Morphology of OLED Film Stacks Containing Solution-Processed Phosphorescent Dendrimers.

Organic light-emitting devices containing solution-processed emissive dendrimers can be highly efficient. The most efficient devices contain a blend of the light-emitting dendrimer in a host and one or more charge-transporting layers. Using neutron reflectometry measurements with in situ photoluminescence, we have investigated the structure of the as-formed film as well as the changes in film structure and dendrimer emission under thermal stress. It was found that the as-formed film stacks comprising poly(3,4-ethylenedioxythiophene):polystyrene sulfonate/host:dendrimer/1,3,5-tris(N-phenylbenzimidazol-2-yl)benzene (where the host was deuterated 4,4'-N,N'-di(carbazolyl)biphenyl or tris(4-carbazol-9-ylphenyl)amine, the host:dendrimer layer was solution-processed, and the 1,3,5-tris(N-phenylbenzimidazol-2-yl)benzene evaporated) had well-defined interfaces, indicating good wetting of each of the layers by the subsequently deposited layer. Upon thermal annealing, there was no change in the poly(3,4-ethylenedioxythiophene):polystyrene sulfonate/host:dendrimer interface, but once the temperature reached above the Tg of the host:dendrimer layer, it became a supercooled liquid into which 1,3,5-tris(N-phenylbenzimidazol-2-yl)benzene dissolved. When the film stacks were held at a temperature just above the onset of the diffusion process, they underwent an initial relatively fast diffusion process before reaching a quasi-stable state at that temperature.

[1]  Baohua Zhang,et al.  Solution-processed multilayer green electrophosphorescent devices with self-host iridium dendrimers as the nondoped emitting layer: achieving high efficiency while avoiding redissolution-induced batch-to-batch variation. , 2017, Chemical communications.

[2]  Jie Zhang,et al.  Deep-blue thermally activated delayed fluorescence dendrimers with reduced singlet-triplet energy gap for low roll-off non-doped solution-processed organic light-emitting diodes , 2017 .

[3]  I. Gentle,et al.  Dependence of Organic Interlayer Diffusion on Glass-Transition Temperature in OLEDs. , 2017, ACS applied materials & interfaces.

[4]  J. Kido,et al.  Influence of solution- and thermal-annealing processes on the sub-nanometer-ordered organic-organic interface structure of organic light-emitting devices. , 2017, Nanoscale.

[5]  X. Jing,et al.  Self-Host Blue-Emitting Iridium Dendrimer Containing Bipolar Dendrons for Nondoped Electrophosphorescent Devices with Superior High-Brightness Performance. , 2016, ACS applied materials & interfaces.

[6]  T. Darwish,et al.  Diffusion at Interfaces in OLEDs Containing a Doped Phosphorescent Emissive Layer , 2016 .

[7]  Phosphorescence quenching of fac-tris(2-phenylpyridyl)iridium(iii) complexes in thin films on dielectric surfaces. , 2016, Physical chemistry chemical physics : PCCP.

[8]  J. Kido,et al.  Molecular Interdiffusion between Stacked Layers by Solution and Thermal Annealing Processes in Organic Light Emitting Devices. , 2015, ACS applied materials & interfaces.

[9]  J. Kido,et al.  Precise Evaluation of Angstrom‐Ordered Mixed Interfaces in Solution‐Processed OLEDs by Neutron Reflectometry , 2014 .

[10]  I. Gentle,et al.  Diffusion – the Hidden Menace in Organic Optoelectronic Devices , 2012, Advanced materials.

[11]  Jeremy L. Ruggles,et al.  Investigating Morphology and Stability of Fac‐tris (2‐phenylpyridyl)iridium(III) Films for OLEDs , 2011 .

[12]  F. Klose,et al.  The multipurpose time-of-flight neutron reflectometer “Platypus” at Australia's OPAL reactor , 2011 .

[13]  Andrew Nelson,et al.  Motofit – integrating neutron reflectometry acquisition, reduction and analysis into one, easy to use, package , 2010 .

[14]  S. Gambino,et al.  Light-emitting dendrimer film morphology: A neutron reflectivity study , 2010 .

[15]  Jiuyan Li,et al.  Dendrimers for organic light-emitting diodes , 2009 .

[16]  S. Gambino,et al.  Control of Charge Transport in Iridium(III) Complex‐Cored Carbazole Dendrimers by Generation and Structural Modification , 2009 .

[17]  Ta-Ya Chu,et al.  A morphologically stable host material for efficient phosphorescent green and red organic light emitting devices , 2008 .

[18]  W. Brostow,et al.  Prediction of glass transition temperatures: Binary blends and copolymers , 2008 .

[19]  P. Burn,et al.  Development of Dendrimers: Macromolecules for Use in Organic Light-Emitting Diodes and Solar Cells , 2007 .

[20]  I. Samuel,et al.  The Development of Light‐Emitting Dendrimers for Displays , 2007 .

[21]  Chung-Chih Wu,et al.  3-(9-Carbazolyl)carbazoles and 3,6-Di(9-carbazolyl)carbazoles as Effective Host Materials for Efficient Blue Organic Electrophosphorescence** , 2007 .

[22]  A. Nelson,et al.  Platypus: a time-of-flight neutron reflectometer at Australia’s new research reactor , 2006 .

[23]  Andrew Nelson,et al.  Co-refinement of multiple-contrast neutron/X-ray reflectivity data using MOTOFIT , 2006 .

[24]  E. Namdas,et al.  Solution‐Processable Red Phosphorescent Dendrimers for Light‐Emitting Device Applications , 2004 .

[25]  E. Namdas,et al.  Synthesis and properties of highly efficient electroluminescent green phosphorescent iridium cored dendrimers , 2003 .

[26]  Ifor D. W. Samuel,et al.  Green Phosphorescent Dendrimer for Light‐Emitting Diodes , 2002 .

[27]  I. Samuel,et al.  CONJUGATED DENDRIMERS FOR LIGHT-EMITTING DIODES : EFFECT OF GENERATION , 1999 .

[28]  Mark E. Thompson,et al.  Asymmetric Triaryldiamines as Thermally Stable Hole Transporting Layers for Organic Light-Emitting Devices , 1998 .