Mechanical properties of monolithic silica aerogels made from polyethoxydisiloxanes

Abstract We report the preparation and characterization of a broad range of hydrophobic monolithic silica aerogels and xerogels made from polyethoxydisiloxane (PEDS-P750E20) precursors. Transparent silica aerogels with densities spanning  ≈  0.05 to >0.32 g/cm3 were synthesized and the effects of density on the mechanical, microstructural, and thermal properties were studied. In the samples investigated, the elastic modulus E was found to vary from 40 kPa to 70 MPa, compressive strength σ C from 500 kPa to 4.2 MPa, fracture strain e F from 9% to >80%, tensile strength σ T from 11 kPa to 315 kPa, and thermal conductivity λ from 13.5 mW/m K to 24.5 mW/m K. The failure mode of the aerogels was observed to be density dependent and transition with increasing density from ductile compaction to elastic deformation to brittle fracture. Within the density range where elastic behavior was observed, the compressive strength of the silica aerogels was measured to be roughly one order of magnitude higher than would be expected from brittle materials due to the materials ability to absorb energy; these aerogels recovered elastically after being subjected to compressive strains as high as 40%. BET analysis using nitrogen adsorption revealed specific surface areas of ≈ 740–780 m2/g and average pore sizes in the range of 26–72 nm.

[1]  Schoeller.  Leitfaden der theoretischen Chemie. Von Prof. W. Herz. Verlag von Ferdinand Enke, Stuttgart. Dritte Auflage , 1924 .

[2]  Ken Qassim,et al.  Ultra-Lightweight Aerogel Superinsulation as an MLI Replacement , 2004 .

[3]  M. Einarsrud,et al.  Improvement of the silica aerogel strengthening process for scaling-up monolithic tile production , 2004 .

[4]  J. Esteve,et al.  Micromechanical properties of silica aerogels , 1999 .

[5]  Ulrich R. Boes,et al.  Aerogel-based thermal insulation , 1998 .

[6]  Finn Harken Kristiansen,et al.  Development of windows based on highly insulating aerogel glazings , 2004 .

[7]  Jie Cai,et al.  Cellulose-silica nanocomposite aerogels by in situ formation of silica in cellulose gel. , 2012, Angewandte Chemie.

[8]  Samuel Brunner,et al.  Thermo-hygric properties of a newly developed aerogel based insulation rendering for both exterior and interior applications , 2012 .

[9]  Mohammad Hasan Abbasi,et al.  Silica aerogel; synthesis, properties and characterization , 2008 .

[10]  Gérard Michot,et al.  The Brazilian test: a tool for measuring the toughness of a material and its brittle to ductile transition , 2006 .

[11]  G. Reichenauer,et al.  Relationship between pore size and the gas pressure dependence of the gaseous thermal conductivity , 2007 .

[12]  Arild Gustavsen,et al.  Aerogel insulation for building applications: A state-of-the-art review , 2011 .

[13]  Kelly E. Parmenter,et al.  Mechanical properties of silica aerogels , 1998 .

[14]  J. Satcher,et al.  Super‐Compressibility of Ultralow‐Density Nanoporous Silica , 2012, Advanced materials.

[15]  M. Einarsrud,et al.  Strengthening and aging of wet silica gels for up-scaling of aerogel preparation , 2007 .

[16]  S. Kistler,et al.  Coherent Expanded Aerogels and Jellies. , 1931, Nature.

[17]  A. V. Rao,et al.  Comparison of some physical properties of silica aerogel monoliths synthesized by different precursors , 1999 .

[18]  H. Sallée,et al.  Investigation of the multi-scale structure of silica aerogels by SAXS , 2001 .

[19]  Lawrence W. Hrubesh,et al.  Thermal properties of organic and inorganic aerogels , 1994 .

[20]  M. Einarsrud,et al.  Strengthening of silica gels and aerogels by washing and aging processes , 2001 .

[21]  P. Achard,et al.  Physical properties of silica gels and aerogels prepared with new polymeric precursors , 1995 .

[22]  G. Nicolaon,et al.  Inorganic oxide aerogels , 1976 .

[23]  Characterization of silica aerogel with the atomic force microscope and SAXS , 1995 .

[24]  S. Kistler.  Coherent Expanded-Aerogels , 1931 .

[25]  Jun Shen,et al.  Physical Properties of Silica Aerogels Prepared with Polyethoxydisiloxanes , 2000 .

[26]  Zhou Bin,et al.  Ultralow density silica aerogels prepared with PEDS , 2009 .

[27]  Mechanical Properties of Gel-Derived Materials , 2000 .

[28]  Erik Bardy,et al.  Thermal Conductivity and Compressive Strain of Aerogel Insulation Blankets Under Applied Hydrostatic Pressure , 2007 .