Relationships between composition, structure and strength of inorganic polymers

Abstract“Inorganic polymers”, or geopolymers, are novel synthetic binders produced by reactions between alkali silicate solutions and solid aluminosilicates. In Part 1 of this study, 12 metakaolin-derived inorganic polymers were produced with various compositions. The effect of the concentration of each of the four most important oxide components of inorganic polymers (Na2O, SiO2, Al2O3 and H2O) was assessed by electron microscopy and by strength testing. Additionally, the effect of the type of alkali cation was determined. In general, the results followed expected trends and there were clear correlations between composition, microstructure and strength. It was found that high strength was related to low porosity and a dense, fine grained microstructure. Such a structure was found in inorganic polymers with high alkali contents (Na2O/Al2O3 = 1.2) and low water contents (H2O/Al2O3 = 12). High silica and low alumina contents (SiO2/Al2O3 = 3.5–3.8) also produced this structure, however, there was a limit beyond which the strength deteriorated. In relation to the effect of alkali cations, sodium was found to give higher resin strength than potassium. The results of the study further confirm that the selection of precursor raw materials remains a critical factor to initial strength development. The relationship between different resin formulations and resulting microstructures are discussed.

[1]  H. Rahier,et al.  Low-temperature synthesized aluminosilicate glasses: Part III Influence of the composition of the silicate solution on production, structure and properties , 1997 .

[2]  Ángel Palomo,et al.  Alkali-activated fly ashes: A cement for the future , 1999 .

[3]  J.S.J. van Deventer,et al.  The potential use of geopolymeric materials to immobilise toxic metals: Part II. Material and leaching characteristics , 1999 .

[4]  J. Phair,et al.  Effect of silicate activator pH on the leaching and material characteristics of waste-based inorganic polymers , 2001 .

[5]  J. Phair,et al.  Mechanism of polysialation in the incorporation of zirconia into fly ash-based geopolymers , 2000 .

[6]  Wei Sun,et al.  IN SITU MONITORING OF THE HYDRATION PROCESS OF K-PS GEOPOLYMER CEMENT WITH ESEM , 2004 .

[7]  J.S.J. van Deventer,et al.  Effect of the Alkali Metal Activator on the Properties of Fly Ash-Based Geopolymers , 1999 .

[8]  J.S.J. van Deventer,et al.  The effect of metal contaminants on the formation and properties of waste-based geopolymers , 1999 .

[9]  Brian H. O'Connor,et al.  Chemical optimisation of the compressive strength of aluminosilicate geopolymers synthesised by sodium silicate activation of metakaolinite , 2003 .

[10]  K. Sagoe-Crentsil,et al.  Relationships between composition, structure and strength of inorganic polymers , 2005 .

[11]  K. MacKenzie,et al.  Synthesis and characterisation of materials based on inorganic polymers of alumina and silica: sodium polysialate polymers , 2000 .

[12]  J.S.J. van Deventer,et al.  Factors affecting the immobilization of metals in geopolymerized flyash , 1998 .