Effects of compatibilizer type and rubber‐wood sawdust content on the mechanical, morphological, and thermal properties of PVC/LDPE blend

This article aimed to investigate the mechanical, morphological and thermal properties of PVC/LDPE blend with and without the addition of compatibilizers. The effects of LDPE content, compatibilizer type and rubber-wood sawdust loading on the properties of the blend were evaluated. The experimental results suggested that as the LDPE content was increased the mechanical properties of PVC-LDPE blend progressively decreased due to poor interfacial adhesion. The continuity and compatibility between PVC and LDPE phases could be improved through three different types of compatibilizers which included chlorinated polyethylene (CPE) poly(methyl-methacrylate-co-butyl acrylate) (PA20) and poly(ethylene-co-methacrylate) (Elvaloy). The PA20 was found to be the most suitable compatibilizer for the blend. A radical transfer reaction was proposed in this work to explain the structure and thermal changes of the PVC in PVC-LDPE blend. The decomposition temperature of PVC in the blend decreased with the loading of the PA20 and the wood sawdust. As the sawdust content was increased the tensile and flexural moduli increased with considerable decreased in the tensile, flexural and impact strength, a slight improvement being achieved if the PA20 was incorporated in the composite. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 598–606, 2006

[1]  N. Sombatsompop,et al.  Influence of Type and Concentration of Maleic Anhydride Grafted Polypropylene and Impact Modifiers on Mechanical Properties of PP/Wood Sawdust Composites , 2005 .

[2]  N. Sombatsompop,et al.  Average mixing torque, tensile and impact properties, and thermal stability of poly(vinyl chloride)/sawdust composites with different silane coupling agents , 2005 .

[3]  J. Martinez-vega,et al.  Effects of hydrothermal ageing on the thermal behaviour of poly(vinyl chloride) filled with wood flour , 2004 .

[4]  N. Sombatsompop,et al.  Effect of moisture content on mechanical properties, thermal and structural stability and extrudate texture of poly(vinyl chloride)/wood sawdust composites , 2004 .

[5]  P. Fabbri,et al.  Modification of cellulose fibres with organosilanes: Under what conditions does coupling occur? , 2004, Journal of colloid and interface science.

[6]  N. Sombatsompop,et al.  Effects of acrylic-based processing aids on processibility, rheology, thermal and structural stability, and mechanical properties of PVC/wood-sawdust composites , 2004 .

[7]  N. Sombatsompop,et al.  Structural changes of PVC in PVC/LDPE melt-blends: Effects of LDPE content and number of extrusions , 2004 .

[8]  A. Duarte,et al.  Modification of cellulosic fibres with functionalised silanes: development of surface properties , 2004 .

[9]  L. Matuana,et al.  Ultraviolet weathering of photostabilized wood-flour-filled high-density polyethylene composites†‡ , 2003 .

[10]  S. Thongsang,et al.  Effect of wood sawdust content on rheological and structural changes, and thermo‐mechanical properties of PVC/sawdust composites , 2003 .

[11]  A. McDonald,et al.  The effect of silane coupling agents on radiata pine fibre for use in thermoplastic matrix composites , 2003 .

[12]  T. Hirotsu,et al.  Crystallization and melting behaviors of maleated polyethylene and its composite with fibrous cellulose , 2003 .

[13]  Ana Espert,et al.  Thermal and thermomechanical properties of biocomposites made from modified recycled cellulose and recycled polypropylene , 2003 .

[14]  Yiu-Wing Mai,et al.  An investigation on the processing of sisal fibre reinforced polypropylene composites , 2003 .

[15]  J. Kenny,et al.  Mechanical characterization of polypropylene–wood flour composites , 2003 .

[16]  Zhengping Fang,et al.  Phase dispersion–crosslinking synergism in binary blends of poly(vinyl chloride) with low‐density polyethylene: Entrapping phenomenon in PVC/LDPE/DCP blend , 2003 .

[17]  X. Colom,et al.  Effects of different treatments on the interface of HDPE/lignocellulosic fiber composites , 2003 .

[18]  Y. Wang,et al.  Comparative study of maleated polyolefins as compatibilizers for polyethylene/wood flour composites , 2003 .

[19]  J. Martinez-vega,et al.  Effect of Wood Flour Content on the Thermal, Mechanical and Dielectric Properties of Poly(vinyl chloride) , 2002 .

[20]  Jun Zhang,et al.  Photoaging and stabilization of rigid PVC/wood-fiber composites , 2001 .

[21]  F. Mengeloglu,et al.  Effects of impact modifiers on the properties of rigid PVC/wood‐fiber composites , 2000 .

[22]  A. Błędzki,et al.  Composites reinforced with cellulose based fibres , 1999 .

[23]  Zhengping Fang,et al.  Study on phase dispersion-crosslinking synergism in binary blends of poly(vinyl chloride) with low density polyethylene , 1997 .

[24]  R. Joseph,et al.  Chemical Modification of Blends of Poly (Vinyl Chloride) With Linear Low Density Polyethylene , 1992 .

[25]  G. Scott,et al.  Polymer blends—IV , 1984 .

[26]  A. Ghaffar,et al.  Polymer blends—II. The use of solid phase dispersants to improve the properties of binary mixtures of incompatible polymers , 1981 .