Magnetization reversal in patterned Co(0001) ultrathin films with perpendicular magnetic anisotropy

Using x‐ray lithography we have patterned dot arrays in Au/Co/Au(111) sandwiches based on ultrathin Co layers with perpendicular anisotropy. Large area arrays of dots with diameters of 1 and 2 μm have been obtained, keeping mostly undamaged the ultrathin Co layer. Hysteresis loops of the arrays depend drastically on the dot diameter. Magneto‐optical domain visualization experiments confirm a magnetization reversal mechanism based on a large distribution of nucleation fields in the film, with complete reversal of the magnetization of one dot through the domain wall propagation after a local nucleation process. This could give information on the magnetization reversal processes in Au/Co/Au(111) continuous films.

[1]  C. Chappert,et al.  Study of large area high density magnetic dot arrays fabricated using synchrotron radiation based x‐ray lithography , 1995 .

[2]  Suzuki,et al.  Magneto-optical-Kerr-effect study of spin-polarized quantum-well states in a Au overlayer on a Co(0001) ultrathin film. , 1995, Physical review. B, Condensed matter.

[3]  S. Gider,et al.  Properties and measurement of scanning tunneling microscope fabricated ferromagnetic particle arrays (invited) , 1994 .

[4]  J. K. Erwin,et al.  Effect of grooves on magnetization reversal in amorphous TbFeCo thin films , 1994 .

[5]  Franck Carcenac,et al.  50‐nm x‐ray lithography using synchrotron radiation , 1994 .

[6]  S. Chou,et al.  Fabrication of single‐domain magnetic pillar array of 35 nm diameter and 65 Gbits/in.2 density , 1994 .

[7]  J. Jupille,et al.  The van der Waals contribution to the adhesion energy at metal-oxide interfaces , 1994 .

[8]  Franck Carcenac,et al.  A 100‐nm patterned x‐ray mask technology based on amorphous SiC membranes , 1990 .

[9]  Meyer,et al.  Magnetization reversal in ultrathin ferromagnetic films with perpendicular anistropy: Domain observations. , 1990, Physical review letters.

[10]  J. Faure,et al.  Magnetic properties of ferromagnetic thin sandwiches correlated to their crystallographic structure and interface morphology: HREM and NMR study , 1989 .

[11]  C. Chappert,et al.  In Situ Rheed and Magneto-Optic Study of Ultrathin Cobalt Films on (111) Gold Substrate: Effect of a Metallic Overlayer , 1993 .