Effect of nanotopography in direct wafer bonding: modeling and measurements

Nanotopography, which refers to surface height variations of tens to hundreds of nanometers that extend across millimeter-scale wavelengths, is a wafer geometry feature that may cause failure in direct wafer bonding processes. In this work, the nanotopography that is acceptable in direct bonding is determined using mechanics-based models that compare the elastic strain energy accumulated in the wafer during bonding to the work of adhesion. The modeling results are presented in the form of design maps that show acceptable magnitudes of height variations as a function of spatial wavelength. The influence of nanotopography in the bonding of prime grade silicon wafers is then assessed through a combination of measurements and analysis. Nanotopography measurements on three 150-mm silicon wafers, which were manufactured using different polishing processes, are reported and analyzed. Several different strategies are used to compare the wafers in terms of bondability and to assess the impact of the measured nanotopography in direct bonding. The measurement and analysis techniques reported here provide a general route for assessing the impact of nanotopography in direct bonding and can be employed when evaluating different processes to manufacture wafers for bonded devices or substrates.

[1]  U. Gösele,et al.  SemiConductor Wafer Bonding: Science and Technology , 1998 .

[2]  John Francis Valley,et al.  Interferometric metrology of wafer nanotopography for advanced CMOS process integration , 2001, SPIE Optics + Photonics.

[3]  Duane S. Boning,et al.  Nanotopography Issues in Shallow Trench Isolation CMP , 2002 .

[4]  U. Gosele,et al.  Silicon wafer bonding: chemistry, elasto-mechanics, and manufacturing , 1989, IEEE SOS/SOI Technology Conference.

[5]  Kevin T. Turner,et al.  Modeling of direct wafer bonding: effect of wafer bow and etch patterns , 2002 .

[6]  F Riedel,et al.  Impact of filtering on nanotopography measurement of 300mm silicon wafers , 2002 .

[7]  R. Deters,et al.  On the Impact of Nanotopography of Silicon Wafers on Post-Chemical Mechanical Polished Oxide Layers , 2002 .

[8]  Duane S. Boning,et al.  Nanotopography effects on chemical mechanical polishing for shallow trench isolation , 2000, 2000 IEEE/SEMI Advanced Semiconductor Manufacturing Conference and Workshop. ASMC 2000 (Cat. No.00CH37072).

[9]  Duane S. Boning,et al.  Modeling and Mapping of Nanotopography Interactions with CMP , 2002 .

[10]  U. Paik,et al.  The Nanotopography Effect of Improved Single-Side-Polished Wafer on Oxide Chemical Mechanical Polishing , 2002 .

[11]  Jea-Gun Park,et al.  Spectral Analyses of the Impact of Nanotopography of Silicon Wafers on Oxide Chemical Mechanical Polishing , 2001 .

[12]  Tony L. Schmitz,et al.  High-speed noninterferometric nanotopographic characterization of Si wafer surfaces , 2002, SPIE Optics + Photonics.

[13]  Z. Suo,et al.  A model of wafer bonding by elastic accommodation , 1998 .

[14]  N. Miki,et al.  Effect of nanoscale surface roughness on the bonding energy of direct-bonded silicon wafers , 2003 .

[15]  U. Gösele,et al.  Thickness Considerations in Direct Silicon Wafer Bonding , 1995 .

[16]  S. Spearing,et al.  Mechanics of wafer bonding: effect of clamping , 2004 .

[17]  Duane S. Boning,et al.  Wafer Nanotopography Effects on CMP: Experimental Validation of Modeling Methods , 2001 .

[18]  R. Deters,et al.  On the impact of nanotopography of silicon wafers on post-CMP oxide layers , 2002 .