A framework for fracture assessments of dissimilar girth welds in offshore pipelines under bending

Abstract This work describes the development of a framework for structural integrity assessments of dissimilar girth welds in clad and lined pipes subjected to high levels of bending load for a wide range of pipe geometries, crack configurations, weld grooves and weld strength mismatch levels based upon an EPRI estimation scheme for crack driving forces coupled with a weld groove simplification procedure and the equivalent stress–strain relationship. Systematic validation of the method is provided and the crack driving force estimation accuracy is demonstrated through comparisons with numerical tools and 3-D finite element analyses for reeled pipelines.

[1]  Bjørn Skallerud,et al.  Thin shell and surface crack finite elements for simulation of combined failure modes , 2005 .

[2]  Peter J. Budden,et al.  Reference Stress Approximations for J and COD of Circumferential Through-Wall Cracked Pipes , 2002 .

[3]  Uwe Zerbst,et al.  Review on fracture and crack propagation in weldments - A fracture mechanics perspective , 2014 .

[4]  John W. Hutchinson,et al.  Fully Plastic Solutions and Large Scale Yielding Estimates for Plane Stress Crack Problems , 1976 .

[6]  J. Hancock,et al.  Two-Parameter Characterization of Elastic-Plastic Crack-Tip Fields , 1991 .

[7]  Zhiliang Zhang,et al.  On the interrelationship between fracture toughness and material mismatch for cracks located at the fusion line of weldments , 1999 .

[8]  Robert A. Ainsworth,et al.  A J integral estimation method for cracks in welds with mismatched mechanical properties , 1997 .

[9]  Bård Nyhus,et al.  SENT Specimens an Alternative to SENB Specimens for Fracture Mechanics Testing of Pipelines , 2003 .

[10]  Uwe Zerbst,et al.  Basic principles of analytical flaw assessment methods , 2000 .

[11]  N. Dowling.  Mechanical Behavior of Materials: Engineering Methods for Deformation, Fracture, and Fatigue , 1993 .

[12]  Yun‐Jae Kim,et al.  Mismatch limit loads and approximate J estimates for tensile plates with constant-depth surface cracks in the center of welds , 2007 .

[13]  Bård Nyhus,et al.  Effects of crack depth and specimen size on ductile crack growth of SENT and SENB specimens for fracture mechanics evaluation of pipeline steels , 2009 .

[14]  H. Saunders,et al.  Advanced Fracture Mechanics , 1985 .

[15]  J. Hutchinson.  Fundamentals of the Phenomenological Theory of Nonlinear Fracture Mechanics , 1983 .

[16]  Rodolfo F. de Souza,et al.  J–CTOD relations in clamped SE(T) fracture specimens including 3-D stationary and growth analysis , 2015 .

[17]  ETD委員会基準化分科会.  ASME Boiler & Pressure Vessel Code Sec. III NB/NC及び同Sec. III Div. 1/Div. 2の比較検討 , 1995 .

[18]  P. J. Budden.  Failure assessment diagram methods for strain-based fracture , 2006 .

[19]  Uwe Zerbst,et al.  SINTAP defect assessment procedure for strength mis-matched structures , 2000 .

[20]  W. Drugan,et al.  Theory of plasticity , 1987 .

[21]  Michael Smith.  Fitness for Service, API 579-1/ASME FFS-1 , 2007 .

[22]  Noel P. O’Dowd,et al.  Fully-Plastic Strain-Based J Estimation Scheme for Circumferential Surface Cracks in Pipes Subjected to Reeling , 2015 .

[23]  Rudi Denys,et al.  J-integral analysis of heterogeneous mismatched girth welds in clamped single-edge notched tension specimens , 2014 .

[24]  F. M. Burdekin,et al.  Engineering critical analyses to BS 7910 — the UK guide on methods for assessing the acceptability of flaws in metallic structures , 2000 .

[25]  T. Anderson,et al.  Fracture mechanics - Fundamentals and applications , 2017 .

[26]  Bjørn Skallerud,et al.  Fracture Control Offshore Pipelines: Advantages of Using Direct Calculations in Fracture Assessments of Pipelines , 2005 .

[27]  A. Cornec,et al.  Plastic stress-strain fields and limit loads of a plane strain cracked tensile panel with a mismatched welded joint , 1997 .

[28]  Erlend Olso̸,et al.  New Assessment Approach For ECA of Clad And Lined Pipes Based On Shell And Line-spring Finite Elements , 2011 .

[29]  Tomasz Tkaczyk,et al.  Fracture Assessment Procedures for Steel Pipelines Using a Modified Reference Stress Solution , 2009 .

[30]  Soheil Manouchehri.  A Discussion of Practical Aspects of Reeled Flowline Installation , 2012 .

[31]  Zhongmin Xiao,et al.  On 3-D crack problems in offshore pipeline with large plastic deformation , 2013 .

[32]  Rudi Denys,et al.  Constraint analysis of defects in strength mismatched girth welds of (pressurized) pipe and Curved Wide Plate tensile test specimens , 2014 .

[33]  Yuh J. Chao,et al.  EFFECT OF MECHANICAL PROPERTY MISMATCH ON FAILURE ASSESSMENT CURVE FOR WELDED JOINT WITH A SEMI-ELLIPTICAL CRACK , 2013 .

[34]  Pei-Ning Li,et al.  Limit load and J estimates of a centre cracked plate with an asymmetric crack in a mismatched weld , 1999 .

[35]  Erling Østby.  Fracture Control — Offshore Pipelines: New Strain-Based Fracture Mechanics Equations Including the Effects of Biaxial Loading, Mismatch, and Misalignment , 2005 .

[36]  Matteo Chiesa,et al.  Efficient fracture assessment of pipelines. A constraint-corrected SENT specimen approach , 2001 .

[37]  Claudio Ruggieri,et al.  J and CTOD estimation procedure for circumferential surface cracks in pipes under bending , 2010 .

[38]  Nikzad Nourpanah,et al.  Development of a reference strain approach for assessment of fracture response of reeled pipelines , 2010 .

[39]  Indra Permana.  A study on engineering critical assessment (ECA) of subsea pipeline girth welds for reeling installation , 2013 .

[40]  Aurélien Pépin,et al.  Methodology for Assessment of Surface Defects in Undermatched Pipeline Girth Welds , 2015 .

[41]  Robert A. Ainsworth,et al.  The estimation of J in three-point-bend specimens with a crack in a mismatched weld , 1997 .

[42]  Claudio Ruggieri,et al.  Fracture assessments of clad pipe girth welds incorporating improved crack driving force solutions , 2015 .