Rapid and controllable flame reduction of TiO2 nanowires for enhanced solar water-splitting.

We report a new flame reduction method to generate controllable amount of oxygen vacancies in TiO2 nanowires that leads to nearly three times improvement in the photoelectrochemical (PEC) water-splitting performance. The flame reduction method has unique advantages of a high temperature (>1000 °C), ultrafast heating rate, tunable reduction environment, and open-atmosphere operation, so it enables rapid formation of oxygen vacancies (less than one minute) without damaging the nanowire morphology and crystallinity and is even applicable to various metal oxides. Significantly, we show that flame reduction greatly improves the saturation photocurrent densities of TiO2 nanowires (2.7 times higher), α-Fe2O3 nanowires (9.4 times higher), ZnO nanowires (2.0 times higher), and BiVO4 thin film (4.3 times higher) in comparison to untreated control samples for PEC water-splitting applications.

[1]  Peng Wang,et al.  Electrochemical reduction induced self-doping of Ti3+ for efficient water splitting performance on TiO2 based photoelectrodes. , 2013, Physical chemistry chemical physics : PCCP.

[2]  S. Feng,et al.  High-performance gas sensing achieved by mesoporous tungsten oxide mesocrystals with increased oxygen vacancies , 2013 .

[3]  R. Sinclair,et al.  Erratum: Codoping titanium dioxide nanowires with tungsten and carbon for enhanced photoelectrochemical performance , 2013, Nature Communications.

[4]  Jinhua Ye,et al.  Reduced TiO2 nanotube arrays for photoelectrochemical water splitting , 2013 .

[5]  Lianjun Liu,et al.  Spontaneous Dissociation of CO2 to CO on Defective Surface of Cu(I)/TiO2–x Nanoparticles at Room Temperature , 2012 .

[6]  P. Schmuki,et al.  Flame annealing effects on self-organized TiO2 nanotubes , 2012 .

[7]  M. Fernández-García,et al.  Advanced nanoarchitectures for solar photocatalytic applications. , 2012, Chemical reviews.

[8]  Teng Zhai,et al.  Hydrogenated TiO2 nanotube arrays for supercapacitors. , 2012, Nano letters.

[9]  Ji‐Yong Shin,et al.  Oxygen-Deficient TiO2−δ Nanoparticles via Hydrogen Reduction for High Rate Capability Lithium Batteries , 2012 .

[10]  Xiaolin Zheng,et al.  Branched TiO₂ nanorods for photoelectrochemical hydrogen production. , 2011, Nano letters.

[11]  Yichuan Ling,et al.  Hydrogen-treated TiO2 nanowire arrays for photoelectrochemical water splitting. , 2011, Nano letters.

[12]  M. Grätzel,et al.  Probing the photoelectrochemical properties of hematite (α-Fe2O3) electrodes using hydrogen peroxide as a hole scavenger , 2011 .

[13]  Thomas F. Jaramillo,et al.  Accelerating materials development for photoelectrochemical hydrogen production: Standards for methods, definitions, and reporting protocols , 2010 .

[14]  P. He,et al.  The effect of oxygen vacancies on the structure and electrochemistry of LiTi2(PO4)3 for lithium-ion batteries: A combined experimental and theoretical study , 2009 .

[15]  Pietro Siciliano,et al.  The Role of Surface Oxygen Vacancies in the NO2 Sensing Properties of SnO2 Nanocrystals , 2008 .

[16]  J. Nowotny,et al.  Defect Chemistry of Titanium Dioxide. Application of Defect Engineering in Processing of TiO2-Based Photocatalysts† , 2008 .

[17]  M. V. Ganduglia-Pirovano,et al.  Oxygen vacancies in transition metal and rare earth oxides: Current state of understanding and remaining challenges , 2007 .

[18]  W. Ingler,et al.  Nanotube enhanced photoresponse of carbon modified (CM)-n-TiO2 for efficient water splitting , 2007 .

[19]  Zhiyong Fan,et al.  High-performance ZnO nanowire field effect transistors , 2006 .

[20]  M. Muhler,et al.  On the role of oxygen defects in the catalytic performance of zinc oxide. , 2006, Angewandte Chemie.

[21]  C. Grimes,et al.  A study on the spectral photoresponse and photoelectrochemical properties of flame-annealed titania nanotube-arrays , 2005 .

[22]  J. Yates,et al.  TiO2-based Photocatalysis: Surface Defects, Oxygen and Charge Transfer , 2005 .

[23]  S. Adler.  Factors governing oxygen reduction in solid oxide fuel cell cathodes. , 2004, Chemical reviews.

[24]  J. Hanson,et al.  Time-resolved Studies for the Mechanism of Reduction of Copper Oxides with Carbon Monoxide: Complex Behavior of Lattice Oxygen and the Formation of Suboxides , 2004 .

[25]  G. Pacchioni.  Oxygen vacancy: the invisible agent on oxide surfaces. , 2003, Chemphyschem : a European journal of chemical physics and physical chemistry.

[26]  J. Nørskov,et al.  Oxygen vacancies as active sites for water dissociation on rutile TiO(2)(110). , 2001, Physical review letters.

[27]  C. Friend,et al.  The Role of Oxygen Vacancies in Methanol Reaction on Oxidized Mo(110) , 1998 .

[28]  A. Manthiram,et al.  Reduction of Aqueous Na(2)WO(4) by NaBH(4) at Ambient Temperatures To Obtain Lower Valent Tungsten Oxides. , 1997, Inorganic chemistry.

[29]  M. Barteau,et al.  Isothermal Reduction Kinetics of Titanium Dioxide-Based Materials , 1997 .

[30]  J. Yates,et al.  Photocatalysis on TiO2 Surfaces: Principles, Mechanisms, and Selected Results , 1995 .

[31]  A. Manthiram,et al.  New Route to Reduced Transition-Metal Oxides , 1994 .

[32]  C. Leygraf,et al.  Effects of electrochemical reduction of polycrystalline TiO2 photoelectrodes in acidic solutions , 1987 .

[33]  Xiaolin Zheng,et al.  Flame synthesis of WO3 nanotubes and nanowires for efficient photoelectrochemical water-splitting , 2013 .

[34]  X. Bao,et al.  The enhancement of TiO2 photocatalytic activity by hydrogen thermal treatment. , 2003, Chemosphere.

[35]  Phaedon Avouris,et al.  Field-Effect Transistors Based on Single Semiconducting Oxide Nanobelts , 2003 .