Effect of process control agent on the porous structure and mechanical properties of a biomedical Ti-Sn-Nb alloy produced by powder metallurgy.

The influence of different amounts and types of process control agent (PCA), i.e., stearic acid and ethylene bis-stearamide, on the porous structure and mechanical properties of a biomedical Ti-16Sn-4Nb (wt.%) alloy was investigated. Alloy synthesis was performed on elemental metal powders using high-energy ball milling for 5h. Results indicated that varying the PCA content during ball milling led to a drastic change in morphology and particle-size distribution of the ball-milled powders. Porous titanium alloy samples sintered from the powders ball milled with the addition of various amounts of PCA also revealed different pore morphology and porosity. The Vickers hardness of the sintered titanium alloy samples exhibited a considerable increase with increasing PCA content. Moreover, the addition of larger amounts of PCA in the powder mixture resulted in a significant increase in the elastic modulus and peak stress for the sintered porous titanium alloy samples under compression. It should also be mentioned that the addition of PCA introduced contamination (mainly carbon and oxygen) into the sintered porous product.

[1]  J. A. Rodríguez,et al.  Structure and properties of attrition-milled aluminium powder , 1997 .

[2]  F. A. Khalid,et al.  Decomposition of process control agent during mechanical milling and its influence on displacement reactions in the Al-TiO2 system , 2005 .

[3]  Joon B. Park.  Biomaterials:An Introduction , 1992 .

[4]  John J. Moore,et al.  Combustion synthesis of advanced materials: Part I. Reaction parameters , 1995 .

[5]  H. Kawahara.  Cytotoxicity of Implantable Metals and Alloys. , 1992 .

[6]  M. Ashby,et al.  Cellular solids: Structure & properties , 1988 .

[7]  M. Ashby,et al.  Metal Foams: A Design Guide , 2000 .

[8]  B Vamsi Krishna,et al.  Low stiffness porous Ti structures for load-bearing implants. , 2007, Acta biomaterialia.

[9]  L. Gibson.  The mechanical behaviour of cancellous bone. , 1985, Journal of biomechanics.

[10]  C. Suryanarayana,et al.  Mechanical alloying and milling , 2004 .

[11]  M. Sacks,et al.  Effect of Particle Size Distribution on the Sintering of Alumina , 1988 .

[12]  W. Nix,et al.  The structure and properties of aluminum alloys produced by mechanical alloying: Powder processing and resultant powder structures , 1981 .

[13]  Z. Lian,et al.  Influence of martensitic transformation on mechanical compatibility of biomedical β type titanium alloy TLM , 2006 .

[14]  R. Giordano,et al.  The effect of different powder particle size on mechanical properties of sintered alumina, resin- and glass-infused alumina. , 2009, Journal of biomedical materials research. Part B, Applied biomaterials.

[15]  C. Wen,et al.  Preparation and Characterisation of New Titanium Based Alloys for Orthopaedic and Dental Applications , 2006 .

[16]  Y. Lin,et al.  Effect of lubricant addition on the powder properties and compacting performance of spray-dried molybdenum powders , 2002 .

[17]  C. Koch,et al.  Nanostructured Materials: Processing, Properties and Applications , 2006 .

[18]  Jack E. Lemons,et al.  Medical Applications of Titanium and Its Alloys: The Material and Biological Issues , 1996 .

[19]  J. Groza.  Nanocrystalline Powder Consolidation Methods , 2007 .

[20]  Seong‐Hyeon Hong,et al.  Manufacturing of aluminum flake powder from foil scrap by dry ball milling process , 2000 .

[21]  H. Plenk.  Prosthesis-bone interface. , 1998, Journal of biomedical materials research.

[22]  R. M. L. Neto,et al.  An Investigation of the use of Stearic Acid as a Process Control Agent in High Energy Ball Milling of Nb-Al and Ni-Al Powder Mixtures , 2003 .

[23]  Yasuo Yamada,et al.  Synthesis of Ti-Sn-Nb alloy by powder metallurgy , 2008 .

[24]  Li Lu,et al.  Influence of process control agent on interdiffusion between Al and Mg during mechanical alloying , 1999 .

[25]  Randall M. German,et al.  Particle packing characteristics , 1989 .

[26]  M. Zawrah,et al.  Effects of process-control agents on mechanical alloying of nanostructured aluminum alloys , 2003 .

[27]  R. German.  Sintering theory and practice , 1996 .

[28]  F. Froes,et al.  Mechanical Alloying of Titanium‐Base Alloys , 1993 .

[29]  L. Ge,et al.  Synthesis and characterization of TiO2 photocatalytic thin films prepared from refluxed PTA sols , 2006 .

[30]  Jeffrey Wadsworth,et al.  Effect of cell morphology on the compressive properties of open-cell aluminum foams , 2000 .

[31]  Y. Okazaki,et al.  New Titanium Alloys to be Considered for Medical Implants , 1996 .

[32]  Gopal S. Upadhyaya,et al.  Powder Metallurgy Technology , 1997 .