Wet etching studies of silicon nitride thin films deposited by electron cyclotron resonance (ECR) plasma enhanced chemical vapor deposition

Silicon nitride films of various compositions have been deposited on silicon substrate by electron cyclotron resonance plasma-enhanced chemical vapor deposition (ECR-PECVD) technique from mixtures of Ar, N2 and SiH4 as precursors. Film composition and refractive index as a function of deposition parameters like gas flow ratio and pressure were studied. Wet etching studies were conducted using diluted phosphoric acid and buffered oxide etch (BOE) solutions of various concentrations. The etching studies using phosphoric acid were conducted in the temperature range of 70-90 °C. For BOE the temperature range was 25-55 °C. The etch rate with BOE solution is much higher than with phosphoric acid. The results indicate that the mechanism of etching with phosphoric acid is different from that with BOE solution.

[1]  V. Shanov,et al.  Composition, structure and properties of silicon nitride films grown from dichlorosilane and ammonia at low pressure , 1992 .

[2]  W. D. Williams,et al.  Plasma Deposited Silicon Nitride for Indium Phosphide Encapsulation , 1989 .

[3]  Physico‐Chemical Properties of Plasma Deposited Silicon Nitride Films , 1992 .

[4]  W. Holber,et al.  Optimization of a Low Damage, High Resolution Etch Process for SiN[sub x] in an ECR Reactor , 1996 .

[5]  W. Lanford.  15N hydrogen profiling: Scientific applications , 1978 .

[6]  R. Jaeger.  Introduction to microelectronic fabrication , 1987 .

[7]  Tsuneo Mitsuyu,et al.  Silicon nitride thin films prepared by the electron cyclotron resonance plasma chemical vapor deposition method , 1989 .

[8]  H. Stein,et al.  Silicon nitride formation from a silane–nitrogen electron cyclotron resonance plasma , 1991 .

[9]  Y. Shioya,et al.  Analysis of the Superior Water Blocking Ability of Electron Cyclotron Resonance‐Plasma SiO2 Film , 1998 .

[10]  D. M. Knotter,et al.  Etching mechanism of silicon nitride in HF-based solutions , 2001 .

[11]  Y. Tsividis.  Operation and modeling of the MOS transistor , 1987 .

[12]  L. Loewenstein,et al.  Chemical Etching of Thermally Oxidized Silicon Nitride: Comparison of Wet and Dry Etching Methods , 1991 .

[13]  K. R. Williams,et al.  Etch rates for micromachining processing , 1996 .

[14]  M. Madou.  Fundamentals of microfabrication , 1997 .

[15]  G. Kovacs.  Micromachined Transducers Sourcebook , 1998 .

[16]  D. Herring.  Energy Levels of F 18 , 1958 .

[17]  K. Buckle,et al.  Electron cyclotron resonance plasma deposition of silicon nitride: Effect of very low rf substrate bias , 1992 .

[18]  W. V. Gelder,et al.  The Etching of Silicon Nitride in Phosphoric Acid with Silicon Dioxide as a Mask , 1967 .

[19]  C. A. Deckert.  Pattern Etching of CVD Si3 N 4 / SiO2 Composites in HF / Glycerol Mixtures , 1980 .