Abstract The service-exposed (∼60 000 h/873 K) Alloy 625 ammonia cracker tubes showed higher strength and lower ductility compared to the virgin material in the solution annealed state. Precipitation of intermetallic γ″ and Ni2(Cr,Mo) phases and the inter and intragranular carbides were found to be responsible for higher strength of the service-exposed alloy. Subjecting the service-exposed alloy to thermal aging treatments subsequently at 923 K and 1123 K (above the service temperature of the exposed alloy) led to the dissolution of the intermetallic phases that in turn increased the ductility of the alloy. Post-service aging of the alloy at 923 K for short durations resulted in the dissolution of the Ni2(Cr,Mo)-phase. The dissolution of the Ni2(Cr,Mo)-phase exhibited significant influence upon yield strength (YS) but negligible effect on ductility. Prolonged aging of the alloy for 500 h at 923 K resulted in the precipitation of intermetallic δ-phase. Post-service aging of the alloy at 1123 K promoted the dissolution of both Ni2(Cr,Mo) and γ″ formed during service. Longer duration aging at the same temperature led to the precipitation of the δ-phase with an associated increase in strength and loss in ductility. Re-solution annealing of the service-exposed alloy at 1423 K caused the dissolution of the strengthening phases. When the re-solution annealed alloy was subjected to prolonged exposure at 923 K, the yield stress was found to increase rapidly with aging time with attendent loss in ductility due to the precipitation of γ″.
[1]
Srikumar Banerjee,et al.
Precipitation of the δ-Ni3Nb phase in two nickel base superalloys
,
1988
.
[2]
Charles Thomas,et al.
The performance of Alloy 625 in long-term intermediate temperature applications
,
1994
.
[3]
Mukul Kumar,et al.
Ordering reactions in an Ni25Mo8Cr alloy
,
1996
.
[4]
Srikumar Banerjee,et al.
Precipitation of an intermetallic phase with Pt2Mo-type structure in alloy 625
,
1999
.
[5]
G. Fuchs,et al.
The Metallurgy of Alloy 625
,
1994
.
[6]
J. Radavich,et al.
Effects of Long-Time Exposure in Alloy 625 at 12OOF, 1400F and 1600F
,
1994
.
[7]
H. M. Tawancy.
Long-term ageing characteristics of some commercial nickel-chromium-molybdenum alloys
,
1981
.
[8]
M. Sundararaman,et al.
Heterogeneous Precipitation of the γ" Phase in Inconel 625
,
1985
.
[9]
H. M. Tawancy.
Order-Strengthening in a nickel-base superalloy (hastelloy alloy S)
,
1980
.