Characterization of internal damage in a MMCp using X-ray synchrotron phase contrast microtomography

The initiation and development of damage inside a 6061 Al alloy reinforced with SiC particles has been studied during in situ mechanical tests using high resolution synchrotron X-ray tomography. The high coherence of the X-ray beam used improves the detection of reinforcements in the matrix as well as the detection of cracks. Qualitatively, the same damage mechanisms are observed at the surface and in the bulk of the sample, the rupture of the SiC particles being the dominant mechanism for the early stages of plastic deformation. Quantitatively, however, it is found that the geometrical characteristics of surface SiC particles differ from those of bulk particles and that the damage growth rate is larger inside the sample. This result can be understood in terms of elastic energy and normal stress levels in the SiC particles as calculated by finite element method (FEM) analysis.

[1]  M. Elices,et al.  Particulate fracture during deformation , 1993, Metallurgical and Materials Transactions A.

[2]  P. Withers,et al.  Weibull modelling of particle cracking in metal matrix composites , 1995 .

[3]  M. Elices,et al.  Reinforcement Fracture and Ductility in Sphere-Reinforced Al-Matrix Composites , 1996 .

[4]  G. Bao.  Damage due to fracture of brittle reinforcements in a ductile matrix , 1992 .

[5]  Françoise Peyrin,et al.  Observation of microstructure and damage in materials by phase sensitive radiography and tomography , 1997 .

[6]  B. Derby,et al.  In situ scanning electron microscope studies of fracture in particulate-reinforced metal-matrix composites , 1994, Journal of Materials Science.

[7]  J. D. Embury,et al.  Damage initiation in metal matrix composites , 1991 .

[8]  P. Cloetens,et al.  Phase objects in synchrotron radiation hard x-ray imaging , 1996 .

[9]  John J. Lewandowski,et al.  Crack initiation and growth toughness of an aluminum metal-matrix composite , 1990 .

[10]  T. Hirano,et al.  In situ x-ray CT under tensile loading using synchrotron radiation , 1995 .

[11]  E. Maire,et al.  Study of the damage mechanisms in an OSPREY™ Al alloy-SiCp composite by scanning electron microscope in situ tensile tests , 1995 .

[12]  Stuart R. Stock,et al.  Direct observation of crack opening as a function of applied load in the interior of a notched tensile sample of AlLi 2090 , 1997 .

[13]  Toshio Mura,et al.  Micromechanics of defects in solids , 1982 .

[14]  Subra Suresh,et al.  On microstructural evolution and micromechanical modelling of deformation of a whisker-reinforced metal-matrix composite , 1989 .

[15]  P. Cloetens,et al.  Damage assessment in an Al/SiC composite during monotonic tensile tests using synchrotron X-ray microtomography , 1997 .

[16]  Shouxin Li,et al.  Thermal residual stress relaxation at surface of SiC/Al composite , 1991 .

[17]  P. Haasen,et al.  Constitution of melt-spun NdFeB-magnets studied by analytical field ion microscopy , 1991 .

[18]  P. Gregson,et al.  The effects of ageing on the physical and mechanical properties of particulate reinforced aluminium alloys , 1991 .

[19]  Stuart R. Stock,et al.  Damage in aligned-fibre SiC/Al quantified using a laboratory X-ray tomographic microscope , 1993 .

[20]  B. Derby,et al.  Damage assessment in particle-reinforced metal matrix composites using x-ray microtomography , 1993 .

[21]  P. Withers,et al.  An introduction to metal matrix composites , 1993 .

[22]  C. Bathias,et al.  Defects in squeeze-cast Al2O3/Al alloy composites and their effects on mechanical properties , 1993 .

[23]  S. Wilkins,et al.  Phase-contrast imaging using polychromatic hard X-rays , 1996, Nature.

[24]  A. Levy,et al.  Elastoplastic finite element analysis of short-fiber-reinforced SiC/Al composites: effects of thermal treatment , 1991 .

[25]  Toshio Mura,et al.  The Elastic Field in a Half Space Due to Ellipsoidal Inclusions With Uniform Dilatational Eigenstrains , 1979 .