Comparison of martensite transformation temperatures in a NiMnGa alloy determined with hot/cold stage optical microscopy and differential scanning calorimetry

The martensite transformation temperatures of both as-grown and heat-treated specimens removed from a Bridgman grown boule of off-stoichiometric Ni2MnGa were determined by differential scanning calorimetry (DSC) and hot/cold stage microscopy. The work showed that martensite start and austenite finish transformation temperatures determined by the hot/cold stage microscope technique were in agreement with those determined by the DSC method. The hot/cold stage microscope technique was shown to be useful for characterizing variations of transformation temperature across a specimen. The results revealed that residual stress, deformation and boule composition variations produce artefacts in DSC traces which need to be identified, understood and controlled. Transmission electron microscope results suggest that the possible contribution of a premartensitic transformation to the high temperature edge of the martensite peak on DSC scans needs further investigation.