The controlling biodegradation of chitosan fibers by N-acetylation in vitro and in vivo

AimIn the present study, we investigated the biodegradation of the fibers of chitosan and its acetylated derivatives in vitro and in vivo.MethodsA series of chitosan fibers, with acetylation degrees of 7.7%, 21.6%, 40.9%, 61.2%, 82.5% and 93.4%, were obtained by acetylating chitosan filament with acetic anhydride, and were investigated by FT-IR analysis, elemental analysis and scanning electron microscopy analysis.ResultsThe in vitro experimental data indicated that the degradation rate of chitosan fiber was strongly dependent on the degree of acetylation, and the degradation rate increased with an enhancement of the acetylation degree of chitosan fibers. In vivo degradation experiment evaluated by light microscopy as well as scanning electron microscopy, was studied by implanting the fibers between the two nerve stumps of the rat sciatic nerve gap (6 months). The findings demonstrated that acetylation degree could influence the degradation rate of chitosan fibers in vivo.ConclusionThese results suggested that acetylated chitosan (chitin) fibers were more biodegradable than chitosan and the biodegradation rate of chitin fiber can be controlled to desirable extent by the variation of acetylation degree.

[1]  M. Shoichet,et al.  Controlling cell adhesion and degradation of chitosan films by N-acetylation. , 2005, Biomaterials.

[2]  D. Britto,et al.  A kinetic study on the thermal degradation of N,N,N-trimethylchitosan , 2004 .

[3]  Zhishen Jia,et al.  Effect of reaction temperature and reaction time on the preparation of low-molecular-weight chitosan using phosphoric acid , 2002 .

[4]  I. Yannas,et al.  Synthesis of Tissues and Organs , 2004, Chembiochem : a European journal of chemical biology.

[5]  Xiaodong Wang,et al.  Fabrication and properties of a porous chitin/chitosan conduit for nerve regeneration , 2004, Biotechnology Letters.

[6]  Y Ikada,et al.  In vitro and in vivo degradation of films of chitin and its deacetylated derivatives. , 1997, Biomaterials.

[7]  S. Hudson,et al.  Improved mechanical properties of chitosan fibers , 1999 .

[8]  Soo-young Park,et al.  Fiber formation and physical properties of chitosan fiber crosslinked by epichlorohydrin in a wet spinning system: The effect of the concentration of the crosslinking agent epichlorohydrin , 2004 .

[9]  K. Creber,et al.  Improvements in the drying process for wet‐spun chitosan fibers , 1998 .

[10]  J. Santerre,et al.  Macrophage phagocytosis of polyethylene particulate in vitro. , 1998, Journal of biomedical materials research.

[11]  Joachim Kohn,et al.  New approaches to biomaterials design , 2004, Nature materials.

[12]  Wang Xuejiang,et al.  Preparation and in vitro investigation of chitosan/nano-hydroxyapatite composite used as bone substitute materials , 2005, Journal of materials science. Materials in medicine.

[13]  Y. Machida,et al.  Biodegradation and distribution of water-soluble chitosan in mice. , 1999, Biomaterials.

[14]  G. C. East,et al.  Wet spinning of chitosan and the acetylation of chitosan fibers , 1993 .

[15]  A. Salgado,et al.  Multichannel mould processing of 3D structures from microporous coralline hydroxyapatite granules and chitosan support materials for guided tissue regeneration/engineering , 2004, Journal of materials science. Materials in medicine.

[16]  Xiaosong Gu,et al.  The interaction of Schwann cells with chitosan membranes and fibers in vitro. , 2004, Biomaterials.

[17]  R. Tan,et al.  Immobilization of glucose oxidase on chitosan–SiO2 gel , 2004 .