Analysis of delamination in IC packages using a new variable-order singular boundary element

Delamination of interfaces in IC packages gives rise to electrical and mechanical failures such as popcorn cracking. Hence it is important to be able to analyse the mechanics of delamination from small interfacial defects which may exist at interfaces due to contamination or random factors. This paper describes the mechanics of interfacial delamination and the application of the boundary element method to analysing delamination propagation at interfaces. Now, a crack tip at an interface between two materials has an order of singularity which is a function of the material properties. For an accurate analysis, a special variable-order singular boundary element has been developed and used. The effect of defect size and location along the pad-encapsulant interface on interfacial delamination has been studied. It was found that the energy release rate or stress intensity factor increases with defect size as well as proximity to the pad corner. This implies that when a small delamination near a pad corner delaminates the crack tip nearer the pad corner will propagate first. The analysis also shown that this delamination. Once started, will continue until the crack tip reaches the pad corner. If the variation of interface toughness as a function of mode mixity is known, the delamination propagation behaviour can be determined. Depending on the shape of the curve describing the variation of interface toughness with mode mixity, the delamination growth can either be stable, catastrophic or initial unstable followed by stable growth.

[1]  R. D. Henshell,et al.  CRACK TIP FINITE ELEMENTS ARE UNNECESSARY , 1975 .

[2]  James R. Rice,et al.  Elastic Fracture Mechanics Concepts for Interfacial Cracks , 1988 .

[3]  C. Shih.  Cracks on bimaterial interfaces: elasticity and plasticity aspects , 1991 .

[4]  S. Benzley.  Representation of singularities with isoparametric finite elements , 1974 .

[5]  Y. L. Gao,et al.  Determination of characterizing parameters for bimaterial interface cracks using the boundary element method , 1992 .

[6]  Y. L. Gao,et al.  Treatment of bimaterial interface crack problems using the boundary element method , 1990 .

[7]  A. Tay,et al.  A criterion for predicting delamination in plastic IC packages , 1993, 31st Annual Proceedings Reliability Physics 1993.

[8]  A. R. Luxmoore,et al.  An assessment of crack tip singularity models for use with isoparametric elements , 1979 .

[9]  Nicholas J. Altiero,et al.  On a unified boundary-integral equation method , 1980 .

[10]  Carlos Alberto Brebbia,et al.  Boundary Elements: An Introductory Course , 1989 .

[11]  On the computation of two-dimensional stress intensity factors using the boundary element method , 1988 .

[12]  Theodore H. H. Pian,et al.  A hybrid‐element approach to crack problems in plane elasticity , 1973 .

[13]  Anthony R. Ingraffea,et al.  Two‐dimensional stress intensity factor computations using the boundary element method , 1981 .

[14]  P. Theocaris.  The order of singularity at a multi-wedge corner of a composite plate , 1974 .

[15]  Zhigang Suo,et al.  Experimental determination of interfacial toughness curves using Brazil-nut-sandwiches , 1990 .

[16]  J. Domínguez,et al.  On the use of quarter‐point boundary elements for stress intensity factor computations , 1984 .

[17]  F. J. Rizzo,et al.  A unified boundary integral equation method for a class of second order elliptic boundary value problems , 1984, The Journal of the Australian Mathematical Society. Series B. Applied Mathematics.

[18]  Simon P. Walker,et al.  Treatment of corners in BIE analysis of potential problems , 1989 .

[19]  Toshio Hattori,et al.  A stress singularity parameters approach for evaluating adhesive strength. , 1988 .

[20]  Toshio Hattori,et al.  A Stress Singularity Parameter Approach for Evaluating Adhesive Strength , 1988 .

[21]  K. de Zeeuw,et al.  Relation between delamination and temperature-cycling induced failures in plastic packaged devices , 1990 .

[22]  T. A. Cruse,et al.  Boundary-Integral Equation Method for Elastic Fracture Mechanics Analysis. , 1976 .

[23]  R. Barsoum.  On the use of isoparametric finite elements in linear fracture mechanics , 1976 .

[24]  J. V. Vroonhoven.  Effects of Adhesion and Delamination on Stress Singularities in Plastic-Packaged Integrated Circuits , 1993 .

[25]  Andrew A. O. Tay,et al.  Predicting delamination in plastic IC packages and determining suitable mold compound properties , 1994 .

[26]  Karl W. Wyatt,et al.  An Interfacial Delamination Analysis for Multichip Module Thin Film Interconnects , 1996 .

[27]  Andrew A. O. Tay,et al.  Influence of temperature, humidity and defect location on delamination in plastic IC packages , 1998, ITherm'98. Sixth Intersociety Conference on Thermal and Thermomechanical Phenomena in Electronic Systems (Cat. No.98CH36208).