Synthesis and Characterization of Self-Standing and Highly Flexible δ-MnO2@CNTs/CNTs Composite Films for Direct Use of Supercapacitor Electrodes.

Self-standing and flexible films worked as pseudocapacitor electrodes have been fabricated via a simple vacuum-filtration procedure to stack δ-MnO2@carbon nanotubes (CNTs) composite layer and pure CNT layer one by one with CNT layers ended. The lightweight CNTs layers served as both current collector and supporter, while the MnO2@CNTs composite layers with birnessite-type MnO2 worked as active layer and made the main contribution to the capacitance. At a low discharge current of 0.2 A g(-1), the layered films displayed a high areal capacitance of 0.293 F cm(-2) with a mass of 1.97 mg cm(-2) (specific capacitance of 149 F g(-1)) and thickness of only 16.5 μm, and hence an volumetric capacitance of about 177.5 F cm(-3). Moreover, the films also exhibited a good rate capability (only about 15% fading for the capacitance when the discharge current increased to 5 A g(-1) from 0.2 A g(-1)), outstanding cycling stability (about 90% of the initial capacitance was remained after 5,000 cycles) and high flexibility (almost no performance change when bended to different angles). In addition, the capacitance of the films increased proportionally with the stacked layers and the geometry area. E.g., when the stacked layers were three times many with a mass of 6.18 mg cm(-2), the areal capacitance of the films was increased to 0.764 F cm(-2) at 0.5 A g(-1), indicating a high electronic conductivity. It is not overstated to say that the flexible and lightweight layered films emerged high potential for future practical applications as supercapacitor electrodes.

[1]  V. Presser,et al.  Carbons and Electrolytes for Advanced Supercapacitors , 2014, Advanced materials.

[2]  Wenjie Mai,et al.  Ultrahigh‐Performance Pseudocapacitor Electrodes Based on Transition Metal Phosphide Nanosheets Array via Phosphorization: A General and Effective Approach , 2015 .

[3]  Meilin Liu,et al.  Phase evolution of an alpha MnO2-based electrode for pseudo-capacitors probed by in operando Raman spectroscopy , 2014 .

[4]  Jim P. Zheng,et al.  Hydrous Ruthenium Oxide as an Electrode Material for Electrochemical Capacitors , 1995 .

[5]  Chi-Chang Hu,et al.  A hierarchical nanostructure consisting of amorphous MnO2, Mn3O4 nanocrystallites, and single-crystalline MnOOH nanowires for supercapacitors , 2011 .

[6]  Meilin Liu,et al.  Investigations into the origin of pseudocapacitive behavior of Mn3O4 electrodes using in operando Raman spectroscopy , 2015 .

[7]  Fei Li,et al.  MnO2-based nanostructures for high-performance supercapacitors , 2015 .

[8]  Changsoon Choi,et al.  Flexible Supercapacitor Made of Carbon Nanotube Yarn with Internal Pores , 2014, Advanced materials.

[9]  Ayyakkannu Manivannan,et al.  Highly conductive electrospun carbon nanofiber/MnO2 coaxial nano-cables for high energy and power density supercapacitors , 2012 .

[10]  F. Qu,et al.  Phase-controlled synthesis of polymorphic MnO2 structures for electrochemical energy storage , 2015 .

[11]  Jie Cheng,et al.  Carbon nanotube/MnO2 composites synthesized by microwave-assisted method for supercapacitors with high power and energy densities , 2009 .

[12]  W. Lu,et al.  MnO 2 -Carbon nanotube composite for high-areal-density supercapacitors with high rate performance , 2016 .

[13]  K. Kar,et al.  Self-standing carbon nanotube forest electrodes for flexible supercapacitors , 2015 .

[14]  J. Tu,et al.  Co3O4–C core–shell nanowire array as an advanced anode material for lithium ion batteries , 2012 .

[15]  Qingwen Li,et al.  Graphene-patched CNT/MnO2 nanocomposite papers for the electrode of high-performance flexible asymmetric supercapacitors. , 2013, ACS applied materials & interfaces.

[16]  Xiaobo Ji,et al.  Electrochemical capacitors utilising transition metal oxides: an update of recent developments , 2011 .

[17]  Genevieve Dion,et al.  Textile energy storage in perspective , 2014 .

[18]  S. Devaraj,et al.  Effect of Crystallographic Structure of MnO2 on Its Electrochemical Capacitance Properties , 2008 .

[19]  Shi Xue Dou,et al.  Electrodeposition of MnO2 nanowires on carbon nanotube paper as free-standing, flexible electrode for supercapacitors , 2008 .

[20]  Zhijun Qiao,et al.  Free-standing porous carbon nanofiber/ultrathin graphite hybrid for flexible solid-state supercapacitors. , 2015, ACS nano.

[21]  M. Boujtita,et al.  Titanium nitride films for micro-supercapacitors: Effect of surface chemistry and film morphology on the capacitance , 2015 .

[22]  Mathieu Toupin,et al.  Charge Storage Mechanism of MnO2 Electrode Used in Aqueous Electrochemical Capacitor , 2004 .

[23]  Jun Chen,et al.  Highly conductive three-dimensional MnO2-carbon nanotube-graphene-Ni hybrid foam as a binder-free supercapacitor electrode. , 2014, Nanoscale.

[24]  H. Pang,et al.  One-step synthesis and graphene-modification to achieve nickel phosphide nanoparticles with electrochemical properties suitable for supercapacitors , 2015 .

[25]  Jun Zhou,et al.  Flexible solid-state supercapacitors based on carbon nanoparticles/MnO2 nanorods hybrid structure. , 2012, ACS nano.

[26]  K. Lian,et al.  Development of pseudocapacitive molybdenum oxide–nitride for electrochemical capacitors , 2015 .

[27]  L. Dai,et al.  Flexible supercapacitors based on carbon nanomaterials , 2014 .

[28]  Li Lu,et al.  Hydrothermal synthesis of MnO2/CNT nanocomposite with a CNT core/porous MnO2 sheath hierarchy architecture for supercapacitors , 2012, Nanoscale Research Letters.

[29]  Dionisios G. Vlachos,et al.  Nickel supported on nitrogen-doped carbon nanotubes as hydrogen oxidation reaction catalyst in alkaline electrolyte , 2016, Nature Communications.

[30]  Zikang Tang,et al.  Integrated random-aligned carbon nanotube layers: deformation mechanism under compression. , 2014, Nanoscale.

[31]  Jyhfu Lee,et al.  Fabrication of Mn/Mn oxide core–shell electrodes with three-dimensionally ordered macroporous structures for high-capacitance supercapacitors , 2013 .

[32]  Lele Peng,et al.  Two dimensional nanomaterials for flexible supercapacitors. , 2014, Chemical Society reviews.

[33]  K. Hashimoto,et al.  Inhibition of charge disproportionation of MnO2 electrocatalysts for efficient water oxidation under neutral conditions. , 2012, Journal of the American Chemical Society.

[34]  J. Pereira‐Ramos,et al.  Doping effects on structure and electrode performance of K-birnessite-type manganese dioxides for rechargeable lithium battery , 2008 .

[35]  H. Pang,et al.  New asymmetric and symmetric supercapacitor cells based on nickel phosphide nanoparticles , 2015 .

[36]  Bin Liu,et al.  Fiber-based flexible all-solid-state asymmetric supercapacitors for integrated photodetecting system. , 2014, Angewandte Chemie.

[37]  Li Li,et al.  Facile Synthesis of MnO2/CNTs Composite for Supercapacitor Electrodes with Long Cycle Stability , 2014 .

[38]  Lian Gao,et al.  Characterization of a manganese dioxide/carbon nanotube composite fabricated using an in situ coating method , 2007 .

[39]  O. V. Kharissova,et al.  Variations of interlayer spacing in carbon nanotubes , 2014 .