Porous and strong bioactive glass (13–93) scaffolds fabricated by freeze extrusion technique

Abstract Scaffolds fabricated by current methods often lack the combination of high strength and high porosity for skeletal substitution of load-bearing bones. In this work, freeze extrusion fabrication (FEF), a solid freeform fabrication technique, was investigated for the creation of porous and strong bioactive glass (13–93) scaffolds for potential applications in the repair of loaded bone. The process parameters for forming three-dimensional (3D) scaffolds with a pre-designed, grid-like microstructure by FEF were determined. Following thermal treatment of the as-formed constructs at temperatures up to 700 °C, scaffolds consisting of dense glass struts and interconnecting pores (porosity ≈ 50%; pore width ≈ 300 μm) were obtained. These scaffolds showed an elastic mechanical response in compression, with a compressive strength of 140 ± 70 MPa and an elastic modulus of 5.5 ± 0.5 GPa, comparable to the values for human cortical bone. The scaffolds supported the proliferation of osteogenic cells in vitro, showing their biocompatibility. These results indicate that 13–93 bioactive glass scaffolds created by the FEF method could have potential application in the repair and regeneration of load-bearing bones.

[1]  E. Sachlos,et al.  Making tissue engineering scaffolds work. Review: the application of solid freeform fabrication technology to the production of tissue engineering scaffolds. , 2003, European cells & materials.

[2]  J. Hollinger,et al.  Evaluation of particulate Bioglass in a rabbit radius ostectomy model. , 1997, Journal of biomedical materials research.

[3]  J. Polak,et al.  Ionic products of bioactive glass dissolution increase proliferation of human osteoblasts and induce insulin-like growth factor II mRNA expression and protein synthesis. , 2000, Biochemical and biophysical research communications.

[4]  D. Day,et al.  In Vitro Bioactive Characteristics of Borate‐Based Glasses with Controllable Degradation Behavior , 2007 .

[5]  Q. Fu,et al.  Oriented bioactive glass (13-93) scaffolds with controllable pore size by unidirectional freezing of camphene-based suspensions: Microstructure and mechanical response. , 2011, Acta biomaterialia.

[6]  B. Bal,et al.  Preparation and in vitro evaluation of bioactive glass (13-93) scaffolds with oriented microstructures for repair and regeneration of load-bearing bones. , 2010, Journal of biomedical materials research. Part A.

[7]  Gregory E. Hilmas,et al.  Aqueous Based Freeze-Form Extrusion Fabrication of Alumina Components (Preprint) , 2009 .

[8]  D. Chamberland,et al.  Effect of bioactive glass particle size on osseous regeneration of cancellous defects. , 1998, Journal of biomedical materials research.

[9]  S F Hulbert,et al.  Potential of ceramic materials as permanently implantable skeletal prostheses. , 1970, Journal of biomedical materials research.

[10]  Dietmar W. Hutmacher,et al.  Scaffold design and fabrication technologies for engineering tissues — state of the art and future perspectives , 2001, Journal of biomaterials science. Polymer edition.

[11]  Wenhai Huang,et al.  Kinetics and mechanisms of the conversion of silicate (45S5), borate, and borosilicate glasses to hydroxyapatite in dilute phosphate solutions , 2006, Journal of materials science. Materials in medicine.

[12]  Y. Fung,et al.  Biomechanics: Mechanical Properties of Living Tissues , 1981 .

[13]  A. Burstein,et al.  The elastic modulus for bone. , 1974, Journal of biomechanics.

[14]  D. Day,et al.  Preparation and bioactive characteristics of a porous 13-93 glass, and fabrication into the articulating surface of a proximal tibia. , 2007, Journal of biomedical materials research. Part A.

[15]  L L Hench,et al.  Gene-expression profiling of human osteoblasts following treatment with the ionic products of Bioglass 45S5 dissolution. , 2001, Journal of biomedical materials research.

[16]  Delbert E Day,et al.  Mechanical and in vitro performance of 13-93 bioactive glass scaffolds prepared by a polymer foam replication technique. , 2008, Acta biomaterialia.

[17]  L L Hench,et al.  Effect of crystallization on apatite-layer formation of bioactive glass 45S5. , 1996, Journal of biomedical materials research.

[18]  S. Goldstein.  The mechanical properties of trabecular bone: dependence on anatomic location and function. , 1987, Journal of biomechanics.

[19]  Delbert E Day,et al.  Growth and differentiation of osteoblastic cells on 13-93 bioactive glass fibers and scaffolds. , 2008, Acta biomaterialia.

[20]  A R Boccaccini,et al.  Mechanical properties of highly porous PDLLA/Bioglass composite foams as scaffolds for bone tissue engineering. , 2005, Acta biomaterialia.

[21]  T. Ikoma,et al.  Fabrication and mechanical and tissue ingrowth properties of unidirectionally porous hydroxyapatite/collagen composite. , 2007, Journal of biomedical materials research. Part B, Applied biomaterials.

[22]  Larry L. Hench,et al.  Regeneration of trabecular bone using porous ceramics , 2003 .

[23]  Aldo R Boccaccini,et al.  45S5 Bioglass-derived glass-ceramic scaffolds for bone tissue engineering. , 2006, Biomaterials.

[24]  D. Kaplan,et al.  Porosity of 3D biomaterial scaffolds and osteogenesis. , 2005, Biomaterials.

[25]  Q. Fu,et al.  Silicate, borosilicate, and borate bioactive glass scaffolds with controllable degradation rate for bone tissue engineering applications. I. Preparation and in vitro degradation. , 2010, Journal of biomedical materials research. Part A.

[26]  Keiichi Kuroki,et al.  Silicate, borosilicate, and borate bioactive glass scaffolds with controllable degradation rate for bone tissue engineering applications. II. In vitro and in vivo biological evaluation. , 2010, Journal of biomedical materials research. Part A.

[27]  P. Ma,et al.  Microtubular architecture of biodegradable polymer scaffolds. , 2001, Journal of biomedical materials research.

[28]  Shen‐guo Wang,et al.  Manufacturing and morphology structure of polylactide-type microtubules orientation-structured scaffolds. , 2006, Biomaterials.

[29]  Delbert E Day,et al.  Bioactive glass in tissue engineering. , 2011, Acta biomaterialia.

[30]  R. B. Ashman,et al.  Relations of mechanical properties to density and CT numbers in human bone. , 1995, Medical engineering & physics.