Mechanical Property Characterization of Fiber-Reinforced Polymer Wood-Polypropylene Composite Panels Manufactured Using a Double Belt Pressing Technology

AbstractA novel manufacturing process for wood-polypropylene composite (WPC) panels reinforced with fiber-reinforced polymer (FRP) sheets was implemented using a double belt pressing technology. FRP sheets were placed on both sides of the WPC agglomerates during fabrication, which resulted in increased productivity and reduced thermal stresses compared with secondary bonding processes. Significant improvements in the mechanical properties of the FRP reinforced sheet panels were found during flexural and tensile tests on the coupon level. Even with addition of only one layer of FRP reinforcement on both sides of a WPC panel, the flexural modulus and strength increased by a factor of 2.6 and 3.8, respectively. Furthermore, the flexural and tensile properties of the WPC material considered in this study were found to be superior compared with the properties of an extruded WPC material. The changes in the flexural modulus of the FRP reinforced WPC panels with respect to the number of FRP layers were predicted...

[1]  R. Lopez-Anido,et al.  Water absorption of wood polypropylene composite sheet piles and its influence on mechanical properties , 2011 .

[2]  D. Gardner,et al.  Time and temperature dependent response of a wood–polypropylene composite , 2011 .

[3]  M. Naghipour,et al.  Analytical and experimental study on flexural performance of WPC–FRP beams , 2011 .

[4]  H. Dagher,et al.  Structural Performance of Wood Plastic Composite Sheet Piling , 2010 .

[5]  Youhong Tang,et al.  Increasing load-bearing capacity of wood-plastic composites by sandwiching natural and glass fabrics , 2010 .

[6]  A. Behravesh,et al.  Experimental Investigation of Injection Molding of Wood/Plastics Composites , 2010 .

[7]  Craig M. Clemons.  Raw materials for wood-polymer composites. , 2008 .

[8]  A. Klyosov,et al.  Wood-Plastic Composites , 2007 .

[9]  M. Wolcott,et al.  Flexural properties of surface reinforced wood/plastic deck board , 2007 .

[10]  M. Sain,et al.  Injection Molded Wheat Straw and Corn Stem Filled Polypropylene Composites , 2006 .

[11]  N. Stark.  Effect of weathering cycle and manufacturing method on performance of wood flour and high-density polyethylene composites†‡ , 2006 .

[12]  C. Grande,et al.  Investigation of Fiber Organization and Damage During Single Screw Extrusion of Natural Fiber Reinforced Thermoplastics , 2005 .

[13]  Qinglin Wu,et al.  Wood‐fiber/high‐density‐polyethylene composites: Coupling agent performance , 2005 .

[14]  M. J. Durá.  Behavior of Hybrid Wood Plastic Composite-Fiber Reinforced Polymer Structural Members for Use in Sustained Loading Applications , 2005 .

[15]  Kenneth J. Fridley,et al.  DEVELOPMENT OF DESIGN VALUES FOR WOOD-PLASTIC COMPOSITE MATERIALS , 2003 .

[16]  Y. Mai,et al.  Thermal de-consolidation of thermoplastic matrix composites—I. Growth of voids , 2002 .

[17]  B. Kokta,et al.  The Influence of Coupling Agents On Mechanical Properties of Composites Containing Cellulosic Fillers , 1990 .

[18]  K. Yam,et al.  Composites from compounding wood fibers with recycled high density polyethylene , 1990 .