The minority carrier lifetime in doped and undoped p-type Hg0.78Cd0.22Te liquid phase epitaxy films

This paper will describe: (1) the first comparative study of recombination mechanisms between doped and undoped p-type Hg1-xCdxTe liquid phase epitaxy films with an x value of about 0.22, and (2) the first determination of τA7i/τA1i ratio by lifetime’s dependence on both carrier concentration and temperature. The doped films were either copper- or gold-doped with the carrier concentration ranging from 2 x 1015 to 1.5 x 1017 cm-3, and the lifetime varied from 2 μs to 8 ns. The undoped (Hg-vacancy) films had a carrier concentration range between 3 x 1015 and 8 x 1016 cm-3, and the lifetime changed from 150 to 3 ns. It was found that for the same carrier concentration, the doped films had lifetimes several times longer than those of the undoped films, limited mostly by Auger 7 and radiative recombination processes. The ineffectiveness of Shockley-Read-Hall (SRH) recombination process in the doped films was also demonstrated in lifetime vs temperature curves. The important ratio of intrinsic Auger 7 lifetime to intrinsic Auger 1 lifetime, τA7i/τA1i, was determined to be about 20 from fitting both concentration and temperature curves. The reduction of minority carrier lifetime in undoped films can be explained by an effective SRH recombination center associated with the Hg vacancy. Indeed, a donor-like SRH recombination center located at midgap (Ev+60 meV) with a capture cross section for minority carriers much larger than that for majority carriers was deduced from fitting lifetime vs temperature curves of undoped films.

[1]  Y. Nemirovsky,et al.  The excess carrier lifetime in p‐type HgCdTe measured by photoconductive decay , 1989 .

[2]  P. Capper,et al.  Minority carrier lifetime in doped and undoped p-type CdxHg1-xTe , 1987 .

[3]  E. Finkman,et al.  Recombination mechanisms in p-type HgCdTe: Freezeout and background flux effects , 1985 .

[4]  A. Krotkus,et al.  Minority carrier recombination in p-type CdxHg1-xTe , 1990 .

[5]  Jose M. Arias,et al.  Assessment of HgCdTe and GaAs/GaAlAs technologies for LWIR infrared imagers , 1992, Optics & Photonics.

[6]  S. Ron,et al.  Investigation of the bulk and surface electronic properties of HgCdTe epitaxial layers using photoelectromagnetic, Hall, and photoconductivity measurements , 1992 .

[7]  D. Polla,et al.  Experimental determination of minority‐carrier lifetime and recombination mechanisms in p‐type Hg1−xCdxTe , 1981 .

[8]  S. Schacham,et al.  Surface recombination velocity of anodic sulfide and ZnS coated p-HgCdTe , 1989 .

[9]  Yael Nemirovsky,et al.  Interface of p‐type Hg1−xCdxTe passivated with native sulfides , 1985 .

[10]  J. Merz,et al.  Status of point defects in HgCdTe , 1985 .

[11]  M. Chen.  Photoconductivity lifetime measurements on HgCdTe using a contactless microwave technique , 1988 .

[12]  J. Faurie,et al.  Minority‐carrier lifetime in p‐type (111)B HgCdTe grown by molecular‐beam epitaxy , 1990 .

[13]  T. N. Casselman,et al.  Calculation of the Auger lifetime in p‐type Hg1‐xCdxTe , 1981 .