Effect of p and n doping on neutral impurity and dielectric cap induced quantum well intermixing in GaAs/AlGaAs structures

We report the diffusion and quantum well intermixing (QWI) effects of the neutral impurities fluorine and boron in p- and n-type AlGaAs in the GaAs/AlGaAs system. Boron was found to show significant diffusion in p-doped AlGaAs material but only exhibited a very small amount of diffusion in n-doped material after furnace annealing. Boron was found to retard intermixing in p-AlGaAs. This may be due to the existence of interstitial B, which may reduce the native group III interstitial concentration. The mechanism of boron impurity-induced disordering (IID) in n-AlGaAs was proposed to be attributed to both the diffusion of point defects generated during ion implantation and the Fermi level effect from the deep acceptor . Extremely fast fluorine diffusion rates, which may be correlated to an interstitial diffusion mechanism, have been observed. Results from fluorine IID suggest the possibility of the ionization of fluorine which gives rise to a higher electron concentration during annealing, leading to higher degrees of intermixing in n-AlGaAs. The intermixing rate of impurity free vacancy disordering (IFVD) using an cap was found to be higher in n-type and intrinsic AlGaAs than in p-type AlGaAs, which suggests that the diffusion of the group III vacancy is inhibited in p-type material which has a higher group III interstitial concentration. These results imply that n-i-p structures should be more effective than conventional p-i-n structures for the IFVD process.

[1]  V. Deline,et al.  Incorporation of boron during the growth of GaAs single crystals , 1980 .

[2]  A. C. Bryce,et al.  Neutral Impurity Disordering of III-V Quantum well Structures for Optoelectronic Integration , 1991 .

[3]  L. Derick,et al.  Surface Protection and Selective Masking during Diffusion in Silicon , 1957 .

[4]  H. l'Haridon,et al.  Investigation of compensation in implanted n-GaAs , 1978 .

[5]  A. C. Bryce,et al.  Transmission electron microscopy study of fluorine and boron implanted and annealed GaAs/AlGaAs , 1994 .

[6]  John H. Marsh,et al.  GaAs/AlGaAs photonic integrated circuits fabricated using impurity-free vacancy disordering , 1995, Photonics West.

[7]  J. Marsh,et al.  Quantum-well laser with integrated passive waveguide fabricated by neutral impurity disordering , 1992, IEEE Photonics Technology Letters.

[8]  P. W. Yu,et al.  Infrared absorption and photoluminescence of defect levels in the 204- to 255-meV range in p-type GaAs , 1986 .

[9]  J. Woodhead,et al.  Boron impurity anti-site defects in p-type gallium-rich gallium arsenide , 1983 .

[10]  Brian T. Cunningham,et al.  Carbon diffusion in undoped, n‐type, and p‐type GaAs , 1989 .

[11]  T. J. Magee,et al.  Annealing of damage and redistribution of Cr in boron‐implanted Si3N4‐capped GaAs , 1980 .

[12]  F. Ren,et al.  Ultrahigh doping of GaAs by carbon during metalorganic molecular beam epitaxy , 1989 .

[13]  J. Cunningham,et al.  Molecular beam epitaxial growth of high‐purity AlGaAs , 1987 .

[14]  Dennis G. Deppe,et al.  Atom diffusion and impurity‐induced layer disordering in quantum well III‐V semiconductor heterostructures , 1988 .

[15]  J. S. Blakemore,et al.  Characterization of n‐type regions in GaAs formed by silicon fluoride molecular ion implantations , 1989 .

[16]  John H. Marsh,et al.  A comparison of carbon and zinc doping in GaAs/AlGaAs lasers bandgap-tuned by impurity-free vacancy disordering , 1994 .