Microstructure, mechanical and wear properties of laser processed SiC particle reinforced coatings on titanium

Abstract Laser processing of Ti–SiC composite coating on titanium was carried out to improve wear resistance using Laser Engineered Net Shaping (LENS™) — a commercial rapid prototyping technology. During the coating process a Nd:YAG laser was used to create small liquid metal pool on the surface of Ti substrate in to which SiC powder was injected to create Ti–SiC metal matrix composite layer. The composite layers were characterized using X-ray diffraction, scanning and transmission electron microscopy equipped with fine probe chemical analysis. Laser parameters were found to have strong influence on the dissolution of SiC, leading to the formation of TiSi2, Ti5Si3 and TiC with a large amount of SiC on the surface. Detailed matrix microstructural analysis showed the formation of non-stoichiometric compounds and TiSi2 in the matrix due to non-equilibrium rapid solidification during laser processing. The average Young's modulus of the composite coatings was found to be in the range of 602 and 757 GPa. Under dry sliding conditions, a considerable increase in wear resistance was observed, i.e., 5.91 × 10− 4 mm3/Nm for the SiC reinforced coatings and 1.3 × 10−3 mm3/Nm for the Ti substrate at identical test conditions.

[1]  J. Mazumder,et al.  Direct materials deposition: designed macro and microstructure , 1998 .

[2]  L. Dubourg,et al.  Laser cladding of MMC coatings on aluminium substrate: influence of composition and microstructure on mechanical properties , 2005 .

[3]  J. Hosson,et al.  Electron microscopy of reaction layers between SiC and Ti-6Al- 4V after laser embedding , 1998 .

[4]  Wilfried Kurz,et al.  Columnar to equiaxed transition in solidification processing , 2001 .

[5]  Vamsi Krishna Balla,et al.  Laser processing of SiC-particle-reinforced coating on titanium , 2010 .

[6]  E. Gutmanas,et al.  Interaction between SiC and Ti powder , 1993 .

[7]  E. Kisi,et al.  In-situ neutron diffraction of titanium silicide, Ti5Si3, during self-propagating high-temperature synthesis (SHS) , 2006 .

[8]  V. Ocelík,et al.  Ti–6Al–4V strengthened by laser melt injection of WCp particles , 2002 .

[9]  G. Pharr,et al.  An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments , 1992 .

[10]  T. N. Baker,et al.  XRD and XPS studies of surface MMC layers developed by laser alloying Ti-6Al-4V using a combination of a dilute nitrogen environment and SiC powder , 2006 .

[11]  J. Hosson,et al.  Reaction layers around SiC particles in Ti: an electron microscopy study , 1999 .

[12]  J. Hosson,et al.  Laser melt injection in aluminum alloys: On the role of the oxide skin , 2000 .

[13]  B. Vamsi Krishna,et al.  Surface modification of AISI 410 stainless steel using laser engineered net shaping (LENSTM) , 2009 .

[14]  Amit Bandyopadhyay,et al.  Functionally graded Co-Cr-Mo coating on Ti-6Al-4V alloy structures. , 2008, Acta biomaterialia.

[15]  J. Hosson,et al.  Sliding wear resistance of metal matrix composite layers prepared by high power laser , 2005 .

[16]  J. Ready.  LIA handbook of Laser materials processing , 2001 .

[17]  Z. A. Munir,et al.  Effect of Particle Dispersion on the Mechanism of Combustion Synthesis of Titanium Silicide , 1990 .

[18]  A. Bandyopadhyay,et al.  Laser surface modification of Al–4Cu–1Mg alloy for enhanced thermal conductivity , 2009 .

[19]  A. Bandyopadhyay,et al.  Titanium silicide (Ti5Si3) synthesis under shock loading , 2006 .

[20]  V. Ocelík,et al.  SiCp/Ti6Al4V functionally graded materials produced by laser melt injection , 2002 .

[21]  A. Bandyopadhyay,et al.  Laser-assisted Zr/ZrO(2) coating on Ti for load-bearing implants. , 2009, Acta biomaterialia.

[22]  N. Dahotre,et al.  Laser surface engineering of steel for hard refractory ceramic composite coating , 1999 .

[23]  K. Stern.  Metallurgical and ceramic protective coatings , 1996 .