Mode I fracture and microstructure for 2024-T3 friction stir welds

Detailed microstructural studies and mode I fracture experiments have been performed on both base material and three families of friction stir welds (FSWs) in 7 mm thick, 2024-T3 aluminum plate, designated hot, medium and cold due to the level of nominal heat input during the joining process. Microstructural studies indicate that the FSW nugget grain structure is relatively uniform in all welds, with a banded microstructure existing on horizontal cross-sections traversing the weld region; the spatial wavelength of the bands corresponds to the tool advance per revolution. The microstructural bands have elevated particle concentrations, with the particles having the same elemental content as base metal impurities, implying that the FSW process is responsible for the observed particle redistribution and microstructural banding. Furthermore, particle redistribution in all welds resulted in (a-1) particle size and volume fraction reduction on the advancing side of the weld nugget and (a-2) an attendant increase in particle volume fraction on the retreating side of the weld nugget. Finally, results indicate that hardness minima are present in the heat affected zone (HAZ) outside of the weld nugget on both the advancing side and retreating side for all welds, with the hot weld having the lowest overall weld hardness. Results from mode I fracture tests indicate that the measured critical COD at a fixed distance behind the crack tip is a viable fracture parameter for FSW joints that is capable of correlating the observed load-crack extension response for both the base metal and all FSWs. In addition, critical COD measurements indicate that FSW joints have a through-thickness variation in fracture resistance. Finally, the observed ductile crack growth path (which remained in the FSW region for all FSW joints) can be correlated with the locations of hardness minima, with microstructure variations affecting local fracture processes and the corresponding crack path.

[1]  Michael A. Sutton,et al.  A Study of Residual Stresses and Microstructure in 2024-T3 Aluminum Friction Stir Butt Welds , 2002 .

[2]  Anthony P. Reynolds,et al.  Processing-Property Correlation in Friction Stir Welds , 2000 .

[3]  A. Reynolds,et al.  Visualization of the material flow in AA2195 friction-stir welds using a marker insert technique , 2001 .

[4]  S. L. Semiatin,et al.  Continuous dynamic recrystallization during friction stir welding of high strength aluminum alloys , 2000 .

[5]  A. Cornec,et al.  Plastic stress-strain fields and limit loads of a plane strain cracked tensile panel with a mismatched welded joint , 1997 .

[6]  Michael A. Sutton,et al.  Characterizing Crack Growth in Thin Aluminum Panels Under Tension-Torsion Loading Using Three-Dimensional Digital Image Correlation , 2001 .

[7]  Michael A. Sutton,et al.  A combined modeling–experimental study of the crack opening displacement fracture criterion for characterization of stable crack growth under mixed mode I/II loading in thin sheet materials , 2000 .

[8]  Michael A. Sutton,et al.  Experimental study of crack growth in thin sheet 2024-T3 aluminum under tension-torsion loading , 2001 .

[9]  Michael A. Sutton,et al.  An Experimental Study of CTOD for Mode I/Mode II Stable Crack Growth in Thin 2024-T3 Aluminum Specimens , 1995 .

[10]  J. Newman,et al.  Orientation effects on the measurement and analysis of critical CTOA in an aluminum alloy sheet , 1995 .

[11]  A. Rosakis,et al.  Three-Dimensional Effects Near a Crack Tip in a Ductile Three-Point Bend Specimen: Part I—A Numerical Investigation , 1990 .

[12]  Murray W. Mahoney,et al.  Effects of friction stir welding on microstructure of 7075 aluminum , 1997 .

[13]  K. Ravi-Chandar,et al.  Experimental determination of stress-intensity factors using caustics and photoelasticity , 1989 .

[14]  R. H. Dodds.  Finite element evaluation of J parameters in 3D , 1987 .

[15]  Kumar V. Jata,et al.  Friction-stir welding effects on microstructure and fatigue of aluminum alloy 7050-T7451 , 2000 .

[16]  J. Newman,et al.  A CTOD-Based Mixed-Mode Fracture Criterion , 1999 .

[17]  Michael A. Sutton,et al.  Local crack closure measurements: Development of a measurement system using computer vision and a far-field microscope , 1999 .

[18]  Hugh Alan Bruck,et al.  Digital image correlation using Newton-Raphson method of partial differential correction , 1989 .

[19]  Michael A. Sutton,et al.  Determining Fatigue Crack Opening Loads from Near-Crack-Tip Displacement Measurements , 1999 .

[20]  M. A. Sutton,et al.  Systematic errors in digital image correlation caused by intensity interpolation , 2000 .

[21]  Michael A. Sutton,et al.  Development and application of a crack tip opening displacement-based mixed mode fracture criterion , 2000 .

[22]  A. Reynolds,et al.  Finite element simulation of material flow in friction stir welding , 2001 .

[23]  Robert L. Taylor,et al.  Microstructural studies of friction stir welds in 2024-T3 aluminum , 2002 .

[24]  W. F. Ranson,et al.  Applications of digital-image-correlation techniques to experimental mechanics , 1985 .

[25]  Pramod Rastogi,et al.  Trends in optical non-destructive testing and inspection , 2000 .