylene Torch Flame , 2009 .

[25]  Jingyi Deng,et al.  Comparison of thermal and ablation behaviors of C/SiC composites and C/ZrB2–SiC composites , 2009 .

[26]  G. Hilmas,et al.  Enhanced densification and mechanical properties of ZrB2–SiC processed by a preceramic polymer coating route , 2008 .

[27]  Jiecai Han,et al.  Oxidation-resistant ZrB2-SiC composites at 2200 °C , 2008 .

[28]  Ke Yang,et al.  Mechanical and ablation properties of 2D-carbon/carbon composites pre-infiltrated with a SiC filler , 2006 .

[29]  Soojin Park,et al.  Influence of molybdenum disilicide filler on carbon-carbon composites , 1999 .

[30]  H. C. Graham,et al.  Thermogravi metric Study of the Oxidation of ZrB2 in the Temperature Range of 800° to 1500°C , 1971 .