The influence of water content and ageing degree of paper insulation on its mechanical strength

The article concerns the issue of mechanical strength of paper insulation in dependence of its ageing degree and water content. The authors focused on tearing resistance of Kraft paper. The tearing resistance of paper was determined using Elmendorf method. The ageing level of the paper samples was described by means of cellulose polymerization degree. The water content in paper samples was determined using Karl Fischer titration method. The investigations were conducted for various combinations of water content in the range from 7.24% to 0.12% and polymerization degree in the range from 1360 to 272. The results proved significant influence of water content in paper insulation on its mechanical strength. The drying of cellulose insulation causes significant weakness of mechanical strength of paper. This conclusion is particularly important in aspect of drying of aged transformer.

[1]  A. W. Stannett,et al.  A review of paper aging in power transformers , 1985 .

[2]  I. Hohlein,et al.  Aging of cellulose at transformer service temperatures. Part 2. Influence of moisture and temperature on degree of polymerization and formation of furanic compounds in free-breathing systems , 2005, IEEE Electrical Insulation Magazine.

[3]  M. Ali,et al.  Degradation of cellulosic insulation in power transformers .4. Effects of ageing on the tensile strength of paper , 2000 .

[4]  P Przybylek,et al.  The influence of cellulose insulation aging degree on its water sorption properties and bubble evolution , 2010, IEEE Transactions on Dielectrics and Electrical Insulation.

[5]  M. Ali,et al.  Degradation of cellulosic insulation in power transformers. Part 2: formation of furan products in insulating oil , 2000 .

[6]  M. Duval,et al.  Improving the reliability of transformer gas-in-oil diagnosis , 2005, IEEE Electrical Insulation Magazine.

[7]  T.A. Prevost,et al.  Cellulose insulation in oil-filled power transformers: part II maintaining insulation integrity and life , 2006, IEEE Electrical Insulation Magazine.

[8]  I. Hohlein,et al.  Aging of cellulose at transformer service temperatures. Part 1: Influence of type of oil and air on the degree of polymerization of pressboard, dissolved gases, and furanic compounds in oil , 2005, IEEE Electrical Insulation Magazine.

[9]  Tapan Kumar Saha,et al.  A study of degradation of cellulosic insulation materials in a power transformer, part 1. Molecular weight study of cellulose insulation paper , 1995 .