Hydrogen Effect against Hydrogen Embrittlement

The well-known term “hydrogen embrittlement” (HE) expresses undesirable effects due to hydrogen such as loss of ductility, decreased fracture toughness, and degradation of fatigue properties of metals. However, this article shows, surprisingly, that hydrogen can have an effect against HE. A dramatic phenomenon was found in which charging a supersaturated level of hydrogen into specimens of austenitic stainless steels of types 304 and 316L drastically improved the fatigue crack growth resistance, rather than accelerating fatigue crack growth rates. Although this mysterious phenomenon has not previously been observed in the history of HE research, its mechanism can be understood as an interaction between hydrogen and dislocations. Hydrogen can play two roles in terms of dislocation mobility: pinning (or dragging) and enhancement of mobility. Competition between these two roles determines whether the resulting phenomenon is damaging or, unexpectedly, desirable. This finding will, not only be the crucial key factor to elucidate the mechanism of HE, but also be a trigger to review all existing theories on HE in which hydrogen is regarded as a dangerous culprit.

[1]  Direct observations of hydrogen enhanced crack propagation in iron , 1984 .

[2]  D. Abraham,et al.  Hydrogen-enhanced localization of plasticity in an austenitic stainless steel , 1995 .

[3]  Ruqian Wu,et al.  Charge transfer mechanism of hydrogen-induced intergranular embrittlement of iron , 2000 .

[4]  G. Schuster,et al.  Fatigue of stainless steel in hydrogen , 1983 .

[5]  C. S. Marchi,et al.  Permeability, solubility and diffusivity of hydrogen isotopes in stainless steels at high gas pressures , 2007 .

[6]  Yukitaka Murakami,et al.  The Effect of Hydrogen on Fatigue Properties of Metals used for Fuel Cell System , 2006 .

[7]  C. S. Marchi,et al.  Effects of alloy composition and strain hardening on tensile fracture of hydrogen-precharged type 316 stainless steels , 2008 .

[8]  H. Matsui,et al.  The effect of hydrogen on the mechanical properties of high purity iron I. Softening and hardening of high purity iron by hydrogen charging during tensile deformation , 1979 .

[9]  三郎 松岡,et al.  炭素量0.08mass%の配管用炭素鋼鋼管の疲労き裂進展とストレッチゾーンに及ぼす水素の影響 , 2008 .

[10]  I. Bernstein,et al.  The effect of hydrogen on the slip character of nickel , 1980 .

[11]  M. R. Louthan.  Strain localization and hydrogen embrittlement , 1983 .

[12]  C. D. Beachem,et al.  A new model for hydrogen-assisted cracking (hydrogen “embrittlement”) , 1972 .

[13]  C. Altstetter,et al.  Hydrogen-enhanced plasticity of 310S stainless steel , 1993 .

[14]  H. Birnbaum,et al.  An HVEM study of hydrogen effects on the deformation and fracture of nickel , 1986 .

[15]  N. Moody,et al.  The effect of hydrogen, tritium and decay helium on the fracture toughness of a stainless steel superalloy , 1986 .

[16]  D. Eliezer,et al.  The influence of austenite stability on the hydrogen embrittlement and stress- corrosion cracking of stainless steel , 1979 .

[17]  H. Birnbaum,et al.  Effects of hydrogen and carbon on thermally activated deformation in nickel , 1992 .

[18]  Atomistic simulation of the effects of hydrogen on the mobility of edge dislocation in alpha iron , 2008 .

[19]  S. Asano,et al.  The lattice hardening due to dissolved hydrogen in iron and steel , 1976 .

[20]  D. Bahr,et al.  Hydrogen effects on dislocation activity in austenitic stainless steel , 2006 .

[21]  D. Abraham,et al.  The effect of hydrogen on the yield and flow stress of an austenitic stainless steel , 1995 .

[22]  D. Delafosse,et al.  Numerical simulations of hydrogen–dislocation interactions in fcc stainless steels.: part I: hydrogen–dislocation interactions in bulk crystals , 2002 .

[23]  R. Kirchheim.  Reducing grain boundary, dislocation line and vacancy formation energies by solute segregation , 2007 .

[24]  H. Matsui,et al.  The effect of hydrogen on the mechanical properties of high purity iron II. Effect of quenched-in hydrogen below room temperature , 1979 .

[25]  Y. Murakami,et al.  Effects of hydrogen on fatigue crack growth behavior of austenitic stainless steels , 2008 .

[26]  V. Gavriljuk,et al.  Diagnostic experimental results on the hydrogen embrittlement of austenitic steels , 2003 .

[27]  Y. Murakami,et al.  Effects of hydrogen charge on microscopic fatigue behaviour of annealed carbon steels , 2006 .

[28]  V. Gavriljuk,et al.  Change in the electron structure caused by C, N and H atoms in iron and its effect on their interaction with dislocations , 2005 .

[29]  R. Asaro,et al.  The role of hydrogen in the ductile fracture of plain carbon steels , 1979 .

[30]  Y. Murakami,et al.  Failure analysis of SUS316L flexible hose for hydrogen station and fatigue life prediction method , 2009 .

[31]  A. Pundt,et al.  Small angle neutron scattering of hydrogen segregation at dislocations in palladium , 2001 .

[32]  Y. Murakami,et al.  Effect of hydrogen and frequency on fatigue behavior of SCM435 steel for storage cylinder of hydrogen station , 2007 .

[33]  J. A. Donovan,et al.  Hydrogen embrittlement of metals , 1972 .

[34]  村上 敬宜.  Metal fatigue : effects of small defects and nonmetallic inclusions , 2002 .

[35]  R. Ritchie,et al.  On the influence of gaseous hydrogen in decelerating fatigue crack growth rates in ultrahigh strength steels , 1981 .

[36]  Petros Athanasios Sofronis,et al.  Hydrogen-enhanced localized plasticity—a mechanism for hydrogen-related fracture , 1993 .

[37]  C. Altstetter,et al.  Hydrogen-induced strain localization and failure of austenitic stainless steels at high hydrogen concentrations , 1991 .

[38]  Y. Murakami.  Metal Fatigue: Effects of Small Defects and Nonmetallic Inclusions , 2002 .

[39]  W. Gerberich,et al.  Dislocation modeling and acoustic emission observation of alternating ductile/brittle events in Fe-3wt%Si crystals , 1990 .

[40]  K. Ogura,et al.  Hydrogen-assisted crack growth of austenitic stainless steel hydrogenated by high temperature cathodic charging , 1988 .

[41]  R. A. Oriani,et al.  Equilibrium aspects of hydrogen-induced cracking of steels , 1974 .

[42]  H. Birnbaum.  Hydrogen effects on deformation -- relation between dislocation behavior and the macroscopic stress-strain behavior , 1994 .

[43]  S. Lynch.  Environmentally Assisted Cracking: Overview of Evidence for an Adsorption-Induced Localised-Slip Process, , 1988 .

[44]  HVEM studies of the effects of hydrogen on the deformation and fracture of AISI type 316 austenitic stainless steel , 1990 .

[45]  A. Inoue,et al.  The Effect of Hydrogen on Crack Propagation Behavior and Microstructures around Cracks in Austenitic Stainless Steels , 1979 .

[46]  Jianhong He,et al.  Effect of strain-induced martensite on hydrogen environment embrittlement of sensitized austenitic stainless steels at low temperatures , 1998 .

[47]  Yukitaka Murakami,et al.  Hydrogen Embrittlement Mechanism in Fatigue of Austenitic Stainless Steels , 2008 .

[48]  P. Sofronis,et al.  Mechanics of the hydrogendashdislocationdashimpurity interactions-I. Increasing shear modulus , 1995 .

[49]  Petros Athanasios Sofronis,et al.  The influence of mobility of dissolved hydrogen on the elastic response of a metal , 1995 .

[50]  Xiangyu Tang,et al.  Hydrogen effects on slip character and ductility in NiCo alloys , 1994 .