3D printed continuous fibre-reinforced composites: Bio-inspired microstructures for improving the translaminar fracture toughness

Abstract Translaminar fracture toughness is a vital property governing the notch sensitivity and damage tolerance of composites. Nature has shown that incorporating material transitions can increase toughness significantly. This work presents finite element models demonstrating that such transitions can indeed increase the translaminar fracture toughness. The designed microstructures were then 3D printed using continuous glass and carbon fibres. The specimens consisted primarily of glass fibres, but with local carbon fibre strips. A new compact tension specimen with a side groove was designed to ensure proper failure. When the strips were sufficiently large, toughness improvements of 20–60% were found after the crack had grown through the strips. These results reveal a powerful strategy for locally increasing the toughness in areas where it is needed the most.

[1]  C. C. Chamis,et al.  Simplified composite micromechanics equations for hygral, thermal and mechanical properties , 1983 .

[2]  L. Gorbatikh,et al.  Recent advances in fibre-hybrid composites: materials selection, opportunities and applications , 2019 .

[3]  R. Ritchie,et al.  Bioinspired structural materials. , 2014, Nature materials.

[4]  S. Pinho,et al.  Translaminar fracture toughness: The critical notch tip radius of 0° plies in CFRP , 2011 .

[5]  D. Lin,et al.  A review on additive manufacturing of polymer-fiber composites , 2017 .

[6]  Xin Wang,et al.  3D printing of polymer matrix composites: A review and prospective , 2017 .

[7]  J. Botsis,et al.  Mode I interlaminar fracture of carbon epoxy laminates: Effects of ply thickness , 2016 .

[8]  E. V. González,et al.  Translaminar fracture toughness of interply hybrid laminates under tensile and compressive loads , 2017 .

[9]  L. P. Canal,et al.  Large scale fiber bridging in mode I intralaminar fracture. An embedded cell approach , 2016 .

[10]  S. Pinho,et al.  An analytical model for the translaminar fracture toughness of fibre composites with stochastic quasi-fractal fracture surfaces , 2014 .

[11]  K. Kedward,et al.  MODELING AND ASSESSMENT OF INTEGRAL CRACK ARREST ZONES IN CFRP LAMINATES , 2007 .

[12]  S. Pinho,et al.  Engineering the translaminar fracture behaviour of thin-ply composites , 2016 .

[13]  O. Kolednik,et al.  Improving strength and toughness of materials by utilizing spatial variations of the yield stress , 2017 .

[14]  S. Pinho,et al.  Intralaminar fracture toughness characterisation of woven composite laminates. Part I: Design and analysis of a compact tension (CT) specimen , 2014 .

[15]  Otmar Kolednik,et al.  The mechanics of tessellations - bioinspired strategies for fracture resistance. , 2016, Chemical Society reviews.

[16]  Pedro P. Camanho,et al.  Determination of the mode I crack resistance curve of polymer composites using the size-effect law , 2014 .

[17]  P. Fratzl,et al.  Bioinspired Design Criteria for Damage‐Resistant Materials with Periodically Varying Microstructure , 2011 .

[18]  Silvestre T. Pinho,et al.  Translaminar fracture toughness testing of composites: A review , 2012 .

[19]  Arash E. Zaghi,et al.  Mechanical Behavior of Hybrid Glass/Steel Fiber Reinforced Epoxy Composites , 2017, Polymers.

[20]  M. Wisnom,et al.  Pseudo-ductility and reduced notch sensitivity in multi-directional all-carbon/epoxy thin-ply hybrid composites , 2018 .

[21]  Joshua M. Pearce,et al.  Anisotropic mechanical property variance between ASTM D638-14 type i and type iv fused filament fabricated specimens , 2018, Polymer Testing.

[22]  S. Pinho,et al.  Intralaminar fracture toughness characterisation of woven composite laminates. Part II: Experimental characterisation , 2014 .

[23]  Peter Davies,et al.  Standard Test Methods for Delamination Resistance of Composite Materials: Current Status , 1998 .

[24]  J. M. Kennedy,et al.  An Assessment of Buffer Strips for Improving Damage Tolerance of Composite Laminates , 1980 .

[25]  R. Ritchie.  The conflicts between strength and toughness. , 2011, Nature materials.

[26]  Ian A. Ashcroft,et al.  Design framework for multifunctional additive manufacturing: coupled optimization strategy for structures with embedded functional systems , 2017 .

[27]  S. Pinho,et al.  Thickness-dependence of the translaminar fracture toughness: Experimental study using thin-ply composites , 2016 .

[28]  L. Gorbatikh,et al.  Stress concentrations in an impregnated fibre bundle with random fibre packing , 2013 .

[29]  O. Kolednik,et al.  Improvement of fatigue life by compliant and soft interlayers , 2016 .

[30]  S. Pinho,et al.  Exploiting nacre-inspired crack deflection mechanisms in CFRP via micro-structural design , 2017 .

[31]  G. Rizvi,et al.  Effect of processing conditions on the bonding quality of FDM polymer filaments , 2008 .

[32]  Yentl Swolfs,et al.  Fibre hybridisation in polymer composites: a review , 2014 .

[33]  Robert Malkin,et al.  Bio-inspired laminate design exhibiting pseudo-ductile (graceful) failure during flexural loading , 2013 .

[34]  S. Pinho,et al.  The importance of translaminar fracture toughness for the penetration impact behaviour of woven carbon/glass hybrid composites , 2017 .