Modeling moisture ingress through polyisobutylene‐based edge‐seals

Photovoltaic devices are often sensitive to moisture and must be packaged in such a way as to limit moisture ingress for 25 years or more. Typically, this is accomplished through the use of impermeable front and backsheets (e.g., glass sheets or metal foils). However, this will still allow moisture ingress between the sheets from the edges. Attempts to hermetically seal with a glass frit or similarly welded bonds at the edge have had problems with costs and mechanical strength. Because of this, low diffusivity polyisobutylene materials filled with desiccant are typically used. Although it is well known that these materials will substantially delay moisture ingress, correlating that to outdoor exposure has been difficult. Here, we use moisture ingress measurements at different temperatures and relative humidities to find fit parameters for a moisture ingress model for an edge-seal material. Then, using meteorological data, a finite element model is used to predict the moisture ingress profiles for hypothetical modules deployed in different climates and mounting conditions, assuming no change in properties of the edge-seal as a function of aging. Copyright © 2014 John Wiley & Sons, Ltd.

[1]  Dennis J. Coyle,et al.  Degradation kinetics of CIGS solar cells , 2009, 2009 34th IEEE Photovoltaic Specialists Conference (PVSC).

[2]  William M. Worek,et al.  Sorption properties for different types of molecular sieve and their influence on optimum dehumidification performance of desiccant wheels , 2006 .

[3]  William Q. Meeker,et al.  Pitfalls of accelerated testing , 1998 .

[4]  Arrelaine A. Dameron,et al.  Evaluation of moisture ingress from the perimeter of photovoltaic modules , 2014 .

[5]  L. Greenspan.  Humidity Fixed Points of Binary Saturated Aqueous Solutions , 1977, Journal of Research of the National Bureau of Standards. Section A, Physics and Chemistry.

[6]  C. E. Rogers,et al.  Diffusion and solubility of methane in polyisobutylene , 1969 .

[7]  D. A. Nissen.  The low-temperature oxidation of calcium by water vapor , 1977 .

[8]  Richard H. Boyd,et al.  Molecular packing and diffusion in polyisobutylene , 1991 .

[9]  John R. Reynolds,et al.  Durable polyisobutylene edge sealants for organic electronics and electrochemical devices , 2012 .

[10]  M. Kempe.  Modeling of rates of moisture ingress into photovoltaic modules , 2006 .

[11]  D. L. King,et al.  Commonly observed degradation in field-aged photovoltaic modules , 2002, Conference Record of the Twenty-Ninth IEEE Photovoltaic Specialists Conference, 2002..

[12]  Hua Liu,et al.  Predicting the reliability of polyisobutylene seal for photovoltaic application , 2012, Optics + Photonics for Sustainable Energy.

[13]  David Cahen,et al.  Factors Affecting the Stability of CdTe/CdS Solar Cells Deduced from Stress Tests at Elevated Temperature , 2003 .

[14]  D. Tarrant,et al.  Stress induced degradation modes in CIGS mini-modules , 2008, 2008 33rd IEEE Photovoltaic Specialists Conference.

[15]  M. Kempe,et al.  Evaluation and modeling of edge-seal materials for photovoltaic applications , 2010, 2010 35th IEEE Photovoltaic Specialists Conference.

[16]  Nick Bosco,et al.  Evaluation of high‐temperature exposure of photovoltaic modules , 2011 .

[17]  Lars Stolt,et al.  A study of the influence of the Ga content on the long-term stability of Cu(In,Ga)Se2 thin film solar cells , 2003 .

[18]  M. Kempe,et al.  Quantitative calcium resistivity based method for accurate and scalable water vapor transmission rate measurement. , 2011, Review of Scientific Instruments.

[19]  Sabu Thomas,et al.  Transport phenomena through polymeric systems , 2001 .

[20]  R. Dixon.  Thermal Aging Predictions from an Arrhenus Plot with Only One Data Point , 1980, IEEE Transactions on Electrical Insulation.