Influence of substrate bias, deposition temperature and post-deposition annealing on the structure and properties of multi-principal-component (AlCrMoSiTi)N coatings

Abstract Nitride films are deposited from a single equiatomic AlCrMoSiTi target by reactive DC magnetron sputtering. The influence of the substrate bias and deposition temperature on the coating structure and properties are investigated. The bias is varied from 0 to − 200 V while maintaining a substrate temperature of 573 K. And the temperature is changed from 300 to 773 K whilst maintaining a substrate bias of − 100 V. From X-ray diffraction analysis, it is found that all the as-deposited coatings are of a single phase with NaCl-type FCC structure. This is attributed to the high mixing entropy of AlN, CrN, MoN, SiN, and TiN, and the limited diffusion kinetics during coating growth. Specific aspects of the coating, namely the grain size, lattice constant and compressive stress, are seen to be influenced more by substrate bias than deposition temperature. In fact, it is possible to classify the deposited films as large grained (~ 15 nm) with a reduced lattice constant (~ 4.15 A) and low compressive residual stresses for lower applied substrate biases, and as small grained (~ 4 nm) with an increased lattice constant (~ 4.25 A) and high compressive residual stresses for applied biases of − 100 V or more. A good correlation between the residual stress and lattice constant under various deposition conditions is found. For the coatings deposited at − 100 V, and at temperatures above 573 K, the hardness could attain to the range of 32 to 35 GPa. Even after annealing in vacuum at 1173 K for 5 h, there is no notable change in the as-deposited phase, grain size or lattice constant of the coatings but an increase in hardness. The thermal stability of microstructure is considered to be a result of the high mixing entropy and sluggish diffusion of these multi-component coatings. For the anneal hardening it is proposed that the overall bonding between target elements and nitrogen is enhanced by thermal energy during annealing.

[1]  F. V. Kiryukhantsev-Korneev,et al.  Hard tribological Ti–B–N, Ti–Cr–B–N, Ti–Si–B–N and Ti–Al–Si–B–N coatings , 2005 .

[2]  A. Matthews,et al.  On the significance of the H/E ratio in wear control: a nanocomposite coating approach to optimised tribological behaviour , 2000 .

[3]  Y. Makino,et al.  Characterization of Zr–Al–N films synthesized by a magnetron sputtering method , 2005 .

[4]  T. Chin,et al.  Formation of simple crystal structures in Cu-Co-Ni-Cr-Al-Fe-Ti-V alloys with multiprincipal metallic elements , 2004 .

[5]  C. Eggs,et al.  Thermal stability of ZrN–Ni and CrN–Ni superhard nanocomposite coatings , 2001 .

[6]  J. Yeh,et al.  Microstructure characterization of AlxCoCrCuFeNi high-entropy alloy system with multiprincipal elements , 2005 .

[7]  J. Schneider,et al.  Influence of the Al distribution on the structure, elastic properties, and phase stability of supersaturated Ti1- xAlxN , 2006 .

[8]  Philip J. Martin,et al.  Nanocomposite Ti-Si-N, Zr-Si-N, Ti-Al-Si-N, Ti-Al-V-Si-N thin film coatings deposited by vacuum arc deposition , 2005 .

[9]  J. Sundgren,et al.  Structure and properties of TiN coatings , 1985 .

[10]  J. Yeh,et al.  Multi-component nitride coatings derived from Ti–Al–Cr–Si–V target in RF magnetron sputter , 2007 .

[11]  C. Mitterer,et al.  Thermal stability of PVD hard coatings , 2003 .

[12]  M. Ohring.  The Materials Science of Thin Films , 1991 .

[13]  T. Shun,et al.  Multi‐Principal‐Element Alloys with Improved Oxidation and Wear Resistance for Thermal Spray Coating , 2004 .

[14]  J. Yeh,et al.  Wear resistance and high-temperature compression strength of Fcc CuCoNiCrAl0.5Fe alloy with boron addition , 2004 .

[15]  H. Holleck.  Metastable coatings — Prediction of composition and structure , 1988 .

[16]  Shou-Yi Chang,et al.  Preparation and characterization of AlCrTaTiZr multi-element nitride coatings , 2006 .

[17]  J. Yeh,et al.  Mechanical performance of the AlxCoCrCuFeNi high-entropy alloy system with multiprincipal elements , 2005 .

[18]  C. Mitterer,et al.  Self-organized nanostructures in the Ti–Al–N system , 2003 .

[19]  S. Deevi,et al.  Single layer and multilayer wear resistant coatings of (Ti,Al)N: a review , 2003 .

[20]  F. Lévy,et al.  Sputter deposited chromium nitride based ternary compounds for hard coatings , 1998 .

[21]  Müller,et al.  Ion-beam-induced epitaxial vapor-phase growth: A molecular-dynamics study. , 1987, Physical review. B, Condensed matter.

[22]  R. W. Siegel,et al.  Mechanical properties of nanophase metals , 1994 .

[23]  S. Vepřek,et al.  Avoiding the high-temperature decomposition and softening of (Al1−xTix)N coatings by the formation of stable superhard nc-(Al1−xTix)N/a-Si3N4 nanocomposite , 2004 .

[24]  F. Lévy,et al.  Thermal decomposition of Zr1 − xAlxN thin films deposited by magnetron sputtering , 2006 .

[25]  Y. Makino.  Prediction of phase change in pseudobinary transition metal aluminum nitrides by band parameters method , 2005 .

[26]  H. Oettel,et al.  Residual stresses in PVD hard coatings , 1995 .

[27]  J. Yeh,et al.  Effect of substrate bias on the structure and properties of multi-element (AlCrTaTiZr)N coatings , 2006 .

[28]  Kenji Yamamoto,et al.  Properties of (Ti, Cr, Al)N coatings with high Al content deposited by new plasma enhanced arc-cathode , 2003 .

[29]  R. Gaboriaud,et al.  Microstructure of (Ti,Si,Al)N nanocomposite coatings , 2004 .

[30]  C. Park,et al.  Synthesis and mechanical evaluation of quaternary Ti–Cr–Si–N coatings deposited by a hybrid method of arc ion plating and sputtering techniques , 2005 .

[31]  Ruifeng Zhang,et al.  On the spinodal nature of the phase segregation and formation of stable nanostructure in the Ti–Si–N system , 2006 .

[32]  Jien-Wei Yeh,et al.  Nanostructured nitride films of multi-element high-entropy alloys by reactive DC sputtering , 2004 .

[33]  T. Shun,et al.  Nanostructured High‐Entropy Alloys with Multiple Principal Elements: Novel Alloy Design Concepts and Outcomes , 2004 .

[34]  O. Knotek,et al.  On spinodal decomposition in magnetron-sputtered (Ti,Zr) nitride and carbide thin films☆ , 1989 .