Influence of the RF Excitation of the Catalyst System on the Morphology of Multiwalled Carbon Nanotubes

Multiwalled carbon nanotubes were synthesized by catalytic chemical vapor deposition using two different methods of heating. By one method, an external resistive tube furnace was used, whereas the other method involved heating with radio frequency excitation by induction coil. A comprehensive comparison was made between these two methods with regards to feed gas utilization, nanotube growth efficiency, nanotube product characterization and morphology, and the formation of amorphous carbon and gaseous byproducts. The carbon nanotubes synthesized using radio frequency excitation exhibited smaller outer diameters, fewer carbon layers, less amorphous carbon, and superior crystalline properties than those produced by external tube furnace. The radio frequency process resulted in more rapid and sustained growth rates of the nanotubes and more efficient use of the carbon source. The reason for these enhanced effects by inductive heating may be due not only to the internally produced thermodynamic heat flow characteristics but perhaps also to induced electron currents generated within the magnetic and metallic catalytic clusters due to RF.

[1]  Z. Rahman,et al.  Analysis of effluent gases during the CCVD growth of multi-wall carbon nanotubes from acetylene , 2006 .

[2]  H. Schlegel,et al.  THE ORIGIN OF THE BARRIERS TO THERMALLY ALLOWED, SIX-ELECTRON, PERICYCLIC REACTIONS: THE EFFECT OF HOMO-HOMO INTERACTIONS ON THE TRIMERIZATION OF ACETYLENE , 1985 .

[3]  L. Forró,et al.  CVD synthesis of high-purity multiwalled carbon nanotubes using CaCO3 catalyst support for large-scale production , 2003 .

[4]  K. Vecchio,et al.  Thermogravimetric analysis of synthesis variation effects on CVD generated multiwalled carbon nanotubes. , 2006, The journal of physical chemistry. B.

[5]  Riichiro Saito,et al.  Raman spectroscopy on isolated single wall carbon nanotubes , 2002 .

[6]  A. Rinzler,et al.  SINGLE-WALL NANOTUBES PRODUCED BY METAL-CATALYZED DISPROPORTIONATION OF CARBON MONOXIDE , 1996 .

[7]  V. V. Chesnokov,et al.  The Relationship between the State of Active Species in a Ni/Al2O3Catalyst and the Mechanism of Growth of Filamentous Carbon , 2001 .

[8]  A. S. Biris,et al.  Growth of Nanoscale Carbon Structures and Their Corresponding Hydrogen Uptake Properties , 2002 .

[9]  W. Chiu,et al.  Growth kinetics and microstructure of carbon nanotubes using open air laser chemical vapor deposition , 2006 .

[10]  Yongdan Li,et al.  Methane decomposition to carbon nanotubes and hydrogen on an alumina supported nickel aerogel catalyst , 2002 .

[11]  H. Shinohara,et al.  Control of diameter distribution of single-walled carbon nanotubes using the zeolite-CCVD method at atmospheric pressure , 2005 .

[12]  I. Kiricsi,et al.  On the role of catalyst, catalyst support and their interaction in synthesis of carbon nanotubes by CCVD , 2003 .

[13]  S. Iijima.  Helical microtubules of graphitic carbon , 1991, Nature.

[14]  L. Duclaux,et al.  Synthesis of high quality multi-walled carbon nanotubes from the decomposition of acetylene on iron-group metal catalysts supported on MgO , 2002 .

[15]  R. Little.  Mechanistic Aspects of Carbon Nanotube Nucleation and Growth , 2003 .

[16]  A. Kawabata,et al.  Growth of diameter-controlled carbon nanotubes using monodisperse nickel nanoparticles obtained with a differential mobility analyzer , 2003 .

[17]  J. Nagy,et al.  Synthesis of single-wall carbon nanotubes by catalytic decomposition of hydrocarbons , 1999 .

[18]  Lizhen Gao,et al.  Carbon nanotube growth on Ni-particles prepared in situ by reduction of La2NiO4 , 2001 .

[19]  L. Olenic,et al.  Carbon nanostructures produced by CCVD with induction heating , 2004 .

[20]  Growing carbon nanotubes , 2004 .