Refined fatigue assessment of joints with welded in-plane attachments by LEFM

The fatigue life of joints with welded in-plane gusset plates is studied. The purpose is to suggest a descriptive detail category to be used in assessment of existing structures. Linear elastic fracture mechanics is used together with fictitious initial crack depths to predict the fatigue life. By calibrating the fictitious crack depths to real fatigue tests and simulating new test results, fatigue strengths dependent on the dimensions of the joint have been derived. The results show that a decreasing length and thickness of the gusset give decreasing stress intensity and higher fatigue strength. A numerical example is presented showing the merit of the proposed strengths in fatigue life. (C) 2013 Elsevier Ltd. All rights reserved.

[1]  R. D. Henshell,et al.  CRACK TIP FINITE ELEMENTS ARE UNNECESSARY , 1975 .

[2]  H. Saunders,et al.  Probabilistic Fracture Mechanics and Fatigue Methods—Applications for Structural Design of Maintenance , 1983 .

[3]  Go Johnston.  Statistical Scatter in Fracture Toughness and Fatigue Crack Growth Rate Data , 1983 .

[4]  Timothy Russell Gurney,et al.  Fatigue of Welded Structures , 1980 .

[5]  P. Paris.  A rational analytic theory of fatigue , 1961 .

[6]  Andreas Andersson,et al.  Monitoring and enhanced fatigue evaluation of a steel railway bridge , 2010 .

[7]  Donald B. Owen,et al.  Survey of Properties and Applications of the Noncentral t-Distribution , 1968 .

[8]  Michael Levén,et al.  Stationary 3D crack analysis with Abaqus XFEM for integrity assessment of subsea equipment , 2012 .

[9]  Yongming Liu,et al.  Probabilistic fatigue life prediction using an equivalent initial flaw size distribution , 2009 .

[10]  F. M. Burdekin,et al.  Engineering critical analyses to BS 7910 — the UK guide on methods for assessing the acceptability of flaws in metallic structures , 2000 .

[11]  H. Y. Choi,et al.  Fatigue life prediction of out-of-plane gusset welded joints using strain energy density factor approach , 2005 .

[12]  John Dalsgaard Sørensen,et al.  A probabilistic damage tolerance concept for welded joints. Part 1: data base and stochastic modelling , 2002 .

[13]  S. J. Maddox,et al.  Fatigue strength of welded structures , 1991 .

[14]  Dawn E. Lehman,et al.  Improved Seismic Performance of Gusset Plate Connections , 2008 .

[15]  Pedro Albrecht,et al.  RAPID CALCULATION OF STRESS INTENSITY FACTORS , 1977 .

[16]  C.-Y. Hou,et al.  Models for the estimation of weldment fatigue crack initiation life , 1997 .

[17]  H. W. Kerr,et al.  Growth and coalescence of fatigue cracks at weld toes in steel , 1991 .

[18]  R. Barsoum.  Triangular quarter‐point elements as elastic and perfectly‐plastic crack tip elements , 1977 .

[19]  M-H Kim,et al.  Testing and analysis of fatigue behaviour in edge details: A comparative study using hot spot and structural stresses , 2008 .

[20]  John Dalsgaard Sørensen,et al.  Fatigue analysis of load-carrying fillet welds , 2006 .

[21]  A. Hobbacher.  Stress intensity factors of plates under tensile load with welded-on flat side gussets , 1992 .

[22]  Ted Belytschko,et al.  Elastic crack growth in finite elements with minimal remeshing , 1999 .

[23]  Gian A. Rassati,et al.  Numerical simulation of gusset plate connections with rectangular hollow section shape brace under quasi-static cyclic loading , 2012 .

[24]  D. Radaj,et al.  Review of fatigue strength assessment of nonwelded and welded structures based on local parameters , 1996 .

[25]  F. V. Lawrence,et al.  Estimating the fatigue crack initiation life of welds , 1978 .

[26]  Mohammad Al-Emrani,et al.  A comparative study of different fatigue failure assessments of welded bridge details , 2013 .

[27]  Ian F. C. Smith,et al.  Fatigue crack growth in a fillet welded joint , 1983 .

[28]  David W. Hoeppner.  Fatigue Testing of Weldments , 1978 .

[29]  Tom Lassen,et al.  Fatigue Life Analyses of Welded Structures , 2006 .

[30]  Mustafa Aygül.  Fatigue Analysis Of Welded Structures Using The Finite Element Method , 2012 .

[31]  K. Miller.  THE SHORT CRACK PROBLEM , 1982 .

[32]  Ted Belytschko,et al.  A finite element method for crack growth without remeshing , 1999 .

[33]  H. O. Fuchs,et al.  Metal fatigue in engineering , 2001 .

[34]  Masahiro Toyosada,et al.  Numerical simulations of fatigue crack initiation and propagation based on re-tensile plastic zone generating load criterion for in-plane gusset welded joints , 2009 .