Reduction of highly concentrated nitrate using nanoscale zero-valent iron: Effects of aggregation and catalyst on reactivity

Abstract Nanoscale zero-valent iron (NZVI) has been studied as an effective nitrate reduction material. Here, the effect of NZVI aggregation on the reduction reaction order and rate was investigated by comparing the nitrate reduction performances of freshly synthesized NZVI (F-NZVI), dried NZVI (D-NZVI), and dried-sonicated NZVI (DS-NZVI). Also, the effects of a catalyst were evaluated by coating 0.2 wt% Ni on previous series of NZVIs: F-Ni-NZVI, D-Ni-NZVI, and DS-Ni-NZVI. Different types of NZVIs could effectively reduce highly concentrated nitrate without requiring pH control. F-NZVI and F-Ni-NZVI showed extremely fast reactions, reducing 10–10,000 ppm within 1 min, and thus their reaction kinetics could not be evaluated under these experimental conditions. In the case of 10,000 ppm of nitrate, NZVI was almost completely consumed after reducing about 5000 ppm within 1 min. In contrast, nitrate reduction using D-NZVI and D-Ni-NZVI were pseudo-first-order reactions and DS-NZVI and DS-Ni-NZVI were 1.37 and 1.71 order reactions, respectively. D-Ni-NZVI and DS-Ni-NZVI obtained a higher reduction rate than D-NZVI and DS-NZVI due to the existence of the Ni catalyst. These experimental results suggest that the aggregate size and catalyst prominently affect the nitrate reduction rate and that the aggregation effect is more important than the catalyst effect as the aggregate size becomes smaller. Furthermore, the importance of the NZVI structure, the branch of chain-like structures and its edges exposed to the aqueous phase in nanoscale, is proposed in this study in order to explain the ultra fast reaction of F-NZVI and F-Ni-NZVI, which have yet to be reported. The final product of the reaction was ammonium, with nitrite being produced as a byproduct; NZVI changed into different shapes of magnetite (Fe 3 O 4 ) after the reaction, depending on the reaction conditions.

[1]  Hsing-Lung Lien,et al.  Nanoscale iron particles for complete reduction of chlorinated ethenes , 2001 .

[2]  R. Misra,et al.  Core-shell magnetite nanoparticles surface encapsulated with smart stimuli-responsive polymer: synthesis, characterization, and LCST of viable drug-targeting delivery system. , 2007, Langmuir : the ACS journal of surfaces and colloids.

[3]  Dongye Zhao,et al.  Rapid and controlled transformation of nitrate in water and brine by stabilized iron nanoparticles , 2009 .

[4]  Jung-Woo Kim,et al.  Aqueous ethanol modified nanoscale zerovalent iron in bromate reduction: synthesis, characterization, and reactivity. , 2009, Environmental science & technology.

[5]  Gordon C. C. Yang,et al.  Chemical reduction of nitrate by nanosized iron: kinetics and pathways. , 2005, Water research.

[6]  D. Damiani,et al.  On the role of Pd β-hydride in the reduction of nitrate over Pd based catalyst , 2008 .

[7]  J. Sueiras,et al.  Catalytic reduction of nitrate on Pt-Cu and Pd-Cu on active carbon using continuous reactor: The effect of copper nanoparticles , 2006 .

[8]  Wei-xian Zhang,et al.  Synthesizing Nanoscale Iron Particles for Rapid and Complete Dechlorination of TCE and PCBs , 1997 .

[9]  H. Schmid,et al.  Liquid–liquid phase transfer of magnetite nanoparticles , 2009 .

[10]  K. Paknikar,et al.  Effect of surface chemistry of Fe-Ni nanoparticles on mechanistic pathways of azo dye degradation. , 2007, Environmental science & technology.

[11]  J. Khim,et al.  Kinetics of reductive denitrification by nanoscale zero-valent iron. , 2000, Chemosphere.

[12]  Hsing-Lung Lien,et al.  Treatment of chlorinated organic contaminants with nanoscale bimetallic particles , 1998 .

[13]  Thomas E. Mallouk,et al.  Delivery Vehicles for Zerovalent Metal Nanoparticles in Soil and Groundwater , 2004 .

[14]  Thomas E. Mallouk,et al.  Hydrodechlorination of Trichloroethylene to Hydrocarbons Using Bimetallic Nickel-Iron Nanoparticles , 2002 .

[15]  L. Liotta,et al.  Catalytic reduction of nitrates and nitrites in water solution on pumice-supported Pd–Cu catalysts , 2000 .

[16]  Paul G Tratnyek,et al.  Evidence for localization of reaction upon reduction of carbon tetrachloride by Granular iron , 2002 .

[17]  Wei-xian Zhang,et al.  Nanoscale Iron Particles for Environmental Remediation: An Overview , 2003 .

[18]  Dongye Zhao,et al.  Rapid and complete destruction of perchlorate in water and ion-exchange brine using stabilized zero-valent iron nanoparticles. , 2007, Water research.

[19]  Bruno Dufour,et al.  Adsorbed triblock copolymers deliver reactive iron nanoparticles to the oil/water interface. , 2005, Nano letters.

[20]  D. Sholl,et al.  TCE dechlorination rates, pathways, and efficiency of nanoscale iron particles with different properties. , 2005, Environmental science & technology.

[21]  B. Gilbert,et al.  The effects of nanoparticle aggregation processes on aggregate structure and metal uptake. , 2009, Journal of colloid and interface science.

[22]  H. Lien,et al.  Nanoscale Pd/Fe bimetallic particles: Catalytic effects of palladium on hydrodechlorination , 2007 .

[23]  M. Aroua,et al.  Bio-electrochemical removal of nitrate from water and wastewater--a review. , 2008, Bioresource technology.

[24]  A. L. Roberts,et al.  Pathways and Kinetics of Chlorinated Ethylene and Chlorinated Acetylene Reaction with Fe(0) Particles , 1999 .

[25]  Dongye Zhao,et al.  Preparation and characterization of a new class of starch-stabilized bimetallic nanoparticles for degradation of chlorinated hydrocarbons in water. , 2005, Environmental science & technology.

[26]  Dongye Zhao,et al.  Hydrodechlorination of trichloroethene using stabilized Fe-Pd nanoparticles: Reaction mechanism and effects of stabilizers, catalysts and reaction conditions , 2008 .

[27]  T. Mallouk,et al.  Remediation of Cr(VI) and Pb(II) aqueous solutions using supported, nanoscale zero-valent iron , 2000 .

[28]  Zhuoyong Zhang,et al.  Rapid and complete dechlorination of PCP in aqueous solution using Ni-Fe nanoparticles under assistance of ultrasound. , 2006, Chemosphere.

[29]  K. Kandori,et al.  Influences of Co2+, Cu2+ and Cr3+ ions on the formation of magnetite , 1999 .

[30]  Xiao-qin Li,et al.  Stoichiometry of Cr(VI) Immobilization Using Nanoscale Zerovalent Iron (nZVI): A Study with High-Resolution X-Ray Photoelectron Spectroscopy (HR-XPS) , 2008 .

[31]  M. Guascito,et al.  Voltammetric and XPS investigations of nickel hydroxide electrochemically dispersed on gold surface electrodes , 1999 .

[32]  Linfeng Wu,et al.  Removal of trichloroethylene from water by cellulose acetate supported bimetallic Ni/Fe nanoparticles. , 2006, Chemosphere.

[33]  K. Kandori,et al.  Effects of metal ions on the morphology and structure of haematite particles produced from forced hydrolysis reaction , 1998 .

[34]  J. Órfão,et al.  Bimetallic catalysts supported on activated carbon for the nitrate reduction in water: Optimization of catalysts composition , 2009 .

[35]  Paul G Tratnyek,et al.  Characterization and properties of metallic iron nanoparticles: spectroscopy, electrochemistry, and kinetics. , 2005, Environmental science & technology.

[36]  Hong Wang,et al.  Characterization of zero-valent iron nanoparticles. , 2006, Advances in colloid and interface science.

[37]  Tie-long Li,et al.  Preparation of spherical iron nanoclusters in ethanol-water solution for nitrate removal. , 2006, Chemosphere.

[38]  E. Grulke,et al.  Role of Ni/Fe Nanoparticle Composition on the Degradation of Trichloroethylene from Water , 2005 .

[39]  Myung-Heui Woo,et al.  Fe(0) nanoparticles for nitrate reduction: stability, reactivity, and transformation. , 2006, Environmental science & technology.

[40]  Woojin Lee,et al.  Inhibition of nZVI reactivity by magnetite during the reductive degradation of 1,1,1-TCA in nZVI/magnetite suspension , 2010 .

[41]  K. Paknikar,et al.  Iron-nickel bimetallic nanoparticles for reductive degradation of azo dye Orange G in aqueous solution , 2008 .

[42]  Heechul Choi,et al.  Arsenic(V) removal from groundwater using nano scale zero-valent iron as a colloidal reactive barrier material. , 2006, Environmental science & technology.

[43]  Yu Zhang,et al.  SYNTHESIS OF NANOMETER-SIZE MAGHEMITE PARTICLES FROM MAGNETITE , 2004 .

[44]  Xiao-qin Li,et al.  Sequestration of Metal Cations with Zerovalent Iron NanoparticlesA Study with High Resolution X-ray Photoelectron Spectroscopy (HR-XPS) , 2007 .

[45]  A. L. Roberts,et al.  Reaction of 1,1,1-Trichloroethane with Zero-Valent Metals and Bimetallic Reductants , 1998 .

[46]  Xiao-qin Li,et al.  Iron nanoparticles: the core-shell structure and unique properties for Ni(II) sequestration. , 2006, Langmuir : the ACS journal of surfaces and colloids.

[47]  F. Kopinke,et al.  Hydrodehalogenation of halogenated hydrocarbons in water with Pd catalysts: Reaction rates and surface competition , 2006 .

[48]  E. Carraway,et al.  Catalytic hydrodechlorination of chlorinated ethenes by nanoscale zero-valent iron , 2008 .

[49]  Navid B. Saleh,et al.  Stabilization of aqueous nanoscale zerovalent iron dispersions by anionic polyelectrolytes: adsorbed anionic polyelectrolyte layer properties and their effect on aggregation and sedimentation , 2008 .

[50]  Heechul Choi,et al.  Removal of arsenic(III) from groundwater by nanoscale zero-valent iron. , 2005, Environmental science & technology.

[51]  Biao Yan,et al.  Preparation and magnetic properties of magnetite nanoparticles by sol-gel method , 2010, 2010 3rd International Nanoelectronics Conference (INEC).

[52]  T. Lim,et al.  Pathways and kinetics of carbon tetrachloride and chloroform reductions by nano-scale Fe and Fe/Ni particles: comparison with commercial micro-scale Fe and Zn. , 2005, Chemosphere.

[53]  E. Carraway,et al.  Reduction of chlorinated ethanes by nanosized zero-valent iron: kinetics, pathways, and effects of reaction conditions. , 2005, Environmental science & technology.

[54]  S. Lo,et al.  Dechlorination of trichloroethylene in aqueous solution by noble metal-modified iron. , 2004, Journal of hazardous materials.