Thermal ageing degradation mechanisms on compressive behavior of 3-D braided composites in experimental and numerical study

Abstract This paper reports the thermal ageing degradation mechanisms on compressive damage behaviors of pure epoxy resin and 3-D carbon fiber/epoxy braided composites. The epoxy resin and the 3-D braided composite have been aged in air for 1, 2, 4, 8, and 16 days at 180 °C. The compressive testing results and the scanning electron microscope (SEM) observations revealed that the epoxy resin degradation only occurred within regions close to surface layer. The inner parts of the epoxy resin were protected from the ageing oxidation by the outside oxidized layer. The compressive behaviors degradation of the braided composite is attributed to the epoxy resin degradation and interface debonding. The numerical study (Finite element analysis, FEA) illustrates the interface crack propagation. The interface degradation and crack propagation are the main mechanisms of the compressive behaviors degradation after the several-day’s high temperature ageing.

[1]  Anthony M. Waas,et al.  Compressive response of Z-pinned woven glass fiber textile composite laminates: Modeling and computations , 2009 .

[2]  B. Lee,et al.  Effects of moisture and thermal cycling on in-plane shear properties of graphite fibre-reinforced cyanate ester resin composites , 1996 .

[3]  Zengping Zhang,et al.  Thermodegradation kinetics of epoxy/DDS/POSS system , 2007 .

[4]  Adrian P. Mouritz,et al.  Review of applications for advanced three-dimensional fibre textile composites , 1999 .

[5]  P. Xue,et al.  Compressive behavior of C/SiC composites over a wide range of strain rates and temperatures , 2013 .

[6]  S. Keller,et al.  Aging of polymeric composite specimens for 5000 hours at elevated pressure and temperature , 2001 .

[7]  Jialu Li,et al.  Effects of heat accelerated aging on tensile strength of three dimensional braided/epoxy resin composites , 2012 .

[8]  G. Lacombe,et al.  Thermal expansion coefficient and thermal fatigue of discontinuous carbon fiber-reinforced copper and aluminum matrix composites without interfacial chemical bond , 2013, Journal of Materials Science.

[9]  J. Grandidier,et al.  The effect of thermo-oxidation on the mechanical behaviour of polymer epoxy materials , 2013 .

[10]  M. Benzeggagh,et al.  Measurement of mixed-mode delamination fracture toughness of unidirectional glass/epoxy composites with mixed-mode bending apparatus , 1996 .

[11]  T. Tsotsis.  Long-Term Thermo-Oxidative Aging in Composite Materials: Experimental Methods , 1998 .

[12]  W. Kuo,et al.  Compressive Damage in Filament-Wound Carbon/Carbon Composites , 2009 .

[13]  S. Nutt,et al.  Thermal aging of fiberglass/carbon-fiber hybrid composites , 2009 .

[14]  J. Cano,et al.  Decomposition behavior of epoxy-resin systems cured by diamines , 2000 .

[15]  Xavier Colin,et al.  A new method for predicting the thermal oxidation of thermoset matrices: Application to an amine crosslinked epoxy , 2001 .

[16]  N. K. Naik,et al.  An analytical model for compressive strength of plain weave fabric composites , 2003 .

[17]  Wei Fan,et al.  Influence of thermo-oxidative aging on the impact property of conventional and graphene-based carbon fabric composites , 2015 .

[18]  R. Byron Pipes,et al.  Digital image correlation measurement of resin chemical and thermal shrinkage after gelation , 2015, Journal of Materials Science.

[19]  N. Hancox.  Thermal effects on polymer matrix composites: Part 2. Thermal degradation , 1998 .

[20]  Shaw-Ming Lee,et al.  Long-term thermo-oxidative aging in composite materials: Failure mechanisms , 1998 .

[21]  K. Shivakumar,et al.  Effect of Thermal Fatigue on Tensile and Flexural Properties of Carbon/Cyanate Ester Pultruded Composite , 2009 .

[22]  B. Gu,et al.  Experimental and numerical analyses of the mechanical behaviors of three-dimensional orthogonal woven composites under compressive loadings with different strain rates , 2014 .

[23]  T. Tsotsis.  5 – Thermo-oxidative ageing of composite materials , 2008 .

[24]  David Stifter,et al.  An investigation of the accelerated thermal degradation of different epoxy resin composites using X-ray microcomputed tomography and optical coherence tomography , 2009 .

[25]  P. Budrugeac,et al.  Accelerated thermal aging of glass-reinforced epoxy resin under oxygen pressure , 1991 .

[26]  T. Tsotsis.  Thermo-Oxidative Aging of Composite Materials , 1995 .

[27]  Wei Zhang,et al.  Effects of temperature and strain rate on impact compression behaviors of three-dimensional carbon fiber/epoxy braided composites , 2015 .

[28]  Zheng-Ming Huang,et al.  A bridging model prediction of the ultimate strength of composite laminates subjected to biaxial loads , 2004 .