Numerical Modeling of Nonuniform Corrosion-Induced Concrete Crack Width

AbstractCorrosion of reinforced concrete is one of the major deterioration mechanisms that results in premature failure of the reinforced concrete structures. In practice, concrete crack width is o...

[1]  A. Brás,et al.  Corrosion inhibitors’ effect on design service life of RC structures , 2014 .

[2]  N. Otsuki,et al.  Influences of Bending Crack and Water-Cement Ratio on Chloride-Induced Corrosion of Main Reinforcing Bars and Stirrups , 2000 .

[3]  A. Hillerborg,et al.  Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements , 1976 .

[4]  Hao Huang,et al.  Safety Monitoring of a Super-High Dam Using Optimal Kernel Partial Least Squares , 2015 .

[5]  Dirk S. Reischl,et al.  DEM simulation of concrete fracture and crack evolution , 2012 .

[6]  H. Nguyen-Xuan,et al.  A simple and robust three-dimensional cracking-particle method without enrichment , 2010 .

[7]  Kefei Li,et al.  Analytical model for non-uniform corrosion-induced concrete cracking , 2018 .

[8]  Weiliang Jin,et al.  Comparison of uniform and non-uniform corrosion induced damage in reinforced concrete based on a Gaussian description of the corrosion layer , 2011 .

[9]  Nicolas Sau,et al.  Peridynamic modeling of concrete structures , 2007 .

[10]  BEM Analysis of Crack Propagation in Concrete Based on Fracture Mechanics , 1992 .

[11]  Cruz Alonso,et al.  Comparison of rates of general corrosion and maximum pitting penetration on concrete embedded steel reinforcement , 1995 .

[12]  T. Rabczuk,et al.  A three-dimensional meshfree method for continuous multiple-crack initiation, propagation and junction in statics and dynamics , 2007 .

[13]  S. Diamond,et al.  The cracking and fracture of mortar , 1982 .

[14]  Christopher K.Y. Leung,et al.  Finite element modeling of concrete cover cracking due to non-uniform steel corrosion , 2015 .

[15]  Zdenek P. Bazant,et al.  PHYSICAL MODEL FOR STEEL CORROSION IN CONCRETE SEA STRUCTURES­ THEORY , 1979 .

[16]  Kapilesh Bhargava,et al.  Model for cover cracking due to rebar corrosion in RC structures , 2006 .

[17]  Fábio Luiz Teixeira Gonçalves,et al.  Probabilistic service life of RC structures under carbonation , 2017 .

[18]  Ch. Zhang,et al.  Two-dimensional X-ray CT image based meso-scale fracture modelling of concrete , 2015 .

[19]  Byung Hwan Oh,et al.  Effects of non-uniform corrosion on the cracking and service life of reinforced concrete structures , 2010 .

[20]  Richard E. Weyers,et al.  MODELING THE TIME-TO-CORROSION CRACKING IN CHLORIDE CONTAMINATED REINFORCED CONCRETE STRUCTURES , 1998 .

[21]  Ted Belytschko,et al.  Application of Particle Methods to Static Fracture of Reinforced Concrete Structures , 2006 .

[22]  Ralejs Tepfers,et al.  Cracking of concrete cover along anchored deformed reinforcing bars , 1979 .

[23]  Xiu-li Du,et al.  Modeling the cracking of cover concrete due to non-uniform corrosion of reinforcement , 2014 .

[24]  T. Rabczuk,et al.  A Meshfree Method based on the Local Partition of Unity for Cohesive Cracks , 2007 .

[25]  G. Paulino,et al.  Concrete fracture prediction using bilinear softening , 2007 .

[26]  T. Belytschko,et al.  A three dimensional large deformation meshfree method for arbitrary evolving cracks , 2007 .

[27]  S. J. Williamson,et al.  Pressure required to cause cover cracking of concrete due to reinforcement corrosion , 2000 .

[28]  Erik Schlangen,et al.  Cracking of the concrete cover due to reinforcement corrosion: A two-dimensional lattice model study , 2013 .

[29]  Yingshu Yuan,et al.  Modeling corroded section configuration of steel bar in concrete structure , 2009 .