In vitro and in vivo degradation of poly(1,3-diamino-2-hydroxypropane-co-polyol sebacate) elastomers.

Biomaterials with a wide range of tunable properties are desirable for application-specific purposes. We have previously developed a class of elastomeric poly(ester amides) based on the amine alcohol 1,3-diamino-2-hydroxypropane termed poly(1,3-diamino-2-hydroxypropane-co-polyol sebacate) or APS. In this work, we have synthesized and characterized formulations of APS polymers and studied the degradation of these polymers in vitro and in vivo. It was found that the chemical, physical, and mechanical properties of APS polymers could be tuned by adjusting monomer feed ratios and polymerization conditions. The degradation kinetics could also be greatly influenced by altering the formulation of APS polymers. In vivo degradation half-lives ranged from 6 to approximately 100 weeks. Furthermore, the dominant degradation mechanism (i.e. hydrolytic or enzymatic) could be controlled by adjusting the specific formulation of the APS polymer. On the basis of the observed in vitro and in vivo biodegradation phenomena, we also propose that the primary modes of degradation are composition dependent.

[1]  Robert Langer,et al.  Biodegradable Xylitol‐Based Polymers , 2008 .

[2]  Jeffrey T Borenstein,et al.  Amino alcohol-based degradable poly(ester amide) elastomers. , 2008, Biomaterials.

[3]  J. Karp,et al.  Synthesis and characterization of photocurable elastomers from poly(glycerol-co-sebacate). , 2007, Biomacromolecules.

[4]  V. Bhardwaj,et al.  Estradiol loaded PLGA nanoparticles for oral administration: effect of polymer molecular weight and copolymer composition on release behavior in vitro and in vivo. , 2007, Journal of controlled release : official journal of the Controlled Release Society.

[5]  A. Miller,et al.  In Vitro Degradation of Poly(lactic‐co2‐glycolic) Acid Random Copolymers , 2007 .

[6]  S. Oh,et al.  Degradation behavior of hydrophilized PLGA scaffolds prepared by melt-molding particulate-leaching method: Comparison with control hydrophobic one , 2006, Journal of materials science. Materials in medicine.

[7]  B. Amsden,et al.  In vivo degradation behavior of photo-cross-linked star-poly(epsilon-caprolactone-co-D,L-lactide) elastomers. , 2006, Biomacromolecules.

[8]  A. Entezami,et al.  DEGRADITION OF POLY (D,L-LACTIDE-CO-GLYCOLIDE) 50:50 IMPLANT IN AQUEOUS MEDIUM , 2005 .

[9]  J Tramper,et al.  The effect of PEGT/PBT scaffold architecture on oxygen gradients in tissue engineered cartilaginous constructs. , 2004, Biomaterials.

[10]  B. Amsden,et al.  Synthesis and Characterization of Thermoset Biodegradable Elastomers Based on Star-Poly(ε-caprolactone-co-d,l-lactide) , 2004 .

[11]  Guillermo Antonio Ameer,et al.  Novel Citric Acid‐Based Biodegradable Elastomers for Tissue Engineering , 2004 .

[12]  Robert Langer,et al.  In vivo degradation characteristics of poly(glycerol sebacate). , 2003, Journal of biomedical materials research. Part A.

[13]  R. Langer,et al.  A tough biodegradable elastomer , 2002, Nature Biotechnology.

[14]  J. Yoon,et al.  Degradation behaviors of biodegradable macroporous scaffolds prepared by gas foaming of effervescent salts. , 2001, Journal of biomedical materials research.

[15]  David J. Mooney,et al.  Controlled growth factor release from synthetic extracellular matrices , 2000, Nature.

[16]  A. Mikos,et al.  In vitro degradation of thin poly(DL-lactic-co-glycolic acid) films. , 1999, Journal of biomedical materials research.

[17]  M. Burrell Enzymes of Molecular Biology , 1993 .

[18]  P. J. Sweeney,et al.  Pronase (EC 3.4.24.4). , 1993, Methods in molecular biology.

[19]  R. Kenley,et al.  Poly(lactide-co-glycolide) decomposition kinetics in vivo and in vitro , 1987 .

[20]  G. Gechele,et al.  Polyamides in solution. III. Viscometry of linear polycaprolactam , 1969 .