Dust‐induced shading on photovoltaic modules

The effect of dust on photovoltaic modules is investigated with respect to concentration and spectral transmittance. Samples were collected in the form of raw dust as well as accumulated dust on exposed sheets of glass at different tilt angles. Spectral transmittance of the samples was determined. Transmittance variation between top, middle and bottom was identified for samples collected at different inclinations, where the worst case was seen at a tilt angle of 30o with a non-uniformity of 4.4% in comparison with 0.2% for the 90° tilt. The measured data showed a decrease in transmittance at wavelengths <570 nm. Integrating this with measured spectral responses of different technologies demonstrates that wide band-gap thin-film technologies are affected more than, for example crystalline silicon technologies. The worst case is amorphous silicon, where a 33% reduction in photocurrent is predicted for a dust concentration of 4.25 mg/cm2. Similarly, crystalline silicon and CIGS technologies are predicted to be less affected, with 28.6% and 28.5% reductions in photocurrent, respectively. The same procedure was repeated with varying Air Mass (AM), tilt angle and dust concentration values to produce a soiling ratio table for different technologies under different AM, tilt angle and dust concentration values. Copyright © 2012 John Wiley & Sons, Ltd.

[1]  M. S. El-Shobokshy,et al.  Degradation of photovoltaic cell performance due to dust deposition on to its surface , 1993 .

[2]  Laurent Pilon,et al.  Optical constants of silica glass from extreme ultraviolet to far infrared at near room temperature. , 2007, Applied optics.

[3]  M. S. El-Shobokshy,et al.  Effect of dust with different physical properties on the performance of photovoltaic cells , 1993 .

[4]  Rohit Pillai,et al.  Impact of dust on solar photovoltaic (PV) performance: Research status, challenges and recommendations , 2010 .

[5]  L. Protin,et al.  Static device for improving a high voltage photovoltaic generator working under dusty conditions , 1990 .

[6]  M. M. Beheary,et al.  Effect of dust on the transparent cover of solar collectors , 2006 .

[7]  R. L. Hammond,et al.  Effects of soiling on PV module and radiometer performance , 1997, Conference Record of the Twenty Sixth IEEE Photovoltaic Specialists Conference - 1997.

[8]  R. Gottschalg,et al.  Effect of shading caused by dust on Cadmium Telluride photovoltaic modules , 2011, 2011 37th IEEE Photovoltaic Specialists Conference.

[9]  Luis Marroyo,et al.  Soiling and other optical losses in solar‐tracking PV plants in navarra , 2011 .

[10]  H. Möller,et al.  Performance Evaluation of CdTe PV Modules under Natural Outdoor Conditions in Kuwait , 2010 .

[11]  Kazuyuki Takami,et al.  Anti-soiling layer coarted on PMMA Fresnel lens for concentrator photovoltaic modules , 2011, 2011 37th IEEE Photovoltaic Specialists Conference.

[12]  Syed A.M. Said,et al.  Effects of dust accumulation on performances of thermal and photovoltaic flat-plate collectors , 1990 .

[13]  D. Goossens,et al.  Aeolian dust deposition on photovoltaic solar cells: the effects of wind velocity and airborne dust concentration on cell performance , 1999 .

[14]  S. Bruynooghe,et al.  Realization of High Performance AR-coatings with Dust- and Water-Repellent Properties , 2008 .

[15]  A. al-Ḥasan.  A new correlation for direct beam solar radiation received by photovoltaic panel with sand dust accumulated on its surface , 1998 .

[16]  D. Goossens,et al.  Wind tunnel experiments and field investigations of eolian dust deposition on photovoltaic solar collectors , 1993 .

[17]  S. Biryukov,et al.  An experimental study of the dry deposition mechanism for airborne dust , 1998 .

[18]  Huey Pang,et al.  Study on Effect of Urban Pollution to Performance of Commercial Copper Indium Diselenide Modules , 2006, 2006 IEEE 4th World Conference on Photovoltaic Energy Conference.