论文信息 - Data from crosslinked PS honeycomb thin film by deep UV irradiation

Data from crosslinked PS honeycomb thin film by deep UV irradiation

Thin polystyrene (PS) films with highly ordered honeycomb pattern were successfully fabricated by an improved phase separation method. The PS film was successfully crosslinked after applying a deep UV irradiation. This work presents a proof of crosslinking PS by characterizing ATR-FTIR, TGA and the wetting property of the honeycomb films, which were prepared using a solvent/non-solvent ratio of 90/10, before and after 6 h of UV irradiation.

Jae-Hak Choi | Ho-Suk Choi | Van-Tien Bui | Hwa Su Lee

[1] Martina H. Stenzel,et al. Honeycomb structured polymer films via breath figures , 2012 .

[2] Bin Wang,et al. Advances in Fabrication Materials of Honeycomb Structure Films by the Breath-Figure Method , 2013, Materials.

[3] Aijuan Zhang,et al. Breath figure arrays: unconventional fabrications, functionalizations, and applications. , 2013, Angewandte Chemie.

[4] Highly ordered and robust honeycomb films with tunable pore sizes fabricated via UV crosslinking after applying improved phase separation , 2015 .

[5] Aijuan Zhang,et al. Fabrication of robust honeycomb polymer films: a facile photochemical cross-linking process. , 2009, Journal of colloid and interface science.

[6] U. Bunz,et al. Breath Figures as a Dynamic Templating Method for Polymers and Nanomaterials , 2006 .

[7] Zhi‐Kang Xu,et al. Multiple interfaces in self-assembled breath figures. , 2014, Chemical communications.