The directional solidification of polypropylene (PP) films results in an oriented semicrystalline microstructure and may offer a method to improve the properties of a product. The directional solidification of isotactic PP samples blended with 0% to 50% atactic PP, by mass, was therefore studied. The effects of composition and processing conditions were monitored to determine how they affect the quality and microstructure of the directionally solidified films. Difficulty was encountered in reproducing testable samples with a unidirectional crystal microstructure. Tensile testing of directionally solidified films was used to quantify the yield strength and elastic modulus of the films. These properties were compared with those of other PP films. The tensile test results do not support the hypothesis that enhanced mechanical properties were produced by directional solidification of the PP films. Improving the sample fabrication method and optimizing the processes involved may, however, lead to directionally solidified PP films with enhanced mechanical properties.
[1]
H. D. Keith,et al.
Spherulitic Crystallization from the Melt. I. Fractionation and Impurity Segregation and Their Influence on Crystalline Morphology
,
1964
.
[2]
A. J. Lovinger,et al.
Model for the shape of polymer spherulites formed in a temperature gradient
,
1976
.
[3]
A. J. Lovinger,et al.
Studies on the α and β forms of isotactic polypropylene by crystallization in a temperature gradient
,
1977
.
[4]
H. Janeschitz-Kriegl,et al.
Crystallization processes in quiescent and moving polymer melts under heat transfer conditions
,
1990
.
[5]
S. Advani,et al.
Solidification of semicrystalline polymers using a variable interface temperature model
,
1996
.
[6]
S. Advani,et al.
A cell model to describe the spherulitic growth in semicrystalline polymers
,
1996
.