Thermomechanical fatigue life prediction in gas turbine superalloys : a fracture mechanics approach

A model is presented that was developed to predict thermomechanical fatigue crack initiation and estimate mode I crack growth of gas turbine hot section gas path superalloys. The model is based on a strain energy density fracture mechanics approach modified to account for thermal exposure and single crystal anisotropy. Thermomechanical fatigue crack initiation and small crack growth is modeled by employing an initial material defect size. Model capability was quantified by applying the model to two hot section gas path superalloys: uncoated MAR-M509 and MCrAlY overlay coated PWA 1480. Thermomechanical fatigue model stresses were obtained from nonlinear finite element analysis of thermomechanical fatigue specimen strain-temperature history. Nonlinear stress-strain behavior was predicted using unified viscoplastic constitutive models. Model thermomechanical fatigue life predictions were in good agreement with observed uniaxial thermomechanical fatigue specimen lives. Thermomechanical fatigue cracking effects captured by the model included coating thickness, single crystal anisotropy, cycle waveshape, dwell, and thermal exposure. 45 refs.

[1]  M. E. Haddad,et al.  Fatigue Crack Propagation of Short Cracks , 1979 .

[2]  Henry L. Bernstein,et al.  Analysis of Cracked Gas Turbine Blades , 1991 .

[3]  J. Rice.  A path-independent integral and the approximate analysis of strain , 1968 .

[4]  F. Erdogan,et al.  Application of the line-spring model to a cylindrical shell containing a circumferential or axial part-through crack , 1982 .

[5]  John W. Hutchinson,et al.  Fully Plastic Solutions and Large Scale Yielding Estimates for Plane Stress Crack Problems , 1976 .

[6]  Huseyin Sehitoglu,et al.  Thermomechanical fatigue, oxidation, and creep: Part i. Damage mechanisms , 1989 .

[7]  T. A. Cruse,et al.  Thermal Barrier Coating Life Prediction Model Development , 1988 .

[8]  Ne Dowling,et al.  Geometry effects and the J-integral approach to elastic-plastic fatigue crack growth , 1976 .

[9]  L. Rémy,et al.  THERMAL-MECHANICAL FATIGUE OF MAR-M 509 SUPERALLOY. COMPARISON WITH LOW-CYCLE FATIGUE BEHAVIOUR , 1991 .

[10]  CLOSURE EFFECTS IN SHORT AND LONG FATIGUE CRACKS , 1984 .

[11]  N. Dowling.  Crack Growth During Low-Cycle Fatigue of Smooth Axial Specimens , 1977 .

[12]  K. P. Walker,et al.  Research and development program for non-linear structural modeling with advanced time-temperature dependent constitutive relationships , 1981 .

[13]  J. Heine,et al.  Thermal Mechanical Fatigue of Coated Blade Materials , 1989 .

[14]  J. Newman.  A crack opening stress equation for fatigue crack growth , 1984 .

[15]  E. Jordan,et al.  Fracture Mechanics Applied to Elevated Temperature Crack Growth , 1989 .

[16]  J. Gallagher,et al.  A Review of Nonlinear Fracture Mechanics Relative to Fatigue , 1979 .

[17]  W. J. Ostergren,et al.  A DAMAGE FUNCTION AND ASSOCIATED FAILURE EQUATIONS FOR PREDICTING HOLD TIME AND FREQUENCY EFFECTS IN ELEVATED TEMPERATURE, LOW CYCLE FATIGUE , 1976 .

[18]  K. J. Miller,et al.  MODELLING SMALL FATIGUE CRACKS INTERACTING WITH GRAIN BOUNDARIES , 1991 .

[19]  V. Moreno,et al.  Creep fatigue life prediction for engine hot section materials (isotropic): Two year update , 1983 .

[20]  On the significance of the threshold for fatigue crack growth , 1984 .

[21]  H. Sehitoglu,et al.  Thermo-Mechanical Fatigue of Mar-M247: Part 1—Experiments , 1990 .

[22]  H. Mughrabi,et al.  ASPECTS OF HIGH‐TEMPERATURE LOW‐CYCLE THERMOMECHANICAL FATIGUE OF A SINGLE CRYSTAL NICKEL‐BASE SUPERALLOY , 1993 .

[23]  K. Sadananda,et al.  A fracture mechanics approach to high temperature fatigue crack growth in Udimet 700 , 1979 .

[24]  A. K. Rao,et al.  On the stress problem of large elliptical cutouts and cracks in circular cylindrical shells , 1974 .

[25]  Gr Leverant,et al.  Thermal-Mechanical Fatigue Crack Propagation in Nickel- and Cobalt-Base Superalloys Under Various Strain-Temperature Cycles , 1973 .

[26]  L. Rémy,et al.  Influence of microstructure on the thermal fatigue behavior of a cast cobalt-base superalloy , 1990 .

[27]  H. Sehitoglu,et al.  Thermo-Mechanical Fatigue of Mar-M247: Part 2—Life Prediction , 1990 .

[28]  J. Newman,et al.  Stress-intensity factor equations for cracks in three-dimensional finite bodies subjected to tension and bending loads , 1984 .