Adhesion and abrasive wear resistance of TiN deposited on electrical discharge machined WC–Co cemented carbides

Electrical discharge machining (EDM) is a non-traditional machining method extensively used to manufacture complex geometries of hard and brittle materials such as WC-Co cemented carbides (CC). Although the thermal action of the EDM process is known to yield a relatively poor surface integrity in these materials, it may be minimized through the implementation of multi-step sequential EDM and post-EDM surface treatments. Particularly, hard coating application has been demonstrated to be effective for decreasing the EDM-induced mechanical degradation. However, additional studies are required on such coating-EDMed substrate systems to determine other crucial properties in terms of applications, e.g. adhesion and micro-scale wear behaviour. In this work the adhesion strength and the microabrasive wear resistance of TiN deposited on EDMed substrates have been evaluated by means of scratch and crater grinder testing, respectively. The results indicate that both critical load for decohesion of the coating from the substrate and coating specific wear rate increase with finer-executed EDM, reaching values close to those measured for a TiN coating deposited on a ground and polished substrate.

[1]  J. Esteve,et al.  Mechanical strength improvement of electrical discharge machined cemented carbides through PVD (TiN, TiAlN) coatings , 2004 .

[2]  A. Gadalla,et al.  Electrical Discharge Machining of Tungsten Carbide‐Cobalt Composites , 1989 .

[3]  I. Hutchings,et al.  Methods of data analysis for the micro-scale abrasion test on coated substrates , 2003 .

[4]  Ian M. Hutchings,et al.  Progress towards standardisation of ball cratering , 2003 .

[5]  A. Matthews,et al.  Micro-scale abrasive wear testing of duplex and non-duplex (single-layered) PVD (Ti,Al)N, TiN and Cr–N coatings , 2002 .

[6]  I. Hutchings,et al.  A micro-abrasive wear test, with particular application to coated systems , 1996 .

[7]  I. Hutchings,et al.  Sources of variability in the free-ball micro-scale abrasion test , 2005 .

[8]  I. Hutchings,et al.  Laboratory characterisation of the wear behaviour of PVD-coated tool steels and correlation with cutting tool performance , 1996 .

[9]  Jun Qu,et al.  Nanoindentation characterization of surface layers of electrical discharge machined WC/Co , 2003 .

[10]  Jun Qu,et al.  Development of the Cylindrical Wire Electrical Discharge Machining Process, Part 1: Concept, Design, and Material Removal Rate , 2002 .

[11]  A. Gadalla,et al.  MACHINING OF WC-Co COMPOSITES , 1989 .

[12]  K. Schiffmann,et al.  Analysis of perforating and non-perforating micro-scale abrasion tests on coated substrates , 2005 .

[13]  Micro-Scale Abrasive Wear Test of Thin Coated Cylindrical Surfaces , 2004 .

[14]  I. Hutchings,et al.  Theory and application of a micro-scale abrasive wear test , 1997 .

[15]  Jun Qu,et al.  Development of the Cylindrical Wire Electrical Discharge Machining Process, Part 2: Surface Integrity and Roundness , 2002 .

[16]  H. Evans,et al.  Mechanical failure of thin brittle coatings , 1995 .

[17]  Staffan Jacobson,et al.  A new test method for the intrinsic abrasion resistance of thin coatings , 1991 .

[18]  S. M. Pandit,et al.  Analysis of Electro Discharge Machining of Cemented Carbides , 1981 .

[19]  L. Casteletti,et al.  Micro-abrasive wear test of niobium carbide layers produced on AISI H13 and M2 steels , 2006 .

[20]  M. Larsson,et al.  The crater grinder method as a means for coating wear evaluation — an update , 1997 .

[21]  J. Richter.  Micro-scale abrasion testing of PVD TiN coatings on conventional and nonledeburitic high-speed steels , 2004 .

[22]  A. Evans,et al.  On the mechanical behavior of brittle coatings and layers , 1983 .

[23]  S. Hogmark,et al.  Influence of residual stresses on fracture and delamination of thin hard coatings , 1999 .

[24]  J. Esteve,et al.  Influence of electrical discharge machining on the sliding contact response of cemented carbides , 2001 .

[25]  Ian M. Hutchings,et al.  Results from an interlaboratory exercise to validate the micro-scale abrasion test , 2005 .

[26]  M. C. Joseph,et al.  Micro-abrasion wear testing of PVD TiN coatings on untreated and plasma nitrided AISI H13 steel , 2001 .

[27]  Sture Hogmark,et al.  Design and evaluation of tribological coatings , 2000 .

[28]  E. Martínez,et al.  Diamond coatings on electrical-discharge machined hardmetals , 2003 .

[29]  C. J. Heuvelman,et al.  Summary report on the CIRP cooperative research on spark-erosion machining of cemented carbides (die-sinking) , 1980 .

[30]  M. Anglada,et al.  Surface integrity effects on the fracture resistance of electrical-discharge-machined WC-Co cemented carbides , 2004 .

[31]  S. Hogmark,et al.  Mechanical and tribological characterization of low-temperature deposited PVD TiN coatings , 1994 .

[32]  I. Hutchings,et al.  Transitions between two-body and three-body abrasive wear: influence of test conditions in the microscale abrasive wear test , 1999 .