Redox Reactions at Cu,Ag/Ta2O5 Interfaces and the Effects of Ta2O5 Film Density on the Forming Process in Atomic Switch Structures

Cu and Ag redox reactions at the interfaces with Ta2O5 and the impact of Ta2O5 film density on the forming process of Cu,Ag/Ta2O5/Pt atomic switch structures are investigated. Cyclic voltammetry measurements revealed that under positive bias to the Cu (Ag) electrode, Cu is preferentially oxidized to Cu2+, while Ag is oxidized to Ag+ ions. Subsequent negative bias causes a reduction of oxidized Cu (Ag) ions at the interfaces. The diffusion coefficient of the Cu and Ag ions in the Ta2O5 film is estimated from the results from different bias voltage sweep rates. It is also found that the redox current is enhanced and the forming voltage of the Cu/Ta2O5/Pt cell is reduced when the density of the Ta2O5 film is decreased. This result indicates the importance of the structural properties of the matrix oxide film in understanding and controlling resistive switching behavior.

[1]  Rainer Waser,et al.  Impact of the Counter‐Electrode Material on Redox Processes in Resistive Switching Memories , 2014 .

[2]  Ilia Valov,et al.  Redox‐Based Resistive Switching Memories (ReRAMs): Electrochemical Systems at the Atomic Scale , 2014 .

[3]  R. Waser,et al.  Generic relevance of counter charges for cation-based nanoscale resistive switching memories. , 2013, ACS nano.

[4]  Masakazu Aono,et al.  Rate-limiting processes in the fast SET operation of a gapless-type Cu-Ta2O5 atomic switch , 2013 .

[5]  T. Hasegawa,et al.  Conductance quantization and synaptic behavior in a Ta2O5-based atomic switch , 2012, Nanotechnology.

[6]  R. Waser,et al.  Nanoionic transport and electrochemical reactions in resistively switching silicon dioxide. , 2012, Nanoscale.

[7]  R. Waser,et al.  Effects of Moisture on the Switching Characteristics of Oxide‐Based, Gapless‐Type Atomic Switches , 2012 .

[8]  Rainer Waser,et al.  Redox processes in silicon dioxide thin films using copper microelectrodes , 2011 .

[9]  I. Shalish,et al.  Method for electrical characterization of nanowires , 2011, Nanotechnology.

[10]  T. Hasegawa,et al.  Short-term plasticity and long-term potentiation mimicked in single inorganic synapses. , 2011, Nature materials.

[11]  M. Kozicki,et al.  Electrochemical metallization memories—fundamentals, applications, prospects , 2011, Nanotechnology.

[12]  Masakazu Aono,et al.  Temperature effects on the switching kinetics of a Cu–Ta2O5-based atomic switch , 2011, Nanotechnology.

[13]  K. Terabe,et al.  Forming and switching mechanisms of a cation-migration-based oxide resistive memory , 2010, Nanotechnology.

[14]  T. Hasegawa,et al.  Nanoionics Switching Devices: “Atomic Switches” , 2009 .

[15]  C. N. Lau,et al.  The mechanism of electroforming of metal oxide memristive switches , 2009, Nanotechnology.

[16]  K. Terabe,et al.  Diffusivity of Cu Ions in Solid Electrolyte and Its Effect on the Performance of Nanometer-Scale Switch , 2008, IEEE Transactions on Electron Devices.

[17]  R. Waser,et al.  Nanoionics-based resistive switching memories. , 2007, Nature materials.

[18]  K. Terabe,et al.  Quantized conductance atomic switch , 2005, Nature.

[19]  M. Wuttig,et al.  Preparation and characterization of tantalum oxide films produced by reactive DC magnetron sputtering , 2003 .

[20]  A. Chu,et al.  Microstructure and corrosion resistance of room-temperature RF sputtered Ta2O5 thin films , 1999 .

[21]  T. Dimitrova,et al.  Interface and oxide properties of rf sputtered Ta2O5- Si structures , 1998 .

[22]  A. Bard,et al.  Standard Potentials in Aqueous Solution , 1985 .