Formation of intermediate phases, Ni3Si2 and Pt6SI5: nucleation, identification, and resistivity

The formation of Ni3Si2 from the reaction of Ni2Si with NiSi, and that of Pt6Si5 from the reaction of Pt2Si with PtSi have been investigated by Rutherford backscattering, x‐ray diffraction, resistance measurements, and optical and electronic microscopy. Standard x‐ray diffraction patterns were calculated for Pt6Si5 and for the high‐temperature form (hexagonal) of Pt2Si. These are shown to match experimental diffraction patterns. Both Ni3Si2 and Pt6Si5 form quite suddenly (at 470 and 535 °C, respectively) according to the pattern of nucleation‐controlled reactions which are anticipated when the free energies of formation of the new phases are sufficiently small. These observations are discussed with respect to the absence of both Ni3Si2 and Pt6Si5 from the sequence of phases which form when Ni and Pt thin films react with Si. Resistivity measurements are reported for Ni3Si2, Pt6Si5, and for the two forms (low and high temperature) of Pt2Si.

[1]  I. Engström.  Structural chemistry of platinum metal silicides , 1970 .

[2]  S. P. Murarka,et al.  Refractory silicides for integrated circuits , 1980 .

[3]  F. d'Heurle,et al.  The thin‐film formation of rhodium silicides , 1980 .

[4]  C. Wickersham,et al.  Temperature dependent formation of surface undulations in explosively crystallized films , 1985 .

[5]  Norman G. Einspruch,et al.  Vlsi Electronics: Microstructure Science , 1982 .

[6]  J. E. E. Baglin,et al.  Formation of thin films of NiSi: Metastable structure, diffusion mechanisms in intermetallic compounds , 1984 .

[7]  L. Hung,et al.  Silicide formation in lateral diffusion couples , 1983 .

[8]  J. Mahan,et al.  Electronic transport properties of tungsten silicide thin films , 1984 .

[9]  W. Chu,et al.  Structure and growth kinetics of Ni2Si on silicon , 1975 .

[10]  M.-A. Nicolet,et al.  Reaction of thin metal films with SiO2 substrates , 1978 .

[11]  G. V. Samsonov,et al.  Handbook of Refractory Compounds , 1980 .

[12]  J. Weeks,et al.  Surface Undulations in Explosive Crystallization : a Thermal Instability , 1983 .

[13]  H. Muta,et al.  Solid‐Solid Reactions in Pt–Si Systems , 1972 .

[14]  G. Ottaviani,et al.  Intermetallic compound formation in thin-film and in bulk samples of the Ni-Si binary system , 1983 .

[15]  R. S. Claassen.  Instrumentation for Materials Research. , 1976 .

[16]  W. B. Pearson,et al.  The crystal chemistry and physics of metals and alloys , 1972 .

[17]  M. Nicolet,et al.  Implanted oxygen in NiSi formation , 1981 .

[18]  G. Majni,et al.  Growth kinetics of NiSi on (100) and (111) silicon , 1984 .

[19]  C. Wickersham,et al.  Impulse stimulated ``explosive'' crystallization of sputter deposited amorphous (In,Ga)Sb films , 1978 .

[20]  G. Majni,et al.  The growth processes of thin film silicides in Si/Ni planar systems , 1985 .

[21]  M. Hansen,et al.  Constitution of Binary Alloys , 1958 .

[22]  Tung-Sheng Kuan,et al.  Formation of iridium silicides from Ir thin films on Si substrates , 1979 .