Rising Crack-Growth-Resistance (R-Curve) Behavior of Toughened Alumina and Silicon Nitride

R-curves for a sinter/HIPed SiC(whisker)-reinforced alumina and a sintered silicon nitride were assessed by direct measurements of lengths of cracks associated with Vickers indentation flaws. The fracture toughness measurements based on (a) initial (as-indented) crack lengths, (b) equilibrium growth of cracks during increasing far-field loading, and (c) crack lengths corresponding to unstable fracture showed definitive trends of R-curves for both materials. The fracture mechanics analyses employed an indenter-material constant that was independently estimated using a physical model for the residual driving force and a free surface correction factor that accounted for the effects of size and shape of the cracks on stress intensity. It is shown that R-curve estimations based on crack length measurements have the intrinsic advantage that crack length dependence of fracture toughness is not assumed a priori as is done in conventional analysis based on strength. The measured fracture toughness of SiC(whisker)-reinforced alumina was in agreement with the prediction of a toughening model based on crack bridging by partially debonded whiskers.

[1]  R. Cook,et al.  Microstructure-strength properties in ceramics. I: Effect of crack size on toughness , 1985 .

[2]  A. Evans,et al.  Elastic/Plastic Indentation Damage in Ceramics: The Median/Radial Crack System , 1980 .

[3]  A. Evans,et al.  Small-scale crack bridging and the fracture toughness of particulate-reinforced ceramics , 1988 .

[4]  R. Steinbrech,et al.  Crack‐Resistance Curves of Surface Cracks in Alumina , 1988 .

[5]  D. Marshall,et al.  Crack Resistance Curves in Magnesia‐Partially‐Stabilized Zirconia , 1988 .

[6]  Y. Mai,et al.  Crack‐Interface Grain Bridging as a Fracture Resistance Mechanism in Ceramics: II, Theoretical Fracture Mechanics Model , 1987 .

[7]  A. Evans,et al.  On the toughening of ceramics by strong reinforcements , 1986 .

[8]  Brian R. Lawn,et al.  A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: I , 1981 .

[9]  W. L. Vaughn,et al.  R-curve behavior in a silicon carbide whisker/alumina matrix composite , 1990 .

[10]  Dinesh K. Shetty,et al.  Crack Stability and Strength Distribution of Ceramics That Exhibit Rising Crack‐Growth‐Resistance (R‐Curve) Behavior , 1989 .

[11]  R. Krause.  Rising Fracture Toughness from the Bending Strength of Indented Alumina Beams , 1988 .

[12]  Chun-Hway Hsueh,et al.  Toughening Behavior in Whisker‐Reinforced Ceramic Matrix Composites , 1988 .

[13]  A “Compressed‐Spring” Analogy for Residual Stress Effects on the Extension of Indenter Flaws , 1984 .

[14]  James C. Newman,et al.  An empirical stress-intensity factor equation for the surface crack , 1981 .

[15]  B. Lawn,et al.  A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: II, Strength Method , 1981 .

[16]  R. Cook,et al.  A Modified Indentation Toughness Technique , 1983 .

[17]  D. Shetty,et al.  Transformation yielding, plasticity and crack-growth-resistance (R-curve) behaviour of CeO2-TZP , 1990 .

[18]  T. W. Thorpe,et al.  A CRITICAL REVIEW OF CRACK TIP STRESS INTENSITY FACTORS FOR SEMI-ELLIPTIC CRACKS* , 1981 .

[19]  L. Rose.  Crack reinforcement by distributed springs , 1987 .

[20]  B. Majumdar,et al.  Analysis of R-curve behavior of non-phase-transforming ceramics , 1988 .

[21]  L. M. Braun,et al.  Technique for the R‐Curve Determination of Y‐TZP Using Indentation‐Produced Flaws , 1990 .

[22]  Robert F. Cook,et al.  The effect of lateral crack growth on the strength of contact flaws in brittle materials , 1986 .

[23]  David R. Clarke,et al.  Fracture stability, R-curves and strength variability , 1988 .

[24]  E. Fuller,et al.  Fracture Resistance Behavior of Silicon Carbide Whisker‐Reinforced Alumina Composites with Different Porosities , 1990 .

[25]  D. Marshall.  Strength Characteristics of Transformation‐Toughened Zirconia , 1986 .

[26]  A. Rosenfield,et al.  Analysis of Indentation Crack as a Wedge‐Loaded Half‐Penny Crack , 1985 .