Analysis of catalyst particle strength by impact testing: The effect of manufacturing process parameters on the particle strength

Abstract The mechanical strength of porous alumina catalyst carrier beads, used in the reforming units with continuous catalytic regeneration, was measured by impact testing. With this testing method particle strength can be measured at higher strain rates than the traditional crushing test method, hence providing a better simulation of pneumatic conveying and chute flow conditions, and also a large number of particles can be tested quickly. This is important for particles with a brittle failure mode such as the alumina particles used in this work as a wide distribution of mechanical strength usually prevails. Extensive impact testing was carried out first with an industrial sample, in order to understand the failure mechanism of this type of particle s and to develop a methodology for analysing the extent of breakage by impact. Then the method was used to analyse the effect of a number of process parameters, such as filler, macroporosity and drying procedure on the particle strength with the aim of optimising the manufacturing process. The impact test results were then used to test the model of breakage behaviour of particulate solids proposed by Vogel and Peukert [Vogel and Peukert, Breakage behaviour of different materials—construction of a mastercurve for the breakage probability. Powder Technol., 129 (2003) pp. 101–110].

[1]  J. Geus,et al.  The sol—gel preparation of porous catalyst spheres , 1991 .

[2]  Dean‐Mo Liu.  Influence of porosity and pore size on the compressive strength of porous hydroxyapatite ceramic , 1997 .

[3]  Mojtaba Ghadiri,et al.  Impact attrition of particulate solids. Part 1: A theoretical model of chipping , 2002 .

[4]  Michael J. Hounslow,et al.  Particle fragmentation in dilute phase pneumatic conveying , 2002 .

[5]  P. Laval,et al.  Methodology for Investigating the Mechanical Strength of Reforming Catalyst Beads , 2000 .

[6]  Jinsheng Fu,et al.  An experimental investigation of particle fragmentation using single particle impact studies , 2002 .

[7]  Agba D. Salman,et al.  A study of solid particle failure under normal and oblique impact , 1995 .

[8]  C. Couroyer.  Attrition of alumina catalyst carrier beads. , 2000 .

[9]  N. Chouteau,et al.  Fragmentation by high velocity impact on a target: a material grindability test , 2003 .

[10]  Jean-Francois Large,et al.  High velocity impact of particles on a target — an experimental study , 1996 .

[11]  F. P. Knudsen.  Dependence of Mechanical Strength of Brittle Polycrystalline Specimens on Porosity and Grain Size , 1959 .

[12]  M. Ghadiri,et al.  Effect of structural characteristics on impact breakage of agglomerates , 2003 .

[13]  Mojtaba Ghadiri,et al.  Impact attrition of particulate solids. Part 2: Experimental work , 2002 .

[14]  M. Ghadiri,et al.  Breakage patterns of agglomerates , 2001 .

[15]  Mojtaba Ghadiri,et al.  Impact attrition of sodium chloride crystals , 1987 .

[16]  Mojtaba Ghadiri,et al.  Impact attrition of sodium carbonate monohydrate crystals , 1993 .

[17]  Brian Scarlett,et al.  Breakage behaviour of enzyme granules in a repeated impact test , 2003 .

[18]  Wolfgang Peukert,et al.  Breakage behaviour of different materials—construction of a mastercurve for the breakage probability , 2003 .

[19]  W. Weibull.  A Statistical Distribution Function of Wide Applicability , 1951 .

[20]  Mojtaba Ghadiri,et al.  Weibull Analysis of Quasi-Static Crushing Strength of Catalyst Particles , 2003 .

[21]  M. Ghadiri,et al.  Impact breakage of poly-methylmethacrylate (PMMA) extrudates: I. Chipping mechanism , 1996 .