Summary In this paper, the penetration of ceramic targets backed by thin metallic plates when impacted by cylindrical projectiles is studied. To achieve this, a two-dimensional axisymmetric numerical analysis of the normal impact problem is performed. The macroscopic material behaviour in the zone of finely pulverized ceramic ahead of the penetrator is modelled by means of a constitutive model taking into account internal friction and volumetric expansion. The amount of comminution at the computational cells is evaluated through a damage evolution equation, and the yield stress is assumed to be a function of the hydrostatic pressure, internal friction and amount of comminution. For the metallic materials involved, an elasto-plastic behaviour with a rupture condition was considered. Moreover, an erosion condition was included as a limit situation when the ruptured material limits its role in the penetration process to purely inertial effects. In this way, a detailed picture of the penetration process of the target by the impacting projectile was obtained. Then, the results of the numerical analysis were compared with the experimental observations of the projectile-target interaction, previously made by Reijer by using a flash X-ray technique. Under certain conditions, remarkable agreement between computations and experiments is encountered, thus suggesting the adequacy of the main assumptions made in the numerical approach to the physical situation.
[1]
Dynamic uniaxial stress experiments on alumina with in‐material Manganin gauges
,
1985
.
[2]
Stephan Bless,et al.
Shear strength of shock‐loaded alumina as determined with longitudinal and transverse manganin gauges
,
1987
.
[3]
J. Rice,et al.
CONDITIONS FOR THE LOCALIZATION OF DEFORMATION IN PRESSURE-SENSITIVE DILATANT MATERIALS
,
1975
.
[4]
Donald A. Shockey,et al.
The strength behavior of granulated silicon carbide at high strain rates and confining pressure
,
1991
.
[5]
Donald A. Shockey,et al.
Failure phenomenology of confined ceramic targets and impacting rods
,
1990
.
[6]
Y. Yeshurun,et al.
Determination of the dynamic response of AD‐85 alumina with in‐material Manganin gauges
,
1985
.
[7]
Lynn Seaman,et al.
Dynamic failure of solids
,
1987
.
[8]
W. Gust,et al.
Dynamic Yield Strengths of B4C, BeO, and Al2O3 Ceramics
,
1971
.
[9]
H. C. Heard,et al.
Mechanical behaviour of polycrystalline BeO, Al2O3 and AlN at high pressure
,
1980
.