Strength improvement to composite T-joints under bending through bio-inspired design

This paper shows that a bio-inspired design methodology is an effective method to strengthen composite T-joints under bending loading. The ply angles in the laminate of a carbon/epoxy T-joint were tailored using an optimisation program mimicking the evolutionary process of adaptive growth in which the wood microfibril orientation in and around the tree branch-trunk joint is tailored to the prevailing bending loading condition. A single objective optimisation program with four ply angle input variables was used to compute the optimal design of the ply stacking pattern which minimised the interlaminar tensile stress in composite T-joints where delamination damage is initiated. FEA and experimental testing were performed to compare the structural properties of the bio-inspired T-joint against a base-line T-joint with a quasi-isotropic ply stacking pattern. The bio-inspired T-joint exhibited a higher bending failure initiation load (improved by 40%) and elastic strain energy capacity (increased by 75%) than the base-line T-joint.

[1]  K. Bethge,et al.  The Structural Optimization of Trees , 1998, Naturwissenschaften.

[2]  Yasuaki Seki,et al.  Biological materials: Structure and mechanical properties , 2008 .

[3]  S. Donaldson,et al.  Strength of composite angle brackets with multiple geometries and nanofiber-enhanced resins , 2011 .

[4]  Stefanie Feih,et al.  Bio-inspired design of aerospace composite joints , 2011 .

[5]  Stefanie Feih,et al.  Composite failure prediction of single-L joint structures under bending , 2005 .

[6]  Dan Zenkert,et al.  Testing and analysis of ultra thick composites , 2010 .

[7]  C. Sun,et al.  Failure in Composite Angle Structures Part I: Initial Failure , 1988 .

[8]  I. Burgert,et al.  Adaptive Growth of Gymnosperm Branches-Ultrastructural and Micromechanical Examinations , 2004, Journal of Plant Growth Regulation.

[9]  Javid Bayandor,et al.  Compression and post-buckling damage growth and collapse analysis of flat composite stiffened panels , 2008 .

[10]  R. A. Shenoi,et al.  Fatigue failure mechanisms in fibre-reinforced plastic laminated tee joints , 1995 .

[11]  C. Mattheck,et al.  Three-dimensional fibre optimisation with computer aided internal optimisation , 1999, The Aeronautical Journal (1968).

[12]  R. A. Shenoi,et al.  Design of joints and attachments in FRP ships' structures , 1994 .

[13]  M A Meyers,et al.  Structure and mechanical properties of selected biological materials. , 2008, Journal of the mechanical behavior of biomedical materials.

[14]  C. Sun,et al.  Failure in Composite Angle Structures Part II: Onset of Delamination , 1988 .

[15]  J. M Dulieu-Barton,et al.  Determination of the stress distribution in foam-cored sandwich construction composite tee joints , 2001 .

[16]  I. Burgert,et al.  A close-up view of wood structure and properties across a growth ring of Norway spruce (Picea abies [L] Karst.) , 2009, Trees.

[17]  Tanchum Weller,et al.  Failure analysis in postbuckled composite T-sections , 2008 .

[18]  R. Long,et al.  Static Strength of Adhesively Bonded ARALL-1 Joints , 1991 .

[19]  R. A. Shenoi,et al.  Thermoelastic stress analysis of a GRP tee joint , 1997 .

[20]  C. Mattheck,et al.  Trees As A Model For Technical Fibre Composites , 2001 .

[21]  Yan Yu,et al.  Microfibril angle variability in Masson Pine (Pinus massoniana Lamb.) using X-ray diffraction , 2007 .

[22]  Influence of Joint Geometry and Load Regimes on Sandwich Tee Joint Behaviour , 1998 .

[23]  E. Olevsky,et al.  Energy absorbent natural materials and bioinspired design strategies: A review , 2010 .

[24]  Francois Barthelat,et al.  Merger of structure and material in nacre and bone - Perspectives on de novo biomimetic materials , 2009 .

[25]  Robert A. Haynes,et al.  New Families of Hygrothermally Stable Composite Laminates with Optimal Extension-Twist Coupling , 2010 .

[26]  S. Donaldson.  Simplified Weight Savings Techniques for Composite Panels , 1983 .

[27]  Javid Bayandor,et al.  An analysis methodology for failure in postbuckling skin-stiffener interfaces , 2008 .

[28]  G. Jeronimidis,et al.  Biomechanics of a branch – stem junction in softwood , 2006, Trees.

[29]  E. Armanios,et al.  Families of Hygrothermally Stable Asymmetric Laminated Composites , 2008 .

[30]  Richard Degenhardt,et al.  Degradation investigation in a postbuckling composite stiffened fuselage panel , 2008 .

[31]  R. A. Shenoi,et al.  Influence of material and geometry variations on the behaviour of bonded tee connections in FRP ships , 1992 .

[32]  Stefanie Feih,et al.  Bio-inspired design of aerospace composite joints for improved damage tolerance , 2012 .

[33]  Donald W. Radford,et al.  Shape Instabilities in Composites Resulting from Laminate Anisotropy , 1993 .

[34]  Peter Fratzl,et al.  The role of material properties for the mechanical adaptation at branch junctions , 2009, Trees.