Influence of Thermal Aging on the Combustion Characteristics of Cables in Nuclear Power Plants

: In this study, the combustion characteristics and emission of toxic gases of a non-class 1E cable in a nuclear power plant were investigated with respect to the aging period. A thermal accelerated aging method was applied using the Arrhenius equation with the activation energy of the cables and the aging periods of the cables set to zero, 10, 20, 30 and 40 years old by considering the lifetime of a nuclear power plant. According to ISO 5660-1 and ISO 19702, the cone calorimeter Fourier transform infrared spectroscopy test was performed to analyze the combustion characteristics and emission toxicity. In addition, scanning electron microscopy and an energy dispersive X-ray spectrometer were used to examine the change in the surface of the sheath and insulation of the cables according to the aging periods. To compare quantitative fire risks at an early period, the fire performance index (FPI) and fire growth index (FGI) are derived from the test results of the ignition time, peak heat release rate (PHRR) and time to PHRR (tPHRR). When comparing FPI and FGI, the fire risks decreased as the aging period increased, which means that early fire risks may be alleviated through the devolatilization of both the sheath and insulation of the cables. However, when comparing heat release and mass loss, which represent the fire risk at the mid and late period, fire intensity and severity increased with the aging period. The emission of toxic gases coincided with the results obtained from the heat release rate, which confirms that the toxicity of non-aged cables is higher than that of aged cables. From the results, it can be concluded that the aging period significantly affects both the combustion characteristics and toxicity of the emission gas. Therefore, cable degradation with aging should be considered when setting up reinforced safety codes and standards for cables and planning proper operation procedures for nuclear power plants. formal analysis, M.H.K. and M.C.L.; funding S.K.L.; investigation, M.H.K.; methodology, M.H.K., H.J.S., S.K.L. and M.C.L.; validation, M.H.K. and M.C.L.; writing—original draft, M.H.K.; writing—review editing,

[1]  N. Bowler,et al.  Aging Mechanisms and Monitoring of Cable Polymers , 2020 .

[2]  Xin Ma,et al.  Combustion behaviors and characteristic parameters determination of sassafras wood under different heating conditions , 2020 .

[3]  Jae-ho Kim,et al.  Investigation on the Insulation Resistance Characteristics of Low Voltage Cable , 2020 .

[4]  Shengtao Li,et al.  Thermal-Oxidative Aging Effects on the Dielectric Properties of Nuclear Cable Insulation , 2020, Materials.

[5]  Shengtao Li,et al.  Influence of Oxygen Diffusion on Thermal Ageing of Cross-Linked Polyethylene Cable Insulation , 2020, Materials.

[6]  Min Chul Lee,et al.  Investigation into the toxicity of combustion products for CR/EPR cables based on aging period , 2020, Journal of Mechanical Science and Technology.

[7]  Wenwei Zhu,et al.  Thermal Effect of Different Laying Modes on Cross-Linked Polyethylene (XLPE) Insulation and a New Estimation on Cable Ampacity , 2019, Energies.

[8]  H. Seo,et al.  An Experimental Study on the Combustion Characteristics of Non Class 1E Cables , 2019, Journal of The Korean Society of Combustion.

[9]  Larbi Boukezzi,et al.  Study of thermal aging effects on the conduction and trapping of charges in XLPE cable insulations under electron beam irradiation , 2018, Radiation Physics and Chemistry.

[10]  B. G. Fernandes,et al.  An approach for reliability prediction of instrumentation & control cables by artificial neural networks and Weibull theory for probabilistic safety assessment of NPPs , 2018, Reliab. Eng. Syst. Saf..

[11]  R. Sonnier,et al.  Fire behavior of halogen-free flame retardant electrical cables with the cone calorimeter. , 2018, Journal of hazardous materials.

[12]  Jiaqing Zhang,et al.  Effects of Insulating Material Ageing on Ignition Time and Heat Release Rate of the Flame Retardant Cables , 2018 .

[13]  Yoshimichi Ohki,et al.  Dielectric and Carrier Transport Properties of Silicone Rubber Degraded by Gamma Irradiation , 2017, Polymers.

[14]  Yongqian Shi,et al.  The influence of zinc hydroxystannate on reducing toxic gases (CO, NO(x) and HCN) generation and fire hazards of thermoplastic polyurethane composites. , 2016, Journal of hazardous materials.

[15]  M. Konstantinović,et al.  Influence of γ-irradiation and temperature on the mechanical properties of EPDM cable insulation , 2016 .

[16]  D. Lázaro,et al.  Study of tunnel pavements behaviour in fire by using coupled cone calorimeter – FTIR analysis , 2016 .

[17]  A. Mekhaldi,et al.  Physico-chemical study of thermally aged EPDM used in power cables insulation , 2015, IEEE Transactions on Dielectrics and Electrical Insulation.

[18]  G. Lee,et al.  Mechanical Properties and Statistical Evaluation of EPR According to the Accelerated Degradation , 2015 .

[19]  J. Chaouki,et al.  A modified microwave thermo-gravimetric-analyzer for kinetic purposes , 2015 .

[20]  Ji Yeon Kim,et al.  Thermal analysis and statistical evaluation of EPR used in nuclear power plants , 2014, 2014 International Conference on Advances in Communication and Computing Technologies (ICACACT 2014).

[21]  F. Richard,et al.  Characterization of the thermal decomposition of two kinds of plywood with a cone calorimeter – FTIR apparatus , 2014 .

[22]  G. Montanari,et al.  Electrical aging markers for EPR-based low-voltage cable insulation wiring of nuclear power plants , 2014 .

[23]  A. Pütün,et al.  PYROLYSIS KINETICS AND THERMAL DECOMPOSITION BEHAVIOR OF POLYCARBONATE - a TGA-FTIR study , 2014 .

[24]  R. Pfaendner.  Photo)oxidative degradation and stabilization of flame retarded polymers , 2013 .

[25]  Gary Harmon,et al.  Methods for testing nuclear power plant cables , 2013, IEEE Instrumentation & Measurement Magazine.

[26]  É. Guillaume,et al.  Accuracy (Trueness and Precision) of Cone Calorimeter Tests with and Without a Vitiated Air Enclosure , 2013 .

[27]  H. E. Kissinger,et al.  Homer Kissinger and the Kissinger equation , 2012 .

[28]  G. Heinrich,et al.  Enhanced thermal stability of polychloroprene rubber composites with ionic liquid modified MWCNTs , 2012 .

[29]  Yan Yu,et al.  The pyrolysis characteristics of moso bamboo , 2012 .

[30]  É. Guillaume,et al.  Characterization of thermal properties and analysis of combustion behavior of PMMA in a cone calorim , 2011 .

[31]  Yongqian Shi,et al.  Effect of cellulose acetate butyrate microencapsulated ammonium polyphosphate on the flame retardancy, mechanical, electrical, and thermal properties of intumescent flame-retardant ethylene-vinyl acetate copolymer/microencapsulated ammonium polyphosphate/polyamide-6 blends. , 2011, ACS applied materials & interfaces.

[32]  Hairui Yang,et al.  Analysis of the behaviour of pollutant gas emissions during wheat straw/coal cofiring by TGFTIR , 2011 .

[33]  A. Zabaniotou,et al.  Thermal degradation studies and kinetic modeling of cardoon (Cynara cardunculus) pyrolysis using thermogravimetric analysis (TGA). , 2011, Bioresource technology.

[34]  Robert Bernstein,et al.  Review of nuclear power plant safety cable aging studies with recommendations for improved approaches and for future work. , 2010 .

[35]  Jun Zhang,et al.  Synergistic Effects of Fe2O3 with Layered Double Hydroxides in EVA/LDH Composites , 2009 .

[36]  Xuguang Jiang,et al.  TG-FTIR analysis of PVC thermal degradation and HCl removal , 2008 .

[37]  B. Kutchko,et al.  Fly ash characterization by SEM–EDS , 2006 .

[38]  K. Chang-Liao,et al.  Monitoring the moisture-related degradation of ethylene propylene rubber cable by electrical and SEM methods , 2006 .

[39]  C. Genestar,et al.  Earth pigments in painting: characterisation and differentiation by means of FTIR spectroscopy and SEM-EDS microanalysis , 2005, Analytical and bioanalytical chemistry.

[40]  V. Balek,et al.  Thermal degradation of PVC cable insulation studied by simultaneous TG-FTIR and TG-EGA methods , 2004 .

[41]  R. Delobel,et al.  Elaboration of a fire retardant coating for polyamide-6 using cold plasma polymerization of a fluorinated acrylate , 2004 .

[42]  P. Nowlen,et al.  An Investigation of the Effects of Thermal Aging on, the Fire Damageability of Electric Cables , 2004 .

[43]  W. Fan,et al.  Effects of poly(ethylene‐co‐propylene) elastomer on mechanical properties and combustion behaviour of flame retarded polyethylene/magnesium hydroxide composites , 2002 .

[44]  R. Iezzi,et al.  Acrylic-fluoropolymer mixtures and their use in coatings , 2000 .

[45]  E. Bravin,et al.  Application of cone calorimeter for the assessment of class of flame retardants for polypropylene , 1998 .

[46]  J. Lin,et al.  Morphology of perfluoroalkylacrylate/stearyl methacrylate polymers and their effect on water/oil repellency , 1997 .