Structural properties of the titanium dioxide thin films grown by atomic layer deposition at various numbers of reaction cycles

Abstract A dependence of structural properties of TiO 2 films grown on both Si- and Ti-substrates by atomic layer deposition (ALD) at the temperature range of 250–300 °C from titanium ethoxide and water on the number of reaction cycles N was investigated using Fourier-transform infrared (FTIR) spectroscopy and X-Ray diffraction (XRD). TiO 2 films grown on both Si- and Ti-substrates revealed amorphous structure at low values of N N up to values 400–3600 resulted in the growth of polycrystalline TiO 2 with structure of anatase on both types of substrates and according to XRD-measurements the sizes of crystallites rose with the increase of N . The maximum anatase crystallite size for TiO 2 grown on Ti-substrate was found to be on ∼35% lower in comparing with that for TiO 2 grown on Si-substrate. A use of titanium methoxide as a Ti precursor with the ligand size smaller than in case of titanium ethoxide allowed to observe an influence of the ligand size on both the growth per cycle and structural properties of TiO 2 . The average growth per cycle of TiO 2 deposited from titanium methoxide and water (0.052 ± 0.01 nm/cycle) was essentially higher than that for TiO 2 grown from titanium ethoxide and water (0.043 ± 0.01 nm/cycle). Ligands of smaller sizes were found to promote the higher crystallinity of TiO 2 in comparison with the case of using the titanium precursor with ligands of bigger sizes.

[1]  M. Ritala,et al.  Atomic force microscopy study of titanium dioxide thin films grown by atomic layer epitaxy , 1993 .

[2]  Riikka L. Puurunen,et al.  Growth Per Cycle in Atomic Layer Deposition: Real Application Examplesof a Theoretical Model , 2003 .

[3]  H. Engqvist,et al.  In Vitro Bioactivity of Atomic Layer Deposited Titanium Dioxide on Titanium and Silicon Substrates , 2007 .

[4]  R. Greenler.  Infrared Study of Adsorbed Molecules on Metal Surfaces by Reflection Techniques , 1966 .

[5]  Pekka Soininen,et al.  Growth of titanium dioxide thin films by atomic layer epitaxy , 1993 .

[6]  Jaan Aarik,et al.  Conformity and structure of titanium oxide films grown by atomic layer deposition on silicon substrates , 2008 .

[7]  M. Ritala,et al.  Titanium isopropoxide as a precursor for atomic layer deposition: characterization of titanium dioxide growth process , 2000 .

[8]  Tuomo Suntola,et al.  Atomic layer growth of TiO2 on silica , 1992 .

[9]  M. Ritala,et al.  Titanium isopropoxide as a precursor in atomic layer epitaxy of titanium dioxide thin films , 1993 .

[10]  S. I. Kol'tsov,et al.  Damping of the Growth of Titanium Oxide Nanolayer Formed by Molecular Layer Deposition Technique on Oxidized Silicon Surface , 2004 .

[11]  Mikko Ritala,et al.  Atomic Layer Deposition of Photocatalytic TiO2 Thin Films from Titanium Tetramethoxide and Water , 2004 .

[12]  M. Ritala,et al.  Atomic layer epitaxy growth of titanium dioxide thin films from titanium ethoxide , 1994 .

[13]  M. Ritala,et al.  Characterization of titanium dioxide atomic layer growth from titanium ethoxide and water , 2000 .

[14]  M. D. Moraes,et al.  Berreman effect applied to phase characterization of thin films supported on metallic substrates: The case of TiO 2 , 2001 .

[15]  M. Ritala,et al.  In Situ Mass Spectrometry Study on Atomic Layer Deposition from Metal (Ti, Ta, and Nb) Ethoxides and Water , 2001 .

[16]  H. Nalwa.  Handbook of thin film materials , 2002 .

[17]  Ian W. Boyd,et al.  Nanocrystalline TiO2 films studied by optical, XRD and FTIR spectroscopy , 2002 .

[18]  J. Aarik,et al.  Influence of structure development on atomic layer deposition of TiO2 thin films , 2001 .

[19]  M. Ritala,et al.  Reaction mechanism studies on titanium isopropoxide-water atomic layer deposition process , 2002 .